1. WO2012001971 - PROCÉDÉ DE PRODUCTION D'UNE TÔLE D'ACIER MAGNÉTIQUE À GRAINS ORIENTÉS

Numéro de publication WO/2012/001971
Date de publication 05.01.2012
N° de la demande internationale PCT/JP2011/003724
Date du dépôt international 29.06.2011
CIB
C21D 8/12 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
12pendant la fabrication d'objets à propriétés électromagnétiques particulières
B21B 3/02 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
21TRAVAIL MÉCANIQUE DES MÉTAUX SANS ENLÈVEMENT SUBSTANTIEL DE MATIÈRE; DÉCOUPAGE DU MÉTAL À L'EMPORTE-PIÈCE
BLAMINAGE DES MÉTAUX
3Laminage des matériaux faits d'alliages particuliers dans la mesure où la nature de l'alliage exige ou permet l'emploi de méthodes ou de séquences particulières
02Laminage des alliages ferreux particuliers
B23K 26/00 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
23MACHINES-OUTILS; TRAVAIL DES MÉTAUX NON PRÉVU AILLEURS
KBRASAGE OU DÉBRASAGE; SOUDAGE; REVÊTEMENT OU PLACAGE PAR BRASAGE OU SOUDAGE; DÉCOUPAGE PAR CHAUFFAGE LOCALISÉ, p.ex. DÉCOUPAGE AU CHALUMEAU; TRAVAIL PAR RAYON LASER
26Travail par rayon laser, p.ex. soudage, découpage ou perçage 
C21D 9/46 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9Traitement thermique, p.ex. recuit, durcissement, trempe ou revenu, adapté à des objets particuliers; Fours à cet effet
46pour tôles
C22C 38/00 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
C22C 38/04 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
04contenant du manganèse
CPC
C21D 10/005
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
10Modifying the physical properties by methods other than heat treatment or deformation
005by laser shock processing
C21D 2201/05
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2201Treatment for obtaining particular effects
05Grain orientation
C21D 8/1222
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
12during manufacturing of articles with special electromagnetic properties
1216the working step(s) being of interest
1222Hot rolling
C21D 8/1233
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
12during manufacturing of articles with special electromagnetic properties
1216the working step(s) being of interest
1233Cold rolling
C21D 8/1255
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
12during manufacturing of articles with special electromagnetic properties
1244the heat treatment(s) being of interest
1255with diffusion of elements, e.g. decarburising, nitriding
C21D 8/1261
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
12during manufacturing of articles with special electromagnetic properties
1244the heat treatment(s) being of interest
1261following hot rolling
Déposants
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP/JP]; 東京都千代田区内幸町二丁目2番3号 2-3, Uchisaiwai-cho 2-chome, Chiyoda-ku, Tokyo 1000011, JP (AllExceptUS)
  • 山口 広 YAMAGUCHI, Hiroi [JP/JP]; JP (UsOnly)
  • 岡部 誠司 OKABE, Seiji [JP/JP]; JP (UsOnly)
  • 千田 邦浩 SENDA, Kunihiro [JP/JP]; JP (UsOnly)
  • 大村 健 OMURA, Takeshi [JP/JP]; JP (UsOnly)
Inventeurs
  • 山口 広 YAMAGUCHI, Hiroi; JP
  • 岡部 誠司 OKABE, Seiji; JP
  • 千田 邦浩 SENDA, Kunihiro; JP
  • 大村 健 OMURA, Takeshi; JP
Mandataires
  • 杉村 憲司 SUGIMURA, Kenji; 東京都千代田区霞が関三丁目2番1号 霞が関コモンゲート西館36階 36F, Kasumigaseki Common Gate West, 3-2-1, Kasumigaseki, Chiyoda-ku, Tokyo 1000013, JP
Données relatives à la priorité
2010-15015230.06.2010JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) PROCESS FOR PRODUCING GRAIN-ORIENTED MAGNETIC STEEL SHEET
(FR) PROCÉDÉ DE PRODUCTION D'UNE TÔLE D'ACIER MAGNÉTIQUE À GRAINS ORIENTÉS
(JA) 方向性電磁鋼板の製造方法
Abrégé
(EN)
Disclosed is a process for producing a grain-oriented magnetic steel sheet, the process comprising production steps that includes a final finish annealing step in which a forsterite coating film is formed on a surface of the steel sheet in an amount of 4.0 g/m2 or more so as to have an average grain diameter of 0.9 µm or less and in which the steel sheet is regulated so as to have a magnetic flux density (B8) of 1.91 T or higher. Laser light having a wavelength of 0.2-0.9 µm is repeatedly irradiated upon the resultant grain-oriented magnetic steel sheet along a linear direction which intersects the rolling direction of the steel sheet. Thus, the grain-oriented magnetic steel sheet can be further reduced in iron loss as compared with conventional grain-oriented magnetic steel sheets.
(FR)
L'invention concerne un procédé de production d'une tôle d'acier magnétique à grains orientés qui comprend une étape finale de recuit de finition dans laquelle un revêtement de forstérite est formé sur une surface de la tôle d'acier dans une quantité d'au moins 4,0 g/m2 de manière à obtenir un diamètre moyen des grains de 0,9 µm ou moins, et dans lequel la tôle d'acier est ajustée de manière à obtenir une densité de flux magnétique (B8) d'au moins 1,91 T. Une lumière laser ayant une longueur d'onde de 0,2-0,9 µm est envoyée de façon répétée sur la tôle d'acier magnétique à grains orientés résultante dans une direction linéaire qui coupe la direction de laminage de la tôle d'acier. Ainsi, la perte de fer de la tôle d'acier magnétique à grains orientés peut encore être réduite par rapport aux tôles d'acier magnétique à grains orientés classiques.
(JA)
 方向性電磁鋼板の製造工程中、最終仕上げ焼鈍工程において、鋼板表面に形成されるフォルステライト被膜の目付量を4.0g/m2以上、平均粒径を0.9μm以下とし、かつ磁束密度B8を1.91T以上とした方向性電磁鋼板に対して、波長が0.2μm以上、0.9μm以下のレーザー光を、鋼板の圧延方向と交差する方向に線状に繰り返して照射することにより、方向性電磁鋼板の鉄損を従来に比べて一層に低減させることができる。