1. WO2004089829 - 複合化酸化インジウム粒子およびその製造方法ならびに導電性塗料、導電性塗膜および導電性シート

公開番号 WO/2004/089829
公開日 21.10.2004
国際出願番号 PCT/JP2004/004655
国際出願日 31.03.2004
予備審査請求日 01.11.2004
IPC
C01G 19/00 2006.1
C化学;冶金
01無機化学
GサブクラスC01DまたはC01Fに包含されない金属を含有する化合物
19すず化合物
CPC
B82Y 30/00
BPERFORMING OPERATIONS; TRANSPORTING
82NANOTECHNOLOGY
YSPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
30Nanotechnology for materials or surface science, e.g. nanocomposites
C01G 15/00
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
15Compounds of gallium, indium or thallium
C01G 19/00
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
19Compounds of tin
C01G 19/006
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
19Compounds of tin
006Compounds containing, besides tin, two or more other elements, with the exception of oxygen or hydrogen
C01G 9/02
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
9Compounds of zinc
02Oxides; Hydroxides
C01P 2002/72
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
2002Crystal-structural characteristics
70defined by measured X-ray, neutron or electron diffraction data
72by d-values or two theta-values, e.g. as X-ray diagram
出願人
  • 日立マクセル株式会社 HITACHI MAXELL, LTD. [JP]/[JP] (AllExceptUS)
  • 澤木 裕子 SAWAKI, Yuko [JP]/[JP] (UsOnly)
  • 岸本 幹雄 KISHIMOTO, Mikio [JP]/[JP] (UsOnly)
発明者
  • 澤木 裕子 SAWAKI, Yuko
  • 岸本 幹雄 KISHIMOTO, Mikio
代理人
  • 河宮 治 KAWAMIYA, Osamu
優先権情報
2003-09861201.04.2003JP
2003-16550610.06.2003JP
公開言語 (言語コード) 日本語 (ja)
出願言語 (言語コード) 日本語 (JA)
指定国 (国コード)
発明の名称
(EN) COMPOSITE INDIUM OXIDE PARTICLE, METHOD FOR PRODUCING SAME, CONDUCTIVE COATING MATERIAL, CONDUCTIVE COATING FILM, AND CONDUCTIVE SHEET
(FR) PARTICULE D'OXYDE D'INDIUM COMPOSITE, PROCEDE DE PRODUCTION CORRESPONDANT, MATERIAU DE REVETEMENT CONDUCTEUR, FILM DE REVETEMENT CONDUCTEUR ET FEUILLE CONDUCTRICE
(JA) 複合化酸化インジウム粒子およびその製造方法ならびに導電性塗料、導電性塗膜および導電性シート
要約
(EN) A zinc compound is mixed into an alkaline solution wherein a tin salt is dissolved, and an aqueous solution of an indium salt is added thereto. The obtained hydroxide or hydrate containing tin, indium and zinc is subjected to a heat treatment at a temperature within the range of 110-300˚C in the presence of water. Then, after filtration and drying, the thus-obtained material is subjected to another heat treatment at a temperature within the range of 300-1000˚C in the air, and further subjected to a reduction treatment at a temperature within the range of 150-400˚C in a reducing atmosphere, thereby forming zinc oxide-tin containing indium oxide composite particles. With this method, there can be obtained zinc oxide-tin containing indium oxide composite particles having an average particle diameter from 5 nm to 100 nm. The thus-obtained zinc oxide-tin containing indium oxide composite particles are suitable for formation of a transparent conductive coating film having ultraviolet-shielding properties.
(FR) Dans la présente invention, on mélange un composé de zinc dans une solution alcaline dans laquelle est dissous un sel d'étain puis on ajoute à ce mélange une solution aqueuse d'un sel d'indium. L'hydroxyde ou l'hydrate obtenu contenant de l'étain, de l'indium et du zinc est soumis à un traitement thermique à une température comprise dans la plage 110-300 °C en présence d'eau. Ensuite, après filtration et séchage, la matière ainsi obtenue est soumise à un autre traitement thermique à une température située dans la plage 300-1000 °C dans l'air, puis soumise à un traitement de réduction à une température comprise entre 150 et 400 °C dans une atmosphère réductrice, ce qui forme ainsi des particules de composite d'oxyde d'indium contenant du zinc, de l'oxyde et de l'étain. A l'aide de ce procédé, on peut obtenir des particules d'oxyde d'indium contenant du zinc, de l'oxyde et de l'étain d'un diamètre particulaire moyen compris entre 5 et 100 nm. Les particules de composite d'oxyde d'indium contenant du zinc, de l'oxyde et de l'étain sont appropriées pour former un film de revêtement conducteur transparent présentant des propriétés de blocage des ultraviolets.
(JA)  スズ塩が溶解されたアルカリ水溶液に亜鉛化合物を混合し、インジウム塩の水溶液を添加し、得られたスズ、インジウム、亜鉛を含有する水酸化物あるいは水和物を水の存在下で110~300℃の温度範囲で加熱処理する。次いで、ろ過、乾燥後、空気中300~1000℃の温度範囲で加熱処理し、さらに還元雰囲気中150~400℃の温度範囲で還元処理を行って酸化亜鉛−スズ含有酸化インジウム複合化粒子とする。これにより、粒子の平均粒子径が5nmから100nmの範囲にある酸化亜鉛−スズ含有酸化インジウム複合化粒子を得る。得られた酸化亜鉛−スズ含有酸化インジウム複合化粒子は、紫外線遮蔽性を併せ持つ透明導電性塗膜の形成に適している。