1. WO2020111639 - TÔLE D'ACIER LAMINÉE À CHAUD À ULTRA-HAUTE RÉSISTANCE AYANT UNE EXCELLENTE QUALITÉ DE FORME ET UNE EXCELLENTE APTITUDE AU PLIAGE, ET SON PROCÉDÉ DE FABRICATION

Numéro de publication WO/2020/111639
Date de publication 04.06.2020
N° de la demande internationale PCT/KR2019/015934
Date du dépôt international 20.11.2019
CIB
C22C 38/04 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
04contenant du manganèse
C22C 38/14 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
14contenant du titane ou du zirconium
C22C 38/00 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
B21B 1/46 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
21TRAVAIL MÉCANIQUE DES MÉTAUX SANS ENLÈVEMENT SUBSTANTIEL DE MATIÈRE; DÉCOUPAGE DU MÉTAL À L'EMPORTE-PIÈCE
BLAMINAGE DES MÉTAUX
1Méthodes de laminage ou laminoirs pour la fabrication des produits semi-finis de section pleine ou de profilés; Séquence des opérations dans les trains de laminoirs; Installation d'une usine de laminage, p.ex. groupement de cages; Succession des passes ou des alternances de passes
46pour laminer du métal immédiatement après la coulée continue
B21B 37/74 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
21TRAVAIL MÉCANIQUE DES MÉTAUX SANS ENLÈVEMENT SUBSTANTIEL DE MATIÈRE; DÉCOUPAGE DU MÉTAL À L'EMPORTE-PIÈCE
BLAMINAGE DES MÉTAUX
37Dispositifs ou procédés de commande spécialement adaptés aux laminoirs ou aux produits laminés
74Commande de la température, p.ex. en refroidissant ou en chauffant les cylindres ou le produit
CPC
B21B 1/46
BPERFORMING OPERATIONS; TRANSPORTING
21MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
BROLLING OF METAL
1Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section
46for rolling metal immediately subsequent to continuous casting
B21B 37/74
BPERFORMING OPERATIONS; TRANSPORTING
21MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
BROLLING OF METAL
37Control devices or methods specially adapted for metal-rolling mills or the work produced thereby
74Temperature control, e.g. by cooling or heating the rolls or the product
C22C 38/00
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/04
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
04containing manganese
C22C 38/14
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
14containing titanium or zirconium
Déposants
  • 주식회사 포스코 POSCO [KR]/[KR]
Inventeurs
  • 공종판 KONG, Jong-Pan
  • 고영주 KO, Young-Ju
  • 박경미 PARK, Kyeong-Mi
Mandataires
  • 특허법인 씨엔에스 C&S PATENT AND LAW OFFICE
Données relatives à la priorité
10-2018-014688026.11.2018KR
Langue de publication coréen (KO)
Langue de dépôt coréen (KO)
États désignés
Titre
(EN) ULTRA-HIGH STRENGTH HOT ROLLED STEEL SHEET HAVING EXCELLENT SHAPE QUALITY AND BENDABILITY, AND METHOD FOR MANUFACTURING SAME
(FR) TÔLE D'ACIER LAMINÉE À CHAUD À ULTRA-HAUTE RÉSISTANCE AYANT UNE EXCELLENTE QUALITÉ DE FORME ET UNE EXCELLENTE APTITUDE AU PLIAGE, ET SON PROCÉDÉ DE FABRICATION
(KO) 형상 품질 및 굽힘성이 우수한 초고강도 열연강판 및 그 제조방법
Abrégé
(EN)
The present invention pertains to an ultra-high strength hot rolled steel sheet having excellent shape quality and bendability, and a method for manufacturing same. An embodiment of the present invention provides: an ultra-high strength hot rolled steel sheet having excellent shape quality and bendability, and a method for manufacturing same, the ultra-high strength hot rolled steel sheet containing, in weight %, 0.16-0.26% of C, 0.75-1.50% of Mn, 0.0009-0.0050% of B, 0.009-0.070% of Ti, and 0.001-0.010% of N, with the remainder comprising Fe and miscellaneous inevitable impurities, wherein relational expressions 1 to 3 below are satisfied, and the sum of martensite and tempered martensite constitutes at least 93% and ferrite constitutes 7% or less (including 0%) of the microstructure by area percentage. [relational expression 1] 0.32 ≤ (C+0.2Mn) ≤ 0.53 [relational expression 2] 130 ≤ (C+0.2Mn)/B ≤ 450 [relational expression 3] 5 ≤ (C+0.2Mn)/Ti ≤ 45 (in relational expressions 1 to 3, the contents of C, Mn, B, and Ti are based on wt%)
(FR)
La présente invention concerne une tôle d'acier laminée à chaud à ultra-haute résistance ayant une excellente qualité de forme et une excellente aptitude au pliage, et son procédé de fabrication. Un mode de réalisation de la présente invention concerne : une tôle d'acier laminée à chaud à ultra-haute résistance ayant une excellente qualité de forme et une excellente aptitude au pliage, et son procédé de fabrication, la tôle d'acier laminée à chaud à ultra-haute résistance contenant, en % en poids, 0,16-0,26 % de C, 0,75-1,50 % de Mn, 0,0009-0,0050 % de B, 0,009-0,070 % de Ti, et 0,001-0,010 % de N, le reste comprenant Fe et des impuretés inévitables diverses, les expressions relationnelles 1 à 3 ci-dessous étant satisfaites, et la somme de martensite et de martensite revenue constituant au moins 93 % et la ferrite représentant 7 % ou moins (y compris 0 %) de la microstructure par pourcentage de surface. [expression relationnelle 1] 0,32 ≤ (C+0,2Mn) ≤ 0,53 [expression relationnelle 2] 130 ≤ (C+0,2Mn)/B ≤ 450 [expression relationnelle 3] 5 ≤ (C+0,2Mn)/Ti ≤ 45 (dans les expressions relationnelles 1 à 3, les teneurs en C, Mn, B et Ti sont basées sur des % en poids)
(KO)
본 발명은 형상 품질 및 굽힘성이 우수한 초고강도 열연강판 및 그 제조방법에 관한 것이다. 본 발명의 일 실시형태는 중량%로, C: 0.16~0.26%, Mn: 0.75~1.50%, B: 0.0009~0.0050%, Ti: 0.009~0.070%, N: 0.001~0.010%, 잔부 Fe 및 기타 불가피한 불순물을 포함하고, 하기 관계식 1 내지 3을 만족하며, 면적분율로 마르텐사이트와 템퍼드 마르텐사이트의 합이 93%이상이고, 페라이트가 7%이하(0%를 포함)인 미세조직을 포함하는 형상 품질 및 굽힘성이 우수한 초고강도 열연강판 및 그 제조방법을 제공한다. [관계식 1] 0.32 ≤ (C+0.2Mn) ≤ 0.53 [관계식 2] 130 ≤ (C+0.2Mn)/B ≤ 450 [관계식 3] 5 ≤ (C+0.2Mn)/Ti ≤ 45 (단, 상기 관계식 1 내지 3의 C, Mn, B, Ti의 함량은 중량%임.)