1. WO2007138815 - ACIER INOXYDABLE AUSTÉNITIQUE

Numéro de publication WO/2007/138815
Date de publication 06.12.2007
N° de la demande internationale PCT/JP2007/059094
Date du dépôt international 26.04.2007
CIB
C22C 38/00 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
C22C 38/58 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
58et plus de 1,5% en poids de manganèse
CPC
C22C 38/001
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
001containing N
C22C 38/02
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
02containing silicon
C22C 38/04
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
04containing manganese
C22C 38/44
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
44with molybdenum or tungsten
C22C 38/46
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
46with vanadium
C22C 38/48
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
48with niobium or tantalum
Déposants
  • 住友金属工業株式会社 SUMITOMO METAL INDUSTRIES, LTD. [JP/JP]; 〒5410041 大阪府大阪市中央区北浜四丁目5番33号 Osaka 5-33, Kitahama 4-chome, Chuo-ku, Osaka-shi, Osaka 5410041, JP (AllExceptUS)
  • 竹田 貴代子 TAKEDA, Kiyoko [JP/JP]; JP (UsOnly)
  • 相良 雅之 SAGARA, Masayuki [JP/JP]; JP (UsOnly)
  • 照沼 正明 TERUNUMA, Masaaki [JP/JP]; JP (UsOnly)
Inventeurs
  • 竹田 貴代子 TAKEDA, Kiyoko; JP
  • 相良 雅之 SAGARA, Masayuki; JP
  • 照沼 正明 TERUNUMA, Masaaki; JP
Mandataires
  • 杉岡 幹二 SUGIOKA, Kanji; 〒6600892 兵庫県尼崎市東難波町五丁目17番23号 尼崎ビル 杉岡特許事務所 Hyogo K. Sugioka Patent Office, Amagasaki Building, 5-17-23, Higashinaniwa-cho, Amagasaki-shi, Hyogo 6600892, JP
Données relatives à la priorité
2006-15012230.05.2006JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) AUSTENITIC STAINLESS STEEL
(FR) ACIER INOXYDABLE AUSTÉNITIQUE
(JA) オーステナイト系ステンレス鋼
Abrégé
(EN)
An austenitic stainless steel which contains, by mass, C: 0.10% or below, Si: 0.01 to 1.0%, Mn: 0.01 to 2%, Cr: 16 to 18%, Ni: more than 10% and less than 14%, Mo: more than 2.0% and up to 3.0%, N: 0.03 to 0.10%, and one or more of V, Nb and Ti in amounts satisfying the relationships (1) and (2) with the balance consisting of Fe and impurities and in which the contents of P and S as impurities are 0.04% or below and 0.003% or below respectively: 0.0013 ≤ (V/51) + (Nb/93) + (Ti/48) ≤ 0.0025 ... (1) {(C/12)+(N/14)} – {(V/51)+(Nb/93)+(Ti/48)} ≤ 0.0058...(2) (wherein each atomic symbol represents the content (% by weight) thereof). The stainless steel is excellent in corrosion resistance, particularly in intergranular corrosion resistance. It is preferable that the contents of Nb and Ti be 0.030% or below and 0.050% or below respectively.
(FR)
La présente invention concerne un acier inoxydable austénitique qui contient, en masse, C : 0,10 % ou moins, Si : de 0,01 à 1,0 %, Mn : de 0,01 à 2 %, Cr : de 16 à 18 %, Ni : plus de 10 % et moins de 14 %, Mo : plus de 2,0 % et jusqu'à 3,0 %, N : de 0,03 à 0,10 %, et un ou plusieurs éléments parmi V, Nb et Ti en quantité satisfaisant aux relations (1) et (2), le reste étant constitué de Fe et d'impuretés et dans lequel la teneur en P et S en tant qu'impuretés est de 0,04 % ou moins et 0,003 % ou moins, respectivement : 0,0013 ≤ (V/51) + (Nb/93) + (Ti/48) ≤ 0,0025... (1) {(C/12) + (N/14)} – {(V/51) + (Nb/93) + (Ti/48)} ≤ 0,0058... (2) (où chaque symbole atomique représente la concentration (pourcentage en poids) de celui-ci). L'acier inoxydable présente d'excellentes propriétés de résistance à la corrosion, et particulièrement de résistance à la corrosion intergranulaire. Il est préférable que les teneurs en Nb et Ti soient de 0,030 % ou moins et de 0,050 % ou moins, respectivement.
(JA)
 質量%で、C:0.10%以下、Si:0.01~1.0%、Mn:0.01~2%、Cr:16~18%、Ni:10%を超えて14%未満、Mo:2.0%を超えて3.0%以下、N:0.03~0.10%、ならびにV、NbおよびTiの1種または2種以上を下記(1)式および(2)式を満たす量で含み、残部がFeおよび不純物からなり、不純物であるPが0.04%以下、Sが0.003%以下であるオーステナイト系ステンレス鋼は、耐食性、特に耐粒界腐食性に優れている。    0.0013≦(V/51)+(Nb/93)+(Ti/48)≦0.0025・・・(1)   {(C/12)+(N/14)}-{(V/51)+(Nb/93)+(Ti/48)}≦0.0058・・・(2)  ただし、(1)式および(2)式の中の元素記号は、その元素の含有量(質量%)である。 なお、Nbは0.030%以下、Tiは0.050%以下であることが望ましい。