1. WO2013130718 - COMPOSITIONS DE VERRE DE BOROALUMINOSILICATE SANS ALCALI À FAIBLE COEFFICIENT DE DILATATION THERMIQUE ET ARTICLES EN VERRE L'INTÉGRANT

Numéro de publication WO/2013/130718
Date de publication 06.09.2013
N° de la demande internationale PCT/US2013/028177
Date du dépôt international 28.02.2013
CIB
C03C 3/091 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
CCOMPOSITION CHIMIQUE DES VERRES, GLAÇURES OU ÉMAUX VITREUX; TRAITEMENT DE LA SURFACE DU VERRE; TRAITEMENT DE SURFACE DES FIBRES OU FILAMENTS DE VERRE, DE SUBSTANCES MINÉRALES OU DE SCORIES; LIAISON DU VERRE AU VERRE OU À D'AUTRES MATÉRIAUX
3Compositions pour la fabrication du verre
04contenant de la silice
076avec 40 à 90% en poids de silice
089contenant du bore
091contenant de l'aluminium
C03C 17/02 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
CCOMPOSITION CHIMIQUE DES VERRES, GLAÇURES OU ÉMAUX VITREUX; TRAITEMENT DE LA SURFACE DU VERRE; TRAITEMENT DE SURFACE DES FIBRES OU FILAMENTS DE VERRE, DE SUBSTANCES MINÉRALES OU DE SCORIES; LIAISON DU VERRE AU VERRE OU À D'AUTRES MATÉRIAUX
17Traitement de surface du verre, p.ex. du verre dévitrifié, autre que sous forme de fibres ou de filaments, par revêtement
02par du verre
C03B 17/02 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
BFABRICATION OU FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES;  TRAITEMENTS ADDITIONNELS DANS LA FABRICATION OU LE FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES
17Façonnage du verre par coulée, poussée ou étirage vers le bas ou latéral au travers de fentes ou par écoulement au-dessus de lèvres
02Façonnage de verre recouvert de couches colorées
C03B 17/06 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
BFABRICATION OU FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES;  TRAITEMENTS ADDITIONNELS DANS LA FABRICATION OU LE FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES
17Façonnage du verre par coulée, poussée ou étirage vers le bas ou latéral au travers de fentes ou par écoulement au-dessus de lèvres
06Façonnage de feuilles de verre
CPC
C03B 17/02
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
17Forming ; molten; glass by flowing-out, pushing-out, ; extruding; or drawing downwardly or laterally from forming slits or by overflowing over lips
02Forming ; molten; glass coated with coloured layers; ; Forming molten glass of different compositions or layers; Forming molten glass comprising reinforcements or inserts
C03B 17/064
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
17Forming ; molten; glass by flowing-out, pushing-out, ; extruding; or drawing downwardly or laterally from forming slits or by overflowing over lips
06Forming glass sheets
064by the overflow downdraw fusion process; Isopipes therefor
C03C 3/091
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
3Glass compositions
04containing silica
076with 40% to 90% silica, by weight
089containing boron
091containing aluminium
C03C 3/093
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
3Glass compositions
04containing silica
076with 40% to 90% silica, by weight
089containing boron
091containing aluminium
093containing zinc or zirconium
Y02P 40/57
YSECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
02TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
PCLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
40Technologies relating to the processing of minerals
50Glass production, e.g. reusing waste heat during processing or shaping
57Improving the yield, e-g- reduction of reject rates
Y10T 428/24942
YSECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
10TECHNICAL SUBJECTS COVERED BY FORMER USPC
TTECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
428Stock material or miscellaneous articles
24Structurally defined web or sheet [e.g., overall dimension, etc.]
24942including components having same physical characteristic in differing degree
Déposants
  • CORNING INCORPORATED [US]/[US]
Inventeurs
  • MAURO, John, Christopher
Mandataires
  • HOMA, Joseph, M.
Données relatives à la priorité
61/604,83929.02.2012US
Langue de publication anglais (EN)
Langue de dépôt anglais (EN)
États désignés
Titre
(EN) LOW CTE ALKALI-FREE BOROALUMINOSILICATE GLASS COMPOSITIONS AND GLASS ARTICLES COMPRISING THE SAME
(FR) COMPOSITIONS DE VERRE DE BOROALUMINOSILICATE SANS ALCALI À FAIBLE COEFFICIENT DE DILATATION THERMIQUE ET ARTICLES EN VERRE L'INTÉGRANT
Abrégé
(EN)
Low CTE glass compositions and glass articles formed from the same are described. In one embodiment, a glass composition includes from about 60 mol.% to about 66 mol.% SiO2; from about 7 mol.% to about 10 mol.% AI2O3; and from about 14 mol.% to about 18 mol.% B2O3 as glass network formers. The glass composition may further include from about 9 mol.% to about 16 mol.% alkaline earth oxide. The alkaline earth oxide includes at least CaO. The CaO may be present in the glass composition in a concentration from about 3 mol.% to about 12 mol.%. The glass composition is free from alkali metals. The glass composition has a coefficient of thermal expansion which is less than or equal to 40x10-7/°C averaged over the temperature range from about 20°C to 300°C. The glass composition is particularly well suited for use as a glass cladding layer in a laminated glass article.
(FR)
La présente invention concerne des compositions de verre à faible coefficient de dilatation thermique et des articles en verre constitués de ladite composition. Dans un mode de réalisation, une composition de verre contient d'environ 60 % en mole à environ 66 % en mole de SiO2 ; d'environ 7 % en mole à environ 10 % en mole de AI2O3 ; et d'environ 14 % en mole à environ 18 % en mole de B2O3 faisant office d'agents formateurs de la structure vitreuse. La composition de verre peut en outre contenir d'environ 9 % en mole à environ 16 % en mole d'oxyde alcalino-terreux. L'oxyde alcalino-terreux contient au moins du CaO. Le CaO peut être présent dans la composition de verre en une concentration d'environ 3 % en mole à environ 12 % en mole. La composition de verre ne contient pas de métal alcalin. La composition de verre a un coefficient de dilatation thermique inférieur ou égal à 40x10-7/°C en moyenne sur la plage de température d'environ 20 °C à 300 °C. La composition de verre convient particulièrement bien pour une utilisation à titre de couche de placage de verre dans un article en verre feuilleté.