1. WO1991015532 - COMPOSITIONS DE POUDRES POUR REVETEMENT

Note: Texte fondé sur des processus automatiques de reconnaissance optique de caractères. Seule la version PDF a une valeur juridique

[ EN ]

CLAIMS
We claim:
1. A thermosetting coating composition in the form of a powder having an average particle size of about 10 to 300 microns comprising:
(1) a hydroxyl polyester component comprised of a semi- crystalline polyester having a Tg of less than
50°C, a hydroxyl number of about 20 to 100, an
inherent viscosity of about 0.1 to 0.5, a melting range of about 70 to 150°C, a number average
molecular weight of about 1500 to 10,000 and a heat of fusion (second heating cycle of DSC) of greater than about 5 cal/g-°C, e.g. 5 to about 20 cal/g-°C; and
(2) a cross-linking effective amount of an ε-caprolactam-blocked bis (1-isocyanato-1-methylethyl)- benzene.

2. A thermosetting coating composition according to Claim 1 comprising:
(1) a hydroxyl polyester component comprised of:
(A) 100 to 15 weight percent, based on the weight of the hydroxyl polyester component, of a
semi-crystalline polyester having a Tg of less than 50°C, a hydroxyl number of about 20 to
100, an inherent viscosity of about 0.1 to
0.5, a melting range of about 70 to 150°C, a
number average molecular weight of about 1500 to 10,000 and a heat of fusion (second heating cycle of DSC) of greater than about 5 cal/g- °C, e.g. 5 to about 20 cal/g-°C; and
(B) 0 to 85 weight percent of an amorphous
polyester having a glass transition temperature (Tg) of greater than 40°C, a
hydroxyl number of about 20 to 100 and an
inherent viscosity of about 0.1 to 0.5; and (2) a cross-linking effective amount of ε-caprolactam- blocked 1,3- or 1,4-bis(1-cyanato-1-methylethyl)- benzene.

3. A thermosetting coating composition according to Claim 2 wherein the amorphous polyester has a Tg
greater than 55°C, a hydroxyl number of about 25 to 80, an acid number of not more than 20 and an inherent viscosity of about 0.15 to 0.45.

4. A thermosetting coating composition according to Claim 2 wherein the semi-crystalline polyester has a Tg of less than 30°C, a melting point of 90 to 140°C, a hydroxyl number of about 30 to 80, an inherent viscosity of about 0.1 to 0.5, a number average molecular weight of about 2000 to 6000 and a heat of fusion (second heating cycle of differential scanning calorimetry) greater than 8 cal/g-°C and the amorphous polyester has a Tg greater than 55°C, a hydroxyl number of about 25 to 80, an acid number of not more than 20 and an inherent viscosity of about 0.15 to 0.45.

5. A thermosetting coating composition according to Claim 4 containing about 10 to 25 weight percent, based on the total weight of the semi-crystalline polyester, the amorphous polyester and the cross-linking agent, of ε-caprolactam-blocked 1,3-bis(1-isocyanato-1-methyl-ethyl)benzene.

6. A thermosetting coating composition according to Claim 2 containing a cross-linking catalyst.

7. A thermosetting coating composition according to Claim 5 containing a cross-linking catalyst.

8. A thermosetting coating composition in the form of a powder having an average particle size of about 15 to 75 microns comprising:
(1) a hydroxyl polyester component comprised of:
(A) 40 to 60 weight percent of a semi-crystalline polyester having a Tg of less than 30°C, a
melting point of 90 to 140°C, a hydroxyl
number of about 30 to 80, an inherent
viscosity of about 0.1 to 0.5, a number
average molecular weight of about 2000 to 6000 and a heat of fusion (second heating cycle of differential scanning calorimetry) greater
than 8 cal/g-°C and comprised of:
(i) diacid residues comprising about 80 to 98
mole percent terephthalic acid residues
and about 2 to 20 mole percent 1,4-cyclo- hexanedicarboxylic acid residues, 1,3- cyclohexanedicarboxylic acid residues,
adipic acid residues or a mixture
thereof;
(ii) diol residues comprising at least about
50 mole percent of residues having the
formula -O-(CH2)n-O-wherein n is 4 to 12; (B) 60 to 40 weight percent, based on the weight
of the hydroxyl polyester component, of an
amorphous polyester having a glass transition temperature (Tg) of greater than 55°C, a hydroxyl number of about 25 to 80, an acid
number of not more than 15 and an inherent
viscosity of about 0.15 to 0.45 and comprised of:
(i) diacid residues of which at least 50
mole percent are terephthalic acid
residues;
(ii) diol residues of which at least 50 mole
percent are 2,2-dimethyl-1,3-propanediol
residues; and
(iii) up to 10 mole percent, based on the
total moles of (ii) and
trimethylolpropane, of trimethylolpropane residues;
(2) about 5 to 30 weight percent, based on the total weight of (1) and (2), of ε-caprolactam-blocked
1,3- or 1,4-bis(1-isocyanato-1-methylethyl)benzene .

9. A thermosetting coating composition according to Claim 7 wherein about 10 to 25 weight percent of the compound of ( 2 ) is present.

10. A thermosetting coating composition according to Claim 8 containing a cross-linking catalyst and a flow aid.

11. A thermosetting coating composition according to Claim 10 containing about 10 to 25 weight percent of the compound of (2).

12. A thermosetting coating composition in the form of a powder having an average particle size of about 15 to 50 microns comprising:
(1) a blend of polymers containing free hydroxy groups comprised of:
(A) about 40 to 60 weight percent of a semi- crystalline polyester having a Tg of less
than 30°C, a melting point of 90 to 140°C, a
hydroxyl number of about 30 to 80, an inherent viscosity of about 0.1 to 0.5, a number
average molecular weight of about 2000 to 6000 and a heat of fusion (second heating cycle of differential scanning calorimetry) greater
than 8 cal/g-°C and comprised of:
(i) diacid residues consisting essentially
of about 85 to 95 mole percent
terephthalic acid residues and about 5
to 15 mole percent 1,4-cyclohexane- dicarboxylic acid residues; and
(ϋ) diol residues consisting essentially of
residues having the formula -O-(CH2)n-O- wherein n is 6 to 12;
(B) about 60 to 40 weight percent of an amorphous polyester having a glass transition
temperature of about 50 to 65°C, a hydroxyl
number of about 35 to 60, an acid number of
not more than 10 and an inherent viscosity of about 0.10 to 0.25 and comprised of:
(i) diacid residues of which at least 50
mole percent are terephthalic acid
residues;

(ii) diol residues of which at least 50 mole
percent are 2,2-dimethyl-1,3-propanediol
residues; and
(iii) up to 10 mole percent, based on the
total moles of (ii) and
trimethylolpropane, of trimethylolpropane residues;
(2) about 10 to 25 weight percent, based on the total weight of (1) and (2), of ε-caprolactam-blocked
1,3- or 1,4-bis(isocyanato-1-methylethyl)benzene;

(3) an acrylic polymer flow aid; and
(4) a cross-linking catalyst selected from organo-tin compounds.

13. A thermosetting coating composition according to Claim 12 which also contains benzoin and wherein the semi-crystalline polyester component is comprised of diacid residues consisting of about 85 to 95 mole percent terephthalic acid residues and about 5 to 15 mole percent 1,4-cyclohexanedicarboxylic acid residues and diol residues consisting of 1,6-hexanediol residues.

14. An article coated with the reaction product of the composition of Claim 1.

15. An article constructed of a metal coated with the reaction product of the composition of Claim 2.

16. An article constructed of steel coated with the reaction product of Claim 5.

17. An article constructed of steel coated with the reaction product of the composition of Claim 12.