1. WO2009107690 - PROCÉDÉ DE FABRICATION D'UN POLYMÈRE OLÉFINIQUE MODIFIÉ

Numéro de publication WO/2009/107690
Date de publication 03.09.2009
N° de la demande internationale PCT/JP2009/053478
Date du dépôt international 19.02.2009
CIB
C08F 8/46 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
FCOMPOSÉS MACROMOLÉCULAIRES OBTENUS PAR DES RÉACTIONS FAISANT INTERVENIR UNIQUEMENT DES LIAISONS NON SATURÉES CARBONE-CARBONE
8Modification chimique par post-traitement
46Réaction avec des acides dicarboxyliques non saturés ou avec leurs anhydrides, p.ex. maléinisation
C08F 4/6592 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
FCOMPOSÉS MACROMOLÉCULAIRES OBTENUS PAR DES RÉACTIONS FAISANT INTERVENIR UNIQUEMENT DES LIAISONS NON SATURÉES CARBONE-CARBONE
4Catalyseurs de polymérisation
42Métaux; Hydrures métalliques; Composés organiques de métal; Leur utilisation comme précurseurs de catalyseurs
44choisis parmi les métaux légers, le zinc, le cadmium, le mercure, le cuivre, l'argent, l'or, le bore, le gallium, l'indium, le thallium, les terres rares ou les actinides
60en mélange avec des métaux réfractaires, des métaux du groupe du fer, des métaux du groupe du platine, du manganèse, technétium, rhénium ou leurs composés
62Métaux réfractaires ou leurs composés
64Titane, zirconium, hafnium ou leurs composés
659Composant couvert par le groupe C08F4/6460
6592contenant au moins un cycle cyclopentadiényle, condensé ou non, p.ex. un cycle indényle ou fluorényle
CPC
C08F 10/00
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
FMACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
10Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
C08F 255/02
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
FMACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
255Macromolecular compounds obtained by polymerising monomers on to polymers of hydrocarbons as defined in group C08F10/00
02on to polymers of olefins having two or three carbon atoms
C08L 2314/06
CCHEMISTRY; METALLURGY
08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
LCOMPOSITIONS OF MACROMOLECULAR COMPOUNDS
2314Polymer mixtures characterised by way of preparation
06Metallocene or single site catalysts
Déposants
  • 住友化学株式会社 SUMITOMO CHEMICAL COMPANY, LIMITED [JP]/[JP] (AllExceptUS)
  • 津久井仁 TSUKUI, Hitoshi [JP]/[JP] (UsOnly)
  • 武井豪志 TAKEI, Tsuyoshi [JP]/[JP] (UsOnly)
Inventeurs
  • 津久井仁 TSUKUI, Hitoshi
  • 武井豪志 TAKEI, Tsuyoshi
Mandataires
  • 中山亨 NAKAYAMA, Tohru
Données relatives à la priorité
2008-04951129.02.2008JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) PROCESS FOR PRODUCING MODIFIED OLEFIN POLYMER
(FR) PROCÉDÉ DE FABRICATION D'UN POLYMÈRE OLÉFINIQUE MODIFIÉ
(JA) 変性オレフィン重合体の製造方法
Abrégé
(EN)
A process for producing a modified olefin polymer which comprises the following steps: (1) a step in which 100 parts by weight of an olefin polymer, 0.01-20 parts by weight of an unsaturated compound having a polar group, and 0.001-20 parts by weight of an organic peroxide are mixed together in a continuous extruder at a temperature (T1) not higher than a decomposition temperature (Th1) at which the organic peroxide has a half-life period of 1 hour, for a time period (S1) shorter than the half-life period (Sh1) of the organic peroxide as measured at the temperature (T1), whereby a first mixture is produced; (2) a step in which the first mixture is kneaded in the continuous extruder at a temperature (T2) not lower than a decomposition temperature (Th2) at which the organic peroxide has a half-life period of 10 seconds, for a time period (S2) which is at least three times the half-life period (Sh2) of the organic oxide as measured at the temperature (T2), whereby a second mixture is produced; and (3) a step in which the second mixture is kneaded in the continuous extruder at a temperature (T3) not higher than a decomposition temperature (Th3) at which the organic peroxide has a half-life period of 10 hours, for a time period (S3) not shorter than the time period (S2).
(FR)
L'invention concerne un procédé de fabrication d'un polymère oléfinique modifié qui comprend les étapes suivantes : (1) une étape lors de laquelle 100 parties en poids d'un polymère oléfinique, 0,01 à 20 parties en poids d'un composé insaturé contenant un groupe polaire et 0,001 à 20 parties en poids d'un peroxyde organique sont mélangées dans une extrudeuse continue à une température (T1) inférieure ou égale à une température de décomposition (Th1) à laquelle le peroxyde organique présente une période de demi-vie d'une heure, pendant une durée (S1) inférieure à la période de demi-vie (Sh1) du peroxyde organique telle que mesurée à la température (T1), un premier mélange étant obtenu ; (2) une étape lors de laquelle le premier mélange est malaxé dans l'extrudeuse continue à une température (T2) supérieure ou égale à une température de décomposition (Th2) à laquelle le peroxyde organique présente une période de demi-vie de 10 secondes, pendant une durée (S2) qui est au moins trois fois la période de demi-vie (Sh2) du peroxyde organique telle que mesurée à la température (T2), un second mélange étant obtenu ; et (3) une étape lors de laquelle le second mélange est malaxé dans l'extrudeuse continue à une température (T3) inférieure ou égale à une température de décomposition (Th3) à laquelle le peroxyde organique présente une période de demi-vie de 10 heures, pendant une durée (S3) supérieure ou égale à la durée (S2).
(JA)
以下の工程からなる変性オレフィン重合体の製造方法:(1)オレフィン重合体100重量部と、極性基を有する不飽和化合物0.01~20重量部と、有機過酸化物0.001~20重量部とを、有機過酸化物の半減時間が1時間である分解温度(Th1)以下の温度(T1)で、温度(T1)での該有機過酸化物の半減時間(Sh1)未満の時間(S1)、連続式押出機内で混合して第1の混合物を生成させる工程;(2)第1の混合物を、該有機過酸化物の半減時間が10秒である分解温度(Th2)以上の温度(T2)で、温度(T2)での該有機過酸化物の半減時間(Sh2)の3倍以上の時間(S2)、該連続式押出機内で混合して第2の混合物を生成させる工程;および(3)第2の混合物を、該有機過酸化物の半減時間が10時間である分解温度(Th3)以下の温度(T3)で、上記時間(S2)以上の時間(S3)、該連続式押出機内で混合する工程。