1. WO2007100109 - 溶銑脱燐方法

公開番号 WO/2007/100109
公開日 07.09.2007
国際出願番号 PCT/JP2007/054104
国際出願日 26.02.2007
IPC
C21C 1/02 2006.01
C化学;冶金
21鉄冶金
C銑鉄の処理,例.精製,錬鉄または鋼の製造;鉄系合金の溶融状態での処理
1銑鉄の精製;鋳鉄
02脱りんまたは脱硫
C21C 5/36 2006.01
C化学;冶金
21鉄冶金
C銑鉄の処理,例.精製,錬鉄または鋼の製造;鉄系合金の溶融状態での処理
5炭素鋼,例.普通軟鋼,中炭素鋼または鋳鋼,の製造
28転炉による鋼の製造
36特殊な成分組成のスラグをつくる方法
CPC
C21C 1/025
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
CPROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
1Refining of pig-iron; Cast iron
02Dephosphorising or desulfurising
025Agents used for dephosphorising or desulfurising
C21C 5/36
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
CPROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
5Manufacture of carbon-steel, e.g. plain mild steel, medium carbon steel or cast steel ; or stainless steel
28Manufacture of steel in the converter
36Processes yielding slags of special composition
出願人
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP/JP]; 〒1000011 東京都千代田区内幸町二丁目2番3号 Tokyo 2-3, Uchisaiwaicho 2-chome, , Chiyoda-ku, Tokyo 1000011, JP (AllExceptUS)
  • 井上明彦 INOUE, Akihiko [JP/JP]; JP (UsOnly)
  • 内田祐一 UCHIDA, Yuichi [JP/JP]; JP (UsOnly)
  • 藤城正太郎 FUJIKI, Shotaro [JP/JP]; JP (UsOnly)
  • 岸本康夫 KISHIMOTO, Yasuo [JP/JP]; JP (UsOnly)
発明者
  • 井上明彦 INOUE, Akihiko; JP
  • 内田祐一 UCHIDA, Yuichi; JP
  • 藤城正太郎 FUJIKI, Shotaro; JP
  • 岸本康夫 KISHIMOTO, Yasuo; JP
代理人
  • 落合憲一郎 OCHIAI, Kenichiro; 〒1030027 東京都中央区日本橋二丁目1番10号柳屋ビル7階JFEテクノリサーチ株式会社特許出願部内 Tokyo c/o Patent Application Dept. JFE TECHNO-RESEARCH CORPORATION 7th Floor, Yanagiya Building 1-10, Nihonbashi 2-chome Chuo-ku, Tokyo 1030027, JP
優先権情報
2006-05236228.02.2006JP
公開言語 (言語コード) 日本語 (JA)
出願言語 (言語コード) 日本語 (JA)
指定国 (国コード)
発明の名称
(EN) METHOD OF DEPHOSPHORIZATION OF MOLTEN IRON
(FR) PROCEDE DE DEPHOSPHORATION DE LA FONTE LIQUIDE
(JA) 溶銑脱燐方法
要約
(EN)
A method in which a smelting agent consisting mainly of a CaO source and an oxygen source are added to molten iron to conduct a dephosphorization treatment. In the method, the molten iron is dephosphorized so that the slag after the treatment has a basicity of 2.2-3.5, excluding 2.2, and a total iron concentration of 10-30 mass% and that the final treatment temperature of the molten iron is 1,320°C or higher. Thus, the dephosphorization can be accelerated while ensuring a high manganese yield and the molten iron can be efficiently dephosphorized.
(FR)
L'invention concerne un procédé selon lequel un agent de fusion, principalement constitué d'une source de CaO, et une source d'oxygène sont ajoutés à de la fonte liquide afin de lui faire subir un traitement de déphosphoration. Selon le présent procédé, la fonte liquide est déphosphorée de sorte que le laitier après traitement ait une basicité strictement supérieure à 2,2 et allant jusqu'à 3,5, et une concentration totale en fer de 10 à 30 % en masse, la température de traitement final de la fonte liquide étant égale ou supérieure à 1 320 °C. La déphosphoration peut ainsi être accélérée tout en assurant un rendement élevé en manganèse et la fonte liquide peut être efficacement déphosphorée.
(JA)
溶銑にCaO源を主体とする精錬剤と酸素源を添加して脱燐処理を行う方法において、処理後のスラグの塩基度が2.2超え3.5以下、T.Fe濃度が10~30mass%となり、且つ溶銑の処理終点温度が1320℃以上となるように、溶銑を脱燐処理することにより、高いMn歩留まりを確保しつつ、脱燐反応を促進させて効率的な溶銑脱燐を行うことができる。