1. WO2020158228 - TÔLE D'ACIER À HAUTE RÉSISTANCE ET PROCÉDÉ DE PRODUCTION D’UNE TELLE TÔLE D'ACIER

Numéro de publication WO/2020/158228
Date de publication 06.08.2020
N° de la demande internationale PCT/JP2019/049749
Date du dépôt international 19.12.2019
CIB
C21D 9/46 2006.1
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9Traitement thermique, p.ex. recuit, durcissement, trempe ou revenu, adapté à des objets particuliers; Fours à cet effet
46pour tôles
C22C 38/00 2006.1
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
C22C 38/06 2006.1
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
06contenant de l'aluminium
C22C 38/58 2006.1
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
58et plus de 1,5% en poids de manganèse
CPC
C21D 9/46
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
9Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
46for sheet metals
C22C 38/00
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/06
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
06containing aluminium
C22C 38/58
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
58with more than 1.5% by weight of manganese
Déposants
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP]/[JP]
Inventeurs
  • 平島 拓弥 HIRASHIMA Takuya
  • 本田 佑馬 HONDA Yuma
  • 中村 章紀 NAKAMURA Akinori
  • 金子 真次郎 KANEKO Shinjiro
Mandataires
  • 熊坂 晃 KUMASAKA Akira
  • 森 和弘 MORI Kazuhiro
  • 磯村 哲朗 ISOMURA Tetsuo
  • 坂井 哲也 SAKAI Tetsuya
Données relatives à la priorité
2019-01279029.01.2019JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) HIGH-STRENGTH STEEL SHEET AND METHOD FOR PRODUCING SAME
(FR) TÔLE D'ACIER À HAUTE RÉSISTANCE ET PROCÉDÉ DE PRODUCTION D’UNE TELLE TÔLE D'ACIER
(JA) 高強度鋼板及びその製造方法
Abrégé
(EN)
Provided are a low-yield-ratio and high-strength steel sheet and a method for producing the same. The present invention is a high-strength steel sheet, the component composition of the steel sheet containing, in terms of mass%, 0.06% to 0.120% C, 0.3% to 0.7% Si, 1.6% to 2.2% Mn, no more than 0.05% P, no ore than 0.0050% S, 0.01% to 0.20% Al, and no more than 0.010% N, the remainder comprising Fe and unavoidable impurities, and the steel structure of the steel sheet having a ferrite main phase and 10% to less than 50% martensite by area ratio with respect to the entire steel structure, the average crystal grain size of the martensite being 3.0 µm or less, the ratio of martensite having an aspect ratio of 3 or less being at least 60% with respect to the total martensite, and the carbon concentration in the martensite having an aspect ratio of 3 or less being 0.30% to 0.90% in terms of mass%.
(FR)
L'invention concerne une tôle d’acier à faible coefficient d’élasticité et à haute résistance ainsi qu’un procédé de production d’une telle tôle d’acier. La présente invention concerne une tôle d'acier à haute résistance, la composition de constituants de la tôle d'acier contenant, en % en masse, de 0,06 % à 0,120 % de C, de 0,3 % à 0,7 % de Si, de 1,6 % à 2,2 % de Mn, pas plus de 0,05 % de P, pas plus de 0,0050 % de S, de 0,01 % à 0,20 % d'Al, et pas plus de 0,010 % de N, le reste comprenant du Fe et des impuretés inévitables, et la structure d'acier de la tôle d'acier ayant une phase ferritique principale et de 10 % à moins de 50 % de martensite par rapport de surface relativement à la totalité de la structure d'acier, la taille moyenne des grains cristallins de la martensite étant inférieure ou égale à 3,0 µm, le rapport de martensite ayant un rapport d'aspect inférieur ou égal à 3 étant d'au moins 60 % relativement à la martensite totale, et la concentration en carbone dans la martensite ayant un rapport d'aspect inférieur ou égal à 3 étant de 0,30 % à 0,90 % en % en masse.
(JA)
低降伏比高強度鋼板及びその製造方法を提供する。本発明は、成分組成は、質量%で、C:0.06%以上0.120%以下、Si:0.3%以上0.7%以下、Mn:1.6%以上2.2%以下、P:0.05%以下、S:0.0050%以下、Al:0.01%以上0.20%以下、N:0.010%以下を含有し、残部はFeおよび不可避的不純物からなり、鋼組織は、主相のフェライトと、鋼組織全体に対する面積率で10%以上50%未満のマルテンサイトを有し、マルテンサイトの平均結晶粒径が3.0μm以下であり、マルテンサイト全体に対する、アスペクト比が3以下のマルテンサイトの割合が60%以上であり、アスペクト比が3以下のマルテンサイト中の炭素濃度が、質量%で、0.30%以上0.90%以下である高強度鋼板とする。