1. WO2020067752 - TÔLE D'ACIER LAMINÉE À FROID À HAUTE RÉSISTANCE AYANT UN RAPPORT D'EXPANSION DE TROU ÉLEVÉ, TÔLE D'ACIER GALVANISÉE À CHAUD PAR TREMPE À HAUTE RÉSISTANCE, ET PROCÉDÉS DE FABRICATION ASSOCIÉS

Numéro de publication WO/2020/067752
Date de publication 02.04.2020
N° de la demande internationale PCT/KR2019/012563
Date du dépôt international 27.09.2019
CIB
C22C 38/38 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
38et plus de 1,5% en poids de manganèse
C22C 38/28 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
28et du titane ou du zirconium
C22C 38/32 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
32et du bore
C22C 38/00 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
C22C 38/02 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
02contenant du silicium 
C22C 38/06 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
06contenant de l'aluminium
CPC
C21D 8/02
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
C22C 38/00
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/02
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
02containing silicon
C22C 38/06
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
06containing aluminium
C22C 38/28
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
28with titanium or zirconium
C22C 38/32
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
32with boron
Déposants
  • 주식회사 포스코 POSCO [KR]/[KR]
Inventeurs
  • 임영록 IM, Young-Roc
  • 박종찬 PARK, Jong-Chan
  • 곽재현 KWAK, Jai-Hyun
  • 구민서 KOO, Min-Seo
Mandataires
  • 특허법인 씨엔에스 C&S PATENT AND LAW OFFICE
Données relatives à la priorité
10-2018-011641628.09.2018KR
10-2019-011704423.09.2019KR
Langue de publication coréen (KO)
Langue de dépôt coréen (KO)
États désignés
Titre
(EN) HIGH-STRENGTH COLD ROLLED STEEL SHEET HAVING HIGH HOLE EXPANSION RATIO, HIGH-STRENGTH HOT-DIP GALVANIZED STEEL SHEET, AND MANUFACTURING METHODS THEREFOR
(FR) TÔLE D'ACIER LAMINÉE À FROID À HAUTE RÉSISTANCE AYANT UN RAPPORT D'EXPANSION DE TROU ÉLEVÉ, TÔLE D'ACIER GALVANISÉE À CHAUD PAR TREMPE À HAUTE RÉSISTANCE, ET PROCÉDÉS DE FABRICATION ASSOCIÉS
(KO) 구멍확장성이 높은 고강도 냉연강판, 고강도 용융아연도금강판 및 이들의 제조방법
Abrégé
(EN)
The present invention provides a high-strength cold rolled steel sheet, a high-strength hot-dip galvanized steel sheet manufactured using the cold rolled steel sheet, and manufacturing methods therefor, the high-strength cold rolled steel sheet comprising, by wt%, 0.17-0.21% of carbon (C), 0.3-0.8% of silicon (Si), 2.7-3.3% of manganese (Mn), 0.3-0.7% of chromium (Cr), 0.01-0.3% of aluminum (Al), 0.01-0.03% of titanium (Ti), 0.001-0.003% of boron (B), 0.04% or less of phosphorus (P), 0.02% or less of sulfur (S), 0.01% or less of nitrogen (N) and the balance of iron (Fe) and other inevitable impurities, wherein the amounts of carbon (C), silicon (Si) and aluminum (Al) satisfy the following mathematical relation (1), the microstructure thereof comprises, in area fraction, 3-7% of retained austenite, 5-15% of fresh martensite, 5% or less of ferrite (including 0%) and the balance of bainite or tempered martensite, and 1-3% of a cementite phase as a second phase is precipitated, by volume fraction, and distributed between bainite laths, or in the laths or grain boundary of a tempered martensite phase. [Mathematical relation (1)] [C] + ([Si]+[Al])/5 ≤ 0.35% (wherein [C], [Si] and [Al] respectively mean the wt% of C, Si and Al.)
(FR)
La présente invention concerne une tôle d'acier laminée à froid à haute résistance, une tôle d'acier galvanisée à chaud par trempe à haute résistance fabriquée à l'aide de la tôle d'acier laminée à froid, et des procédés de fabrication associés. La tôle d'acier laminée à froid à haute résistance comprend, en % massiques, de 0,17 à 0,21 % de carbone (C), de 0,3 à 0,8 % de silicium (Si), de 2,7 à 3,3 % de Manganèse (Mn), de 0,3 À 0,7 % de chrome (Cr), de 0,01 à 0,3 % d'aluminium (Al), de 0,01 à 0,03 % de titane (Ti), de 0,001 à 0,003 % de bore (B), 0,04 % ou moins de phosphore (P), 0,02 % ou moins de soufre (S), 0,01 % ou moins d'azote (N) et le reste étant du fer (Fe) et d'autres impuretés inévitables. Les quantités de carbone (C), de silicium (Si) et d'aluminium (Al) satisfont la relation mathématique (1) suivante, la microstructure de celle-ci comprend, en fraction de surface, de 3 à 7 % d'austénite résiduelle, de 5 à 15 % de martensite fraîche, 5 % ou moins de ferrite (y compris 0 %) et le reste étant de la bainite ou de la martensite revenue, et 1-3 % d'une phase de cémentite en tant que deuxième phase est précipitée, par fraction volumique, et distribuée entre des lattes de bainite, ou dans la limite des lattes ou des grains d'une phase martensite revenue. [Relation mathématique (1)] [C] + ([Si]+[Al])/5 ≤ 0,35 % (où [C], [Si] et [Al] représentent respectivement les % massiques de C, Si et Al).
(KO)
본 발명은 중량%로, 탄소(C): 0.17~0.21%, 규소(Si): 0.3~0.8%, 망간(Mn): 2.7~3.3%, 크롬(Cr): 0.3~0.7%, 알루미늄(Al): 0.01~0.3%, 티타늄(Ti): 0.01~0.03%, 보론(B): 0.001~0.003%, 인(P): 0.04% 이하, 황(S): 0.02% 이하, 질소(N): 0.01% 이하, 잔부 철(Fe) 및 기타 불가피한 불순물을 포함하고, 상기 탄소(C), 규소(Si) 및 알루미늄(Al)의 함량은 하기 수학식 (1) 을 만족하고, 미세조직이 면적분율로 잔류 오스테나이트 3~7%, 프레시 마르텐사이트 5~15%, 페라이트 5%이하(0%를 포함), 잔부는 베이나이트 또는 템퍼드 마르텐사이트를 포함하며, 상기 베이나이트 래스(lath) 사이, 또는 템퍼드 마르텐사이트 상의 래스 혹은 결정립 경계에 제 2 상으로서 세멘타이트 상이, 부피분율로 1~3%로 석출하여 분포하는 고강도 냉연강판, 상기 냉연강판을 이용하여 제조한 고강도 용융아연도금강판 및 이들의 제조방법을 제공한다. [수학식 (1)] [C] + ([Si]+[Al])/5 ≤ 0.35% (여기서 [C], [Si], [Al] 는 각각 C, Si, Al의 중량%를 의미한다.)