Traitement en cours

Veuillez attendre...

Paramétrages

Paramétrages

Aller à Demande

1. WO2020115526 - TÔLE D'ACIER LAMINÉE À FROID ET RECUITE, SON PROCÉDÉ DE PRODUCTION ET UTILISATION D'UN TEL ACIER PERMETTANT DE PRODUIRE DES PIÈCES DE VÉHICULE

Numéro de publication WO/2020/115526
Date de publication 11.06.2020
N° de la demande internationale PCT/IB2018/059625
Date du dépôt international 04.12.2018
CIB
C21D 6/00 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
6Traitement thermique des alliages ferreux
C21D 8/02 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
02pendant la fabrication de produits plats ou de bandes
C21D 8/04 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
02pendant la fabrication de produits plats ou de bandes
04pour produire des produits plats ou des bandes pour l'emboutissage profond
C21D 9/46 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9Traitement thermique, p.ex. recuit, durcissement, trempe ou revenu, adapté à des objets particuliers; Fours à cet effet
46pour tôles
C22C 38/04 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
04contenant du manganèse
C22C 38/06 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
06contenant de l'aluminium
CPC
C21D 1/00
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
1General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
C21D 2211/001
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
001Austenite
C21D 2211/004
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
004Dispersions; Precipitations
C21D 2211/005
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
005Ferrite
C21D 6/005
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
6Heat treatment of ferrous alloys
005containing Mn
C21D 8/0236
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0221characterised by the working steps
0236Cold rolling
Déposants
  • ARCELORMITTAL [LU]/[LU]
Inventeurs
  • DE DIEGO CALDERON, Irène
  • HELL, Jean-Christophe
Mandataires
  • PLAISANT, Sophie
Données relatives à la priorité
Langue de publication anglais (EN)
Langue de dépôt anglais (EN)
États désignés
Titre
(EN) COLD ROLLED AND ANNEALED STEEL SHEET, METHOD OF PRODUCTION THEREOF AND USE OF SUCH STEEL TO PRODUCE VEHICLE PARTS
(FR) TÔLE D'ACIER LAMINÉE À FROID ET RECUITE, SON PROCÉDÉ DE PRODUCTION ET UTILISATION D'UN TEL ACIER PERMETTANT DE PRODUIRE DES PIÈCES DE VÉHICULE
Abrégé
(EN)
A cold rolled and annealed steel sheet comprising by weight: 0.6 < C < 1.3%, 15≤Mn<35%, 6 ≤ Al < 15%, Si ≤ 2.40 %, S ≤ 0.03%, P ≤ 0.1%, N ≤ 0.1%, possibly one or more optional elements chosen among Ni, Cr and Cu in an individual amount of up to 3% and possibly one or more elements chosen among B, Ta, Zr, Nb, V, Ti, Mo, and W in a cumulated amount of up to 2.0%, the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, the microstructure of said sheet comprising of ordered ferrite between 1% and 10%, optionally of up to 10% of kappa carbides, the remainder being made of austenite, and, the density of said steel sheet being equal or below 7.2 and the FWHM for the austenite matrix is between 0.700 and 1.100.
(FR)
L'invention concerne une tôle d'acier laminée à froid et recuite comprenant en poids : 0,6 < C < 1,3%, 15≤Mn<35%, 6 ≤ Al < 15%, Si ≤ 2,40 %, S ≤ 0,03%, P ≤ 0,1%, N ≤ 0,1%, éventuellement un ou plusieurs éléments facultatifs choisis parmi Ni, Cr et Cu en une quantité individuelle allant jusqu'à 3 % et éventuellement un ou plusieurs éléments choisis parmi B, Ta, Zr, Nb, V, Ti, Mo, et W en une quantité cumulée allant jusqu'à 2,0 %, le reste de la composition étant constitué de fer et d'impuretés inévitables résultant de l'élaboration, la microstructure de ladite tôle comprenant une ferrite ordonnée à hauteur de 1 % à 10 %, éventuellement jusqu'à 10 % de carbures kappa, le reste étant constitué d'austénite, et la densité de ladite tôle d'acier étant égale ou inférieure à 7,2 et la valeur FWHM correspondant à la matrice austénitique étant comprise entre 0,700 et 1,100.