1. WO2020109403 - COMPOSITION DE COUCHE BARRIÈRE AMELIORÉE À BASE D'ALCOOL POLYVINYLIQUE, COUCHE BARRIÈRE ET PROCÉDÉS POUR SA FABRICATION

Numéro de publication WO/2020/109403
Date de publication 04.06.2020
N° de la demande internationale PCT/EP2019/082771
Date du dépôt international 27.11.2019
CIB
C09D 129/04 2006.01
CCHIMIE; MÉTALLURGIE
09COLORANTS; PEINTURES; PRODUITS À POLIR; RÉSINES NATURELLES; ADHÉSIFS; COMPOSITIONS NON PRÉVUES AILLEURS; UTILISATIONS DE SUBSTANCES, NON PRÉVUES AILLEURS
DCOMPOSITIONS DE REVÊTEMENT, p.ex. PEINTURES, VERNIS OU VERNIS-LAQUES; APPRÊTS EN PÂTE; PRODUITS CHIMIQUES POUR ENLEVER LA PEINTURE OU L'ENCRE; ENCRES; CORRECTEURS LIQUIDES; COLORANTS POUR BOIS; PRODUITS SOLIDES OU PÂTEUX POUR COLORIAGE OU IMPRESSION; EMPLOI DE MATÉRIAUX À CET EFFET
129Compositions de revêtement à base d'homopolymères ou de copolymères de composés possédant un ou plusieurs radicaux aliphatiques non saturés, chacun ne contenant qu'une seule liaison double carbone-carbone et l'un au moins étant terminé par un radical alcool, éther, aldéhyde, cétone, acétal ou cétal; Compositions de revêtement à base de polymères hydrolysés d'esters d'alcools non saturés avec des acides carboxyliques saturés; Compositions de revêtement à base de dérivés de tels polymères
02Homopolymères ou copolymères d'alcools non saturés
04Alcool polyvinylique; Homopolymères ou copolymères partiellement hydrolysés d'esters d'alcools non saturés avec des acides carboxyliques saturés
B32B 27/30 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
32PRODUITS STRATIFIÉS
BPRODUITS STRATIFIÉS, c. à d. FAITS DE PLUSIEURS COUCHES DE FORME PLANE OU NON PLANE, p.ex. CELLULAIRE OU EN NID D'ABEILLES
27Produits stratifiés composés essentiellement de résine synthétique
30comprenant une résine vinylique; comprenant une résine acrylique
CPC
B32B 27/30
BPERFORMING OPERATIONS; TRANSPORTING
32LAYERED PRODUCTS
BLAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
27Layered products comprising ; a layer of; synthetic resin
30comprising vinyl ; (co)polymers; comprising acrylic (co)polymers
C08J 5/00
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
JWORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G
5Manufacture of articles or shaped materials containing macromolecular substances
C08L 27/12
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
LCOMPOSITIONS OF MACROMOLECULAR COMPOUNDS
27Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers
02not modified by chemical after-treatment
12containing fluorine atoms
C09D 129/04
CCHEMISTRY; METALLURGY
09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
129Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an alcohol, ether, aldehydo, ketonic, acetal, or ketal radical; Coating compositions based on hydrolysed polymers of esters of unsaturated alcohols with saturated carboxylic acids; Coating compositions based on derivatives of such polymers
02Homopolymers or copolymers of unsaturated alcohols
04Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids
Déposants
  • BILLERUDKORSNÄS AB [SE]/[SE]
Inventeurs
  • NADERI, Ali
Mandataires
  • KRANSELL & WENNBORG KB
Données relatives à la priorité
18208433.527.11.2018EP
18208434.327.11.2018EP
Langue de publication anglais (EN)
Langue de dépôt anglais (EN)
États désignés
Titre
(EN) ENHANCED PVOH-BASED BARRIER LAYER COMPOSITION, BARRIER LAYER AND METHODS FOR ITS MANUFACTURE
(FR) COMPOSITION DE COUCHE BARRIÈRE AMELIORÉE À BASE D'ALCOOL POLYVINYLIQUE, COUCHE BARRIÈRE ET PROCÉDÉS POUR SA FABRICATION
Abrégé
(EN)
There is provided a packaging material comprising a fibre based substrate and a gas barrier layer based on a polyvinyl alcohol (PVOH), wherein said gas barrier layer comprises an interpolymer complex forming agent (IPCFA), which IPCFA is a watersoluble polymer exhibiting functional groups capable of forming hydrogen bonds with -OH groups of the PVOH. Said PVOH has a weight average molecular weight (Mw) measured according to ASTM D4001 - 13 in the range of about 80 kg/mol to 135 kg/mol, the proportion of said IPCFA to PVOH in said gas barrier layer is in the range of 0.5 to 7.0 % (w/w) and said packaging material has an oxygen permeability (OP) below 14 ml μm/m2 day atm, which OP is obtained by multiplying the oxygen transmission rate (OTR) of the packaging material measured according to ASTM F1927-7 at a relative humidity (RH) of 80% and 23 °C by the thickness of the gas barrier layer.
(FR)
L'invention concerne un matériau d'emballage comprenant un substrat à base de fibres et une couche barrière aux gaz à base d'alcool polyvinylique (PVOH), ladite couche barrière aux gaz comprenant un agent de formation de complexe interpolymère (IPCFA), ledit IPCFA étant un polymère soluble dans l'eau présentant des groupes fonctionnels capables de former des liaisons hydrogène avec des groupes -OH de l'alcool polyvinylique. Ledit alcool polyvinylique présente un poids moléculaire moyen en poids (Mw) mesuré selon la norme ASTM D4001 - 13 dans la plage d'environ 80 kg/mol à 135 kg/mol, la proportion dudit IPCFA sur PVOH dans ladite couche barrière aux gaz est dans la plage de 0,5 à 7,0 % (p/p) et ledit matériau d'emballage a une perméabilité à l'oxygène (OP) en dessous de 14 ml µm/m 2 jour atm, ladite OP est obtenue par multiplication du taux de transmission d'oxygène (OTR) du matériau d'emballage mesuré selon la norme ASTM F1927-7 à une humidité relative (RH) de 80 % et 23 °C par l'épaisseur de la couche barrière aux gaz.