1. WO2020114106 - MATÉRIAU COMPOSITE RABS/PBT/ASG ET SON PROCÉDÉ DE PRÉPARATION

Numéro de publication WO/2020/114106
Date de publication 11.06.2020
N° de la demande internationale PCT/CN2019/112049
Date du dépôt international 18.10.2019
CIB
C08L 55/02 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
LCOMPOSITIONS CONTENANT DES COMPOSÉS MACROMOLÉCULAIRES
55Compositions contenant des homopolymères ou des copolymères obtenus par des réactions de polymérisation ne faisant intervenir que des liaisons non saturées carbone-carbone, non prévues dans les groupes C08L23/-C08L53/254
02Polymères ABS
C08L 67/02 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
LCOMPOSITIONS CONTENANT DES COMPOSÉS MACROMOLÉCULAIRES
67Compositions contenant des polyesters obtenus par des réactions créant une liaison ester carboxylique dans la chaîne principale; Compositions contenant des dérivés de tels polymères
02Polyesters dérivés des acides dicarboxyliques et des composés dihydroxylés
C08L 25/14 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
LCOMPOSITIONS CONTENANT DES COMPOSÉS MACROMOLÉCULAIRES
25Compositions contenant des homopolymères ou des copolymères de composés possédant un ou plusieurs radicaux aliphatiques non saturés, chacun ne contenant qu'une seule liaison double carbone-carbone et l'un au moins étant terminé par un cycle carbocyclique aromatique; Compositions des dérivés de tels polymères
02Homopolymères ou copolymères d'hydrocarbures
04Homopolymères ou copolymères du styrène
08Copolymères du styrène
14avec des esters non saturés
Déposants
  • 华南理工大学 SOUTH CHINA UNIVERSITY OF TECHNOLOGY [CN]/[CN]
Inventeurs
  • 何和智 HE, Hezhi
  • 湛志明 ZHAN, Zhiming
  • 冯彦洪 FENG, Yanhong
  • 殷小春 YIN, Xiaochun
  • 瞿金平 QU, Jinping
Mandataires
  • 广州市华学知识产权代理有限公司 GUANGZHOU HUAXUE INTELLECTUAL PROPERTY AGENCY CO., LTD.
Données relatives à la priorité
201811485833.606.12.2018CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) RABS/PBT/ASG COMPOSITE MATERIAL AND PREPARATION METHOD THEREFOR
(FR) MATÉRIAU COMPOSITE RABS/PBT/ASG ET SON PROCÉDÉ DE PRÉPARATION
(ZH) 一种rABS/PBT/ASG复合材料及其制备方法
Abrégé
(EN)
An rABS/PBT/ASG composite material and a preparation method therefor, which utilize the characteristics of rABS having carboxyl and hydroxyl; rABS and ASG are pre-blended for thickening so that the epoxy group on the molecular chain of ASG reacts with the carboxyl and hydroxyl on rABS; moreover, an acrylonitrile-styrene segment in ASG and rABS are thermodynamically mutually dissolved, and then are reacted and blended with PBT to prepare the rABS/PBT/ASG composite material. ASG has the effect of a chain extender and solubilizer in the entire blend. The present method effectively increases the molecular weight of rABS, increases the mechanical properties of the composite material, simultaneously avoids a competitive reaction between rABS, PBT and ASG during direct blending, reduces the possibility of chain extension and thickening of PBT, and may obtain a blend system having a smaller dispersed phase particle size and more uniform particle distribution. The blend prepared by the described method has good compatibility, the tensile strength, impact strength and elongation at break of the composite material are all improved; meanwhile, the obtained composite material has the advantages of both ABS and PBT materials, and has broad application prospects in the field of ABS plastic recycling.
(FR)
L'invention concerne un matériau composite rABS/PBT/ASG et son procédé de préparation, qui utilisent les caractéristiques du rABS comportant du carboxyle et de l'hydroxyle ; le rABS et l'ASG sont pré-mélangés en vue de leur épaississement de telle sorte que le groupe époxy sur la chaîne moléculaire de l'ASG réagit avec le carboxyle et l'hydroxyle sur le rABS ; de plus, un segment acrylonitrile-styrène dans l'ASG et le rABS sont thermodynamiquement dissous l'un dans l'autre, puis sont mis à réagir et mélangés avec du PBT pour préparer le matériau composite rABS/PBT/ASG. L'ASG joue le rôle d'un allongeur de chaîne et d'un agent de solubilisation dans l'ensemble du mélange. Le présent procédé augmente efficacement le poids moléculaire du rABS, améliore les propriétés mécaniques du matériau composite, évite simultanément une réaction compétitive entre le rABS, le PBT et l'ASG pendant le mélange direct, réduit la possibilité d'allongement de chaîne et d'épaississement du PBT, et permet d'obtenir un système de mélange présentant une taille de particules en phase dispersée plus petite et une distribution des particules plus homogène. Le mélange préparé par le procédé décrit présente une bonne compatibilité, et la résistance à la traction, la résistance aux chocs et l'allongement à la rupture du matériau composite sont tous améliorés ; dans le même temps, le matériau composite obtenu présente les avantages à la fois des matériaux que sont l'ABS et le PBT, et offre de vastes perspectives d'application dans le domaine du recyclage des matières plastiques en ABS.
(ZH)
一种rABS/PBT/ASG复合材料及其制备方法,利用了rABS具有羧基和羟基的特点,预先使rABS与ASG共混增粘,使ASG分子链上的环氧基团与rABS上的羧基和羟基反应,并且ASG中的丙烯腈-苯乙烯链段和rABS热力学互溶,然后再与PBT反应共混来制备rABS/PBT/ASG复合材料。其中,ASG在整个共混物中起到扩链剂和增溶剂的作用。该方法有效的提升了rABS的分子量,增加了复合材料的力学性能,同时避免了直接共混中rABS、PBT与ASG的竞争反应,减少了PBT扩链增粘的可能,可获得分散相粒径更小,粒子分布更均匀的共混体系。由此制备的共混物相容性好,复合材料的拉伸强度和冲击强度以及断裂伸长率全面提高,所得复合材料兼具ABS和PBT材料的优点,在ABS塑料回收利用的领域应用前景广阔。