処理中

しばらくお待ちください...

設定

設定

出願の表示

1. WO2012002566 - 加工性に優れた高強度鋼板およびその製造方法

公開番号 WO/2012/002566
公開日 05.01.2012
国際出願番号 PCT/JP2011/065415
国際出願日 29.06.2011
IPC
C22C 38/06 2006.01
C化学;冶金
22冶金;鉄または非鉄合金;合金の処理または非鉄金属の処理
C合金
38鉄合金,例.合金鋼
06アルミニウムを含有するもの
C22C 38/54 2006.01
C化学;冶金
22冶金;鉄または非鉄合金;合金の処理または非鉄金属の処理
C合金
38鉄合金,例.合金鋼
18クロムを含有するもの
40ニッケルを共に含有するもの
54ほう素を共に含有するもの
C21D 9/46 2006.01
C化学;冶金
21鉄冶金
D鉄系金属の物理的構造の改良;鉄系もしくは非鉄系金属または合金の熱処理用の一般的装置;脱炭,焼もどし,または他の処理による金属の可鍛化
9特定の品物に用いられる熱処理,例.焼なまし,硬化,焼入れまたは焼戻し;それに用いる炉
46金属薄板用
CPC
C21D 2211/005
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
005Ferrite
C21D 2211/009
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
009Pearlite
C21D 8/0226
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0221characterised by the working steps
0226Hot rolling
C21D 8/0263
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0247characterised by the heat treatment
0263following hot rolling
C21D 9/46
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
9Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
46for sheet metals
C22C 38/001
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
001containing N
出願人
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP]/[JP] (AllExceptUS)
  • 河村 健二 KAWAMURA, Kenji [JP]/[JP] (UsOnly)
  • 川邉 英尚 KAWABE, Hidetaka [JP]/[JP] (UsOnly)
  • 瀬戸 一洋 SETO, Kazuhiro [JP]/[JP] (UsOnly)
  • 片山 教幸 KATAYAMA, Noriyuki [JP]/[JP] (UsOnly)
発明者
  • 河村 健二 KAWAMURA, Kenji
  • 川邉 英尚 KAWABE, Hidetaka
  • 瀬戸 一洋 SETO, Kazuhiro
  • 片山 教幸 KATAYAMA, Noriyuki
代理人
  • 落合 憲一郎 OCHIAI, Kenichiro
優先権情報
2010-14741929.06.2010JP
公開言語 (言語コード) 日本語 (JA)
出願言語 (言語コード) 日本語 (JA)
指定国 (国コード)
発明の名称
(EN) HIGH-STRENGTH STEEL SHEET WITH EXCELLENT PROCESSABILITY AND PROCESS FOR PRODUCING SAME
(FR) TÔLE D'ACIER À RÉSISTANCE ÉLEVÉE PRÉSENTANT UNE EXCELLENTE APTITUDE AU TRAITEMENT AINSI QUE PROCÉDÉ DE FABRICATION ASSOCIÉ
(JA) 加工性に優れた高強度鋼板およびその製造方法
要約
(EN)
Provided are a high-strength steel sheet which is thin and has excellent processability and a process for producing the steel sheet. The process comprises: a hot rolling step in which a steel material having a composition containing, in terms of mass%, 0.08-0.15% C, 0.5-1.5% Si, 0.5-1.5% Mn, 0.01-0.1% Al, and up to 0.005% N is hot-rolled to obtain a hot-rolled sheet; annealing in which the hot-rolled sheet is pickled and then held for 5-400 seconds in the first temperature range of from the Ac1 transformation point to the Ac3 transformation point in a continuous annealing line, without being cold-rolled; and cooling in which the sheet is cooled from the first temperature range to 700ºC at an average cooling rate of 5 ºC/sec or higher and held for 30-400 seconds in the second temperature range of from 700ºC to 400ºC. Thus, a structure comprising a ferrite phase and a second phase comprising pearlite can be obtained, the ferrite phase and the pearlite accounting for 75-90% by area and 10-25% by area, respectively, of the whole structure. The pearlite accounts for 70% by area or more of the whole second phase and has an average grain diameter of 5 µm or less. As a result, a high-strength steel sheet which has a strength (TS) as high as 540 MPa or above, excellent stretchability and stretch flangeability, and excellent processability is obtained.
(FR)
L'invention concerne une fine tôle d'acier à résistance élevée présentant une excellente aptitude au traitement ainsi que le procédé de fabrication de celle-ci. Plus spécifiquement, une matière première d'acier dont la composition, en % en masse, est la suivante: C: 0,08 à 0,15 %, Si: 0,5 à 1,5 %, Mn: 0,5 à 1,5 %, Al: 0,01 à 0,1 %, N: 0,005% au plus, est soumise à un processus d'étirage à chaud, plus précisément à un laminage à chaud, permettant d'obtenir une tôle étirée. Ensuite, après nettoyage acide de la tôle étirée, cette dernière, sans laminage à froid et dans une ligne de recuit en continu, est soumise à un traitement de recuit qui la maintient pendant 5 à 400s dans une première plage de température d'un point critique Ac1 à un point critique Ac3. Ensuite, la première plage de température est abaissée jusqu'à 700 ℃ à une vitesse moyenne de 5 ℃/s, puis un traitement de refroidissement permet de maintenir la tôle pendant 30 à 400s dans une seconde plage de température de 700 à 400 ℃. Ainsi, on peut obtenir une structure à deux phases, qui, dans un rapport de surface de la structure dans son entier, comporte, 75 à 90 % d'une phase de ferrite et 10 à 25 % d'une phase de perlite. En outre, la perlite représente, en rapport de surface de la deuxième phase, au moins 70%, et la taille de grain moyen de cette perlite est inférieure ou égale à 5 μm. Cette tôle d'acier à résistance élevée présentant une excellente aptitude au traitement a un taux de résistance TS supérieur ou égal à 540 MP ainsi qu'une excellente aptitude à l'étirement des bordures.
(JA)
薄肉の、加工性に優れた高強度鋼板およびその製造方法を提供する。mass%で、C:0.08~0.15%、Si:0.5~1.5%、Mn:0.5~1.5%、Al:0.01~0.1%、N:0.005%以下を含む組成を有する鋼素材に、熱間圧延を行い熱延板とする熱延工程と、前記熱延板に酸洗を施したのち、該熱延板に、冷間圧延を省略して、連続焼鈍ラインで、Ac1変態点~Ac3変態点の第一の温度域で5~400s間保持する焼鈍処理と、第一の温度域~700℃までを、5℃/s以上の平均冷却速度で冷却し、さらに700℃~400℃の第二の温度域での滞留時間を30~400sとする冷却処理を行う。これにより、組織全体に対する面積率で、75~90%のフェライト相と、10~25%のパーライトを含む第二相とからなる組織を得ることができる。なお、パーライトは、第二相全体に対する面積率で70%以上を占め、パーライトの平均粒径は5μm以下となる。これにより、TS:540MPa以上の高強度と、優れた伸びと伸びフランジ性とを兼備する、加工性に優れた高強度鋼板となる。