1. WO2020156374 - CONSTITUANT DE FIBRE DE VERRE À FAIBLE CONSTANTE DIÉLECTRIQUE ET SON PROCÉDÉ DE FABRICATION

Numéro de publication WO/2020/156374
Date de publication 06.08.2020
N° de la demande internationale PCT/CN2020/073474
Date du dépôt international 21.01.2020
CIB
C03C 13/00 2006.1
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
CCOMPOSITION CHIMIQUE DES VERRES, GLAÇURES OU ÉMAUX VITREUX; TRAITEMENT DE LA SURFACE DU VERRE; TRAITEMENT DE SURFACE DES FIBRES OU FILAMENTS DE VERRE, DE SUBSTANCES MINÉRALES OU DE SCORIES; LIAISON DU VERRE AU VERRE OU À D'AUTRES MATÉRIAUX
13Compositions pour fibres ou filaments de verre
C03C 6/04 2006.1
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
CCOMPOSITION CHIMIQUE DES VERRES, GLAÇURES OU ÉMAUX VITREUX; TRAITEMENT DE LA SURFACE DU VERRE; TRAITEMENT DE SURFACE DES FIBRES OU FILAMENTS DE VERRE, DE SUBSTANCES MINÉRALES OU DE SCORIES; LIAISON DU VERRE AU VERRE OU À D'AUTRES MATÉRIAUX
6Charges de mélanges vitrifiables
04contenant de la silice non combinée, p.ex. sable
CPC
C03C 1/00
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
1Ingredients generally applicable to manufacture of glasses, glazes, or vitreous enamels
C03C 13/00
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
13Fibre or filament compositions
Déposants
  • 河南光远新材料股份有限公司 HENAN GUANGYUAN NEW MATERIAL CO., LTD [CN]/[CN]
  • 华东理工大学 EAST CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY [CN]/[CN]
Inventeurs
  • 黄建国 HUANG, Jianguo
  • 宁祥春 NING, Xiangchun
Mandataires
  • 北京八月瓜知识产权代理有限公司 BEIJING BAYUEGUA INTELLECTUAL PROPERTY AGENCY CO. , LTD.
Données relatives à la priorité
201910090936.030.01.2019CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) LOW-DIELECTRIC GLASS FIBER COMPONENT AND MANUFACTURING METHOD THEREOF
(FR) CONSTITUANT DE FIBRE DE VERRE À FAIBLE CONSTANTE DIÉLECTRIQUE ET SON PROCÉDÉ DE FABRICATION
(ZH) 一种低介电玻璃纤维组分及其制造方法
Abrégé
(EN)
Provided is a low-dielectric glass fiber component, comprising the following components by mass fraction: SiO2: 54.0–57.0%, Al2O3: 12.0–15.0%, B2O3: 16.0–25.0%, CaO: 1.0–2.5%, MgO: 2.0–5.0%, ZnO: 2.0–4.0%, TiO2: 0.4–2.0%, ZrO2: 0–0.5%, and Bi2O3: 0.1–1.5%; in addition to controlling the SiO2, Al2O3, B2O3 oxide composition to within a certain range, the mixed alkaline earth effect is utilized to control the total amount of RO to less than 10%, in particular, MgO/RO = 0.3 to 0.5 and ZnO/RO = 0.2 to 0.5, so as to control the phase separation and crystallization range of the glass; furthermore, by means of adding a small amount of ZrO2 and TiO2, the water resistance and acid and alkali resistance of glass are improved. A small amount of Bi2O3 is introduced into the composition to reduce the high temperature viscosity of the glass melt, and thereby achieve the effect of reducing the melting temperature and conserving energy and reducing emissions in glass production; at the same time, the dielectric properties of the glass are not impaired.
(FR)
La présente invention concerne un constituant de fibre de verre à faible constante diélectrique, comprenant les constituants suivants en fraction en masse : SiO2 : de 54,0 à 57,0 %, Al2O3 : de 12,0 à 15,0 %, B2O3 : de 16,0 à 25,0 %, CaO : de 1,0 à 2,5 %, MgO : de 2,0 à 5,0 %, ZnO : de 2,0 à 4,0 %, TiO2 : de 0,4 à 2,0 %, ZrO2 : de 0 à 0,5 %, et Bi2O3 : de 0,1 à 1,5 % ; l’effet mixte de terre alcaline est utilisé à la fois pour réguler la composition d’oxyde SiO2, Al2O3, B2O3 à l’intérieur d’une certaine plage, et pour réguler la quantité totale de RO jusqu’à moins de 10 %, en particulier, MgO/RO = 0,3 à 0,5 et ZnO/RO = 0,2 à 0,5, afin de réguler la séparation de phase et la plage de cristallisation du verre ; en outre, en ajoutant une petite quantité de ZrO2 et de TiO2, la résistance à l’eau et la résistance aux acides et aux alcalins du verre sont améliorées. Une petite quantité de Bi2O3 est introduite dans la composition afin de réduire la viscosité à haute température de fusion du verre, et d'atteindre ainsi l’effet de réduction de la température de fusion et de conserver l’énergie et de réduire les émissions dans la production de verre ; en même temps, les propriétés diélectriques du verre ne sont pas altérées.
(ZH)
一种低介电玻璃纤维组分,按质量分数计,包括如下组分:SiO 2:54.0-57.0%,Al 2O 3:12.0-15.0%,B 2O 3:16.0-25.0%,CaO:1.0-2.5%,MgO:2.0-5.0%,ZnO:2.0-4.0%,TiO 2:0.4-2.0%,ZrO 2:0-0.5%,Bi 2O 3:0.1-1.5%;除了控制SiO 2、Al 2O 3、B 2O 3氧化物组成在一定范围内,还利用混合碱土效应,控制RO总量小于10%,特别是MgO/RO=0.3~0.5,ZnO/RO=0.2~0.5,以控制玻璃的分相、析晶范围,并且通过复合添加少量ZrO 2和TiO 2,改善玻璃的耐水、耐酸碱性。在组成中引入少量Bi 2O 3,使玻璃熔体高温粘度降低,从而实现玻璃生产中降低熔制温度和节能减排的效能,同时不损害玻璃的介电性能。