1. WO2020155244 - PROCÉDÉ DE PRÉPARATION DE MAGNÉSIE DE HAUTE DENSITÉ À L'AIDE D'UN FRITTAGE PAR MICRO-ONDES DE MAGNÉSITE

Numéro de publication WO/2020/155244
Date de publication 06.08.2020
N° de la demande internationale PCT/CN2019/076095
Date du dépôt international 26.02.2019
CIB
C04B 2/10 2006.1
CCHIMIE; MÉTALLURGIE
04CIMENTS; BÉTON; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES
BCHAUX; MAGNÉSIE; SCORIES; CIMENTS; LEURS COMPOSITIONS, p.ex. MORTIERS, BÉTON OU MATÉRIAUX DE CONSTRUCTION SIMILAIRES; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES; TRAITEMENT DE LA PIERRE NATURELLE
2Chaux, magnésie ou dolomite
10Préchauffage, cuisson, calcination ou refroidissement
C04B 2/00 2006.1
CCHIMIE; MÉTALLURGIE
04CIMENTS; BÉTON; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES
BCHAUX; MAGNÉSIE; SCORIES; CIMENTS; LEURS COMPOSITIONS, p.ex. MORTIERS, BÉTON OU MATÉRIAUX DE CONSTRUCTION SIMILAIRES; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES; TRAITEMENT DE LA PIERRE NATURELLE
2Chaux, magnésie ou dolomite
CPC
C04B 2/00
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2Lime, magnesia or dolomite
C04B 2/102
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2Lime, magnesia or dolomite
10Preheating, burning calcining or cooling
102of magnesia, e.g. dead burning
Déposants
  • 东北大学 NORTHEASTERN UNIVERSITY [CN]/[CN]
Inventeurs
  • 马北越 MA, Beiyue
  • 靳恩东 JIN, Endong
  • 任鑫明 REN, Xinming
  • 刘朝阳 LIU, Zhaoyang
  • 付高峰 FU, Gaofeng
  • 于景坤 YU, Jingkun
Mandataires
  • 沈阳东大知识产权代理有限公司 SHENYANG DONGDA INTELLECTUAL PROPERTY AGENCY CO., LTD
Données relatives à la priorité
201910107678.201.02.2019CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) METHOD FOR PREPARING HIGH-DENSITY MAGNESIA BY USING MICROWAVE SINTERING OF MAGNESITE
(FR) PROCÉDÉ DE PRÉPARATION DE MAGNÉSIE DE HAUTE DENSITÉ À L'AIDE D'UN FRITTAGE PAR MICRO-ONDES DE MAGNÉSITE
(ZH) 一种利用菱镁矿微波烧结制备高密度镁砂的方法
Abrégé
(EN)
A method for preparing high-density magnesia by using microwave sintering of magnesite, relating to the technical field of efficient utilization of metallurgical resources. The specific preparation method comprises: calcining magnesite in a high-temperature furnace to obtain primary light-burned magnesia powder; putting the light-burned magnesia powder in a ball mill tank, using deionized water as a ball mill medium, completing the hydration and ball-milling treatment of light-burned magnesia, and after drying treatment, obtaining magnesium hydroxide powder; putting the magnesium hydroxide powder in a high-temperature furnace for secondary calcining to obtain secondary light-burned magnesia powder; and forming the secondary light-burned magnesia powder into a green body, and performing microwave sintering at a certain temperature and time to obtain high-density magnesia.
(FR)
L'invention concerne un procédé de préparation de magnésie de haute densité à l'aide d'un frittage par micro-ondes de magnésite, se rapportant au domaine technique de l'utilisation efficace de ressources métallurgiques. Le procédé de préparation spécifique consiste : à calciner la magnésite dans un four à haute température pour obtenir une poudre de magnésie primaire légèrement calcinée ; à introduire la poudre de magnésie légèrement calcinée dans un réservoir de broyeur à boulets, à utiliser l'eau déionisée comme milieu pour broyeur à boulets, à achever l'hydratation et le traitement par broyage à boulets de la magnésie légèrement calcinée, et après un traitement de séchage, à obtenir une poudre d'hydroxyde de magnésium ; à introduire la poudre d'hydroxyde de magnésium dans un four à haute température en vue d'une calcination secondaire pour obtenir une poudre de magnésie légèrement calcinée secondaire ; et à former de la poudre de magnésie légèrement calcinée secondaire dans une ébauche crue, et à réaliser un frittage par micro-ondes à une certaine température et pendant un certain temps pour obtenir de la magnésie de haute densité.
(ZH)
一种利用菱镁矿微波烧结制备高密度镁砂的方法,属于冶金资源高效利用技术领域。具体制备方法为:将菱镁矿置于高温炉内煅烧,获得一次轻烧氧化镁粉;将轻烧氧化镁粉置于球磨罐中,以去离子水为球磨介质,同时对轻烧氧化镁完成水化和球磨处理,经过干燥处理,获得氢氧化镁粉;将氢氧化镁粉置于高温炉内二次煅烧,获得二次轻烧氧化镁粉;将二次轻烧氧化镁粉成型制成素坯,在一定温度、时间下进行微波烧结,制得高密度镁砂。