Traitement en cours

Veuillez attendre...

PATENTSCOPE sera indisponible durant quelques heures pour des raisons de maintenance le dimanche 05.04.2020 à 10:00 AM CEST
Paramétrages

Paramétrages

1. WO2007142116 - PROCÉDÉ DE FABRICATION DE PARTICULES D'OXYDE MÉTALLIQUE

Numéro de publication WO/2007/142116
Date de publication 13.12.2007
N° de la demande internationale PCT/JP2007/061085
Date du dépôt international 31.05.2007
CIB
C01G 25/00 2006.01
CCHIMIE; MÉTALLURGIE
01CHIMIE INORGANIQUE
GCOMPOSÉS CONTENANT DES MÉTAUX NON COUVERTS PAR LES SOUS-CLASSES C01D OU C01F104
25Composés du zirconium
H01M 8/02 2006.01
HÉLECTRICITÉ
01ÉLÉMENTS ÉLECTRIQUES FONDAMENTAUX
MPROCÉDÉS OU MOYENS POUR LA CONVERSION DIRECTE DE L'ÉNERGIE CHIMIQUE EN ÉNERGIE ÉLECTRIQUE, p.ex. BATTERIES
8Éléments à combustible; Leur fabrication
02Détails
CPC
C01G 1/02
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
1Methods of preparing compounds of metals not covered by subclasses C01B, C01C, C01D, or C01F, in general
02Oxides
C01G 25/00
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
25Compounds of zirconium
C01G 25/02
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
25Compounds of zirconium
02Oxides
C01P 2006/12
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
2006Physical properties of inorganic compounds
12Surface area
C01P 2006/40
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
2006Physical properties of inorganic compounds
40Electric properties
H01M 8/124
HELECTRICITY
01BASIC ELECTRIC ELEMENTS
MPROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
8Fuel cells; Manufacture thereof
10Fuel cells with solid electrolytes
12operating at high temperature, e.g. with stabilised ZrO2 electrolyte
124characterised by the process of manufacturing or by the material of the electrolyte
Déposants
  • 日産化学工業株式会社 NISSAN CHEMICAL INDUSTRIES, LTD. [JP/JP]; 〒1010054 東京都千代田区神田錦町3丁目7番地1 Tokyo 7-1, Kanda-Nishiki-cho 3-chome, Chiyoda-ku Tokyo 1010054, JP (AllExceptUS)
  • 大森 豊 OHMORI, Yutaka [JP/JP]; JP (UsOnly)
  • 加藤 博和 KATO, Hirokazu [JP/JP]; JP (UsOnly)
  • 山口 健二 YAMAGUCHI, Kenji [JP/JP]; JP (UsOnly)
Inventeurs
  • 大森 豊 OHMORI, Yutaka; JP
  • 加藤 博和 KATO, Hirokazu; JP
  • 山口 健二 YAMAGUCHI, Kenji; JP
Mandataires
  • 萼 経夫 HANABUSA, Tsuneo; 〒1010062 東京都千代田区神田駿河台3丁目2番地 新御茶ノ水アーバントリニティ 萼特許事務所内 Tokyo c/o Hanabusa Patent Office, Shin-Ochanomizu Urban Trinity, 2, Kandasurugadai 3-chome, Chiyoda-ku Tokyo 1010062, JP
Données relatives à la priorité
2006-15577905.06.2006JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) METHOD FOR PRODUCING METAL OXIDE PARTICLE
(FR) PROCÉDÉ DE FABRICATION DE PARTICULES D'OXYDE MÉTALLIQUE
(JA) 金属酸化物粒子の製造方法
Abrégé
(EN)
Disclosed is a method for stably producing a metal oxide solid solution particle at low temperature, wherein an alkaline zirconia sol is used as a raw material which is mixed with a metal compound, and then dried and fired. Specifically disclosed is a method for producing metal oxide particles (A3) such as zirconia particles wherein a metal oxide is solid-solubilized. The method comprises a step (I) for obtaining a sol of a metal oxide (A2) such as zirconia containing a precursor of the metal oxide by mixing an alkaline zirconia sol (A1), which is obtained by a method comprising a step (i) for heating a zirconium salt (B2) at 60-110˚C in an aqueous medium containing a carbonate of quaternary ammonium and a step (ii) for performing a hydrothermal treatment at 110-250˚C, with a compound (B1) containing an element selected from group II and group III elements of the periodic table; and a step (II) for drying the thus-obtained sol and then firing the resulting at a temperature of 500-1200˚C.
(FR)
L'invention concerne un procédé de fabrication de manière stable de particules de solution solide d'oxyde métallique à basse température, un sol de zircone alcalin étant utilisé en tant que matière première qui est mélangée avec un composé métallique, puis séchée et brûlée. L'invention concerne spécifiquement un procédé de fabrication de particules d'oxyde métallique (A3) telles que des particules de zircone, selon lequel un oxyde métallique est solubilisé dans un solide. Le procédé comprend une étape (I) consistant à obtenir un sol d'un oxyde métallique (A2) tel que la zircone contenant un précurseur de l'oxyde métallique en mélangeant un sol de zircone alcalin (A1), qui est obtenu par un procédé comprenant une étape (i) consistant à chauffer un sel de zirconium (B2) à 60-110 °C dans un milieu aqueux contenant un carbonate d'ammonium quaternaire et une étape (ii) consistant à réaliser un traitement hydrothermal à 110-250 °C, avec un composé (B1) contenant un élément choisi parmi les éléments des groupes II et III du tableau périodique ; et une étape (II) consistant à sécher le sol ainsi obtenu et à brûler le produit résultant à une température de 500-1200 °C.
(JA)
【課題】アルカリ性のジルコニアゾルを原料に用い、金属化合物と混合し、乾燥、焼成することにより、低温で安定に金属酸化物固溶体粒子を製造する方法を提供する。 【解決手段】第4級アンモニウムの炭酸塩を含む水性媒体中でジルコニウム塩(B2)を60~110°Cで加熱する工程(i)と、110~250°Cで水熱処理を行う工程(ii)とを含む方法により得られたアルカリ性ジルコニア(A1)ゾルと、周期律表のII族及びIII族から成る群より選ばれた元素を含む化合物(B1)とを混合し、金属酸化物の前駆体を含むジルコニア等の金属酸化物(A2)ゾルを得る工程(I)、得られた該ゾルを乾燥し、500~1200°Cの温度で焼成する工程(II)を含む、金属酸化物が固溶したジルコニア粒子等の金属酸化物粒子(A3)の製造方法である。