1. WO2020201437 - PRODUIT EN ACIER DE HAUTE DURETÉ ET PROCÉDÉ DE FABRICATION D’UN TEL PRODUIT

Numéro de publication WO/2020/201437
Date de publication 08.10.2020
N° de la demande internationale PCT/EP2020/059423
Date du dépôt international 02.04.2020
CIB
C21D 8/02 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
02pendant la fabrication de produits plats ou de bandes
C22C 38/04 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
04contenant du manganèse
C22C 38/42 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
42et du cuivre
C22C 38/44 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
44et du molybdène ou du tungstène
C22C 38/54 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
54et du bore
CPC
C21D 1/00
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
1General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
C21D 2211/008
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
008Martensite
C21D 8/0226
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0221characterised by the working steps
0226Hot rolling
C21D 8/0263
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0247characterised by the heat treatment
0263following hot rolling
C22C 38/02
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
02containing silicon
C22C 38/04
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
04containing manganese
Déposants
  • SSAB TECHNOLOGY AB [SE]/[SE]
Inventeurs
  • LARSSON, Magnus
  • GLADH, Magnus
Mandataires
  • VALEA AB
Données relatives à la priorité
19167552.905.04.2019EP
19185759.811.07.2019EP
Langue de publication anglais (EN)
Langue de dépôt anglais (EN)
États désignés
Titre
(EN) HIGH-HARDNESS STEEL PRODUCT AND METHOD OF MANUFACTURING THE SAME
(FR) PRODUIT EN ACIER DE HAUTE DURETÉ ET PROCÉDÉ DE FABRICATION D’UN TEL PRODUIT
Abrégé
(EN)
A hot-rolled steel strip product comprising a composition consisting of, in terms of weight percentages, 0.14 % to 0.35 % C, 0 % to 0.5 % Si, 0.05 % to 0.40 % Mn, 0.1 % or less Al, 0.1 % to 0.4 % Cu, 0.2 % to 0.9 % Ni, 0.2 % to 0.9 % Cr, 0.2 % or less Mo, 0.005 % or less Nb, 0.035 % or less Ti, 0.05 % or less V, 0.0005 % to 0.0050 % B, 0.025 % or less P, 0.008 % or less S, 0.01 % or less N, 0.01 % or less Ca, and the remainder being Fe and inevitable impurities, wherein the steel product has a Brinell hardness in the range of 420 to 580 HBW.
(FR)
L’invention concerne un produit de type bande d'acier laminée à chaud comprenant une composition constituée, en pourcentages en poids, de 0,14 % à 0,35 % de C, de 0 % à 0,5 % de Si, de 0,05 % à 0,40 % de Mn, de 0,1 % ou moins d'Al, de 0,1 % à 0,4 % de Cu, de 0,2 % à 0,9 % de Ni, de 0,2 % à 0,9 % de Cr, de 0,2 % ou moins de Mo, de 0,005 % ou moins de Nb, de 0,035 % ou moins de Ti, de 0,05 % ou moins de V, de 0,0005 % à 0,0050 % de B, 0,025 % ou moins de P, de 0,008 % ou moins de S, de 0,01 % ou moins de N, de 0,01 % ou moins de Ca, le reste étant du Fe et des impuretés inévitables, le produit en acier ayant une dureté Brinell comprise dans la plage de 420 à 580 HBW.