1. WO2012002177 - AGENT DE DURCISSEMENT LATENT À BASE DE CHÉLATE D'ALUMINIUM

Numéro de publication WO/2012/002177
Date de publication 05.01.2012
N° de la demande internationale PCT/JP2011/063930
Date du dépôt international 17.06.2011
CIB
C08G 85/00 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
GCOMPOSÉS MACROMOLÉCULAIRES OBTENUS PAR DES RÉACTIONS AUTRES QUE CELLES FAISANT INTERVENIR UNIQUEMENT DES LIAISONS NON SATURÉES CARBONE-CARBONE
85Procédés généraux pour la préparation des composés prévus dans la présente sous-classe
C08G 18/02 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
GCOMPOSÉS MACROMOLÉCULAIRES OBTENUS PAR DES RÉACTIONS AUTRES QUE CELLES FAISANT INTERVENIR UNIQUEMENT DES LIAISONS NON SATURÉES CARBONE-CARBONE
18Polymérisats d'isocyanates ou d'isothiocyanates
02d'isocyanates ou d'isothiocyanates uniquement
C08G 59/70 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
GCOMPOSÉS MACROMOLÉCULAIRES OBTENUS PAR DES RÉACTIONS AUTRES QUE CELLES FAISANT INTERVENIR UNIQUEMENT DES LIAISONS NON SATURÉES CARBONE-CARBONE
59Polycondensats contenant plusieurs groupes époxyde par molécule; Macromolécules obtenues par réaction de polycondensats polyépoxydés avec des composés monofonctionnels à bas poids moléculaire; Macromolécules obtenues par polymérisation de composés contenant plusieurs groupes époxyde par molécule en utilisant des agents de durcissement ou des catalyseurs qui réagissent avec les groupes époxyde
18Macromolécules obtenues par polymérisation à partir de composés contenant plusieurs groupes époxyde par molécule en utilisant des agents de durcissement ou des catalyseurs qui réagissent avec les groupes époxyde
68caractérisées par les catalyseurs utilisés
70Chélates
C08G 65/18 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
GCOMPOSÉS MACROMOLÉCULAIRES OBTENUS PAR DES RÉACTIONS AUTRES QUE CELLES FAISANT INTERVENIR UNIQUEMENT DES LIAISONS NON SATURÉES CARBONE-CARBONE
65Composés macromoléculaires obtenus par des réactions créant une liaison éther dans la chaîne principale de la macromolécule
02à partir d'éthers cycliques par ouverture d'un hétérocycle
04uniquement à partir d'éthers cycliques
06Ethers cycliques ne possédant en dehors du cycle que des atomes de carbone et d'hydrogène
16Ethers cycliques possédant au moins quatre atomes dans le cycle
18Oxétanes
C08K 5/07 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
KEMPLOI COMME ADJUVANTS DE SUBSTANCES NON MACROMOLÉCULAIRES INORGANIQUES OU ORGANIQUES
5Emploi d'ingrédients organiques
04Composés contenant de l'oxygène
07Aldéhydes; Cétones
C08K 5/5419 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
KEMPLOI COMME ADJUVANTS DE SUBSTANCES NON MACROMOLÉCULAIRES INORGANIQUES OU ORGANIQUES
5Emploi d'ingrédients organiques
54Composés contenant du silicium
541contenant de l'oxygène
5415contenant au moins une liaison Si-O
5419contenant au moins une liaison Si-C
CPC
C08G 18/0866
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
18Polymeric products of isocyanates or isothiocyanates
06with compounds having active hydrogen
08Processes
0838Manufacture of polymers in the presence of non-reactive compounds
0842in the presence of liquid diluents
0861in the presence of a dispersing phase for the polymers or a phase dispersed in the polymers
0866the dispersing or dispersed phase being an aqueous medium
C08G 18/6212
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
18Polymeric products of isocyanates or isothiocyanates
06with compounds having active hydrogen
28characterised by the compounds used containing active hydrogen
40High-molecular-weight compounds
62Polymers of compounds having carbon-to-carbon double bonds
6212Polymers of alkenylalcohols; Acetals thereof; Oxyalkylation products thereof
C08G 18/8029
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
18Polymeric products of isocyanates or isothiocyanates
06with compounds having active hydrogen
70characterised by the isocyanates or isothiocyanates used
72Polyisocyanates or polyisothiocyanates
80Masked polyisocyanates
8003masked with compounds having at least two groups containing active hydrogen
8006with compounds of C08G18/32
8009with compounds of C08G18/3203
8022with polyols having at least three hydroxy groups
8029Masked aromatic polyisocyanates
C08G 59/188
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
59Polycondensates containing more than one epoxy group per molecule
18Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; ; e.g. general methods of curing
188using encapsulated compounds
C08G 59/70
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
59Polycondensates containing more than one epoxy group per molecule
18Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; ; e.g. general methods of curing
68characterised by the catalysts used
70Chelates
C08G 65/18
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
65Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
02from cyclic ethers by opening of the heterocyclic ring
04from cyclic ethers only
06Cyclic ethers having no atoms other than carbon and hydrogen outside the ring
16Cyclic ethers having four or more ring atoms
18Oxetanes
Déposants
  • ソニーケミカル&インフォメーションデバイス株式会社 SONY CHEMICAL & INFORMATION DEVICE CORPORATION [JP/JP]; 東京都品川区大崎一丁目11番2号 ゲートシティ大崎イーストタワー8階 Gate City Osaki East Tower 8F., 1-11-2, Osaki, Shinagawa-ku, Tokyo 1410032, JP (AllExceptUS)
  • 神谷 和伸 KAMIYA Kazunobu [JP/JP]; JP (UsOnly)
Inventeurs
  • 神谷 和伸 KAMIYA Kazunobu; JP
Mandataires
  • 特許業務法人 田治米国際特許事務所 TAJIME & TAJIME; 神奈川県川崎市多摩区三田1-26-28 ニューウェル生田ビル201号室 Room No. 201, New-Well-Ikuta Bldg., 26-28, Mita 1-chome, Tama-ku, Kawasaki-shi, Kanagawa 2140034, JP
Données relatives à la priorité
2010-14646828.06.2010JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) ALUMINUM CHELATE-BASED LATENT CURING AGENT
(FR) AGENT DE DURCISSEMENT LATENT À BASE DE CHÉLATE D'ALUMINIUM
(JA) アルミニウムキレート系潜在性硬化剤
Abrégé
(EN)
Disclosed is a novel aluminum chelate-based latent curing agent having a core-shell type microcapsule structure, wherein an aluminum chelate-based curing agent and a cationic polymerizable compound are enclosed in capsules formed of an interfacial polymerization product of a polyfunctional isocyanate. This aluminum chelate-based latent curing agent can cure a glycidyl ether type epoxy compound at a lower temperature and higher speed, compared with an aluminum chelate-based latent curing agent which is produced through emulsion/interfacial polymerization of a polyfunctional isocyanate in the coexistence of a radical polymerizable-monomer, such as divinylbenzene, and a radical polymerization initiator.
(FR)
La présente invention concerne un nouvel agent de durcissement latent à base de chélate d'aluminium qui possède une structure de microcapsule de type cœur-écorce, un agent de durcissement à base de chélate d'aluminium et un composé polymérisable cationique étant enfermés dans des capsules formées d'un produit de polymérisation interfaciale d'un isocyanate polyfonctionnel. Ledit agent de durcissement latent à base de chélate d'aluminium peut durcir un composé époxy de type éther de glycidyle, à une température inférieure et à une vitesse supérieure à celles d'un agent de durcissement latent à base de chélate d'aluminium qui est produit par polymérisation d'émulsion/interfaciale d'un isocyanate polyfonctionnel coexistant avec un monomère polymérisable par voie radicalaire, tel que le divinylbenzène, et un initiateur de polymérisation par voie radicalaire.
(JA)
 ジビニルベンゼン等のラジカル重合性モノマーとラジカル重合開始剤とを共存下で多官能イソシアネートの乳化・界面重合により製造したアルミニウムキレート系潜在性硬化剤よりも、グリシジルエーテル型エポキシ化合物をより低温速硬化できる新規なアルミニウムキレート系潜在性硬化剤は、コアシェル型にマイクロカプセル化されたものであって、アルミニウムキレート系硬化剤とカチオン重合性化合物とが、多官能イソシアネートの界面重合物からなるカプセルに内包されているものである。