1. WO2021000729 - ACIER NON CASSANT POUR BARRE D'ACIER POUR BÉTON PRÉCONTRAINT, ET SON PROCÉDÉ DE PRODUCTION

Numéro de publication WO/2021/000729
Date de publication 07.01.2021
N° de la demande internationale PCT/CN2020/096482
Date du dépôt international 17.06.2020
CIB
C22C 38/02 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
02contenant du silicium 
C22C 38/04 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
04contenant du manganèse
C22C 33/06 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
33Fabrication des alliages ferreux
04par fusion
06en utilisant des alliages-mère
C21C 7/06 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
CTRAITEMENT DE LA FONTE BRUTE, p.ex. AFFINAGE, FABRICATION DE FER OU D'ACIER PUDDLÉS; TRAITEMENT DES ALLIAGES FERREUX À L'ÉTAT LIQUIDE
7Traitement à l'état liquide des alliages ferreux, p.ex. des aciers, non couverts par les groupes C21C1/-C21C5/149
04Elimination des impuretés par addition d'agent traitant
06de l'oxygène, p.ex. calmer
C21C 7/072 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
CTRAITEMENT DE LA FONTE BRUTE, p.ex. AFFINAGE, FABRICATION DE FER OU D'ACIER PUDDLÉS; TRAITEMENT DES ALLIAGES FERREUX À L'ÉTAT LIQUIDE
7Traitement à l'état liquide des alliages ferreux, p.ex. des aciers, non couverts par les groupes C21C1/-C21C5/149
04Elimination des impuretés par addition d'agent traitant
072Traitement par des gaz
C21C 7/076 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
CTRAITEMENT DE LA FONTE BRUTE, p.ex. AFFINAGE, FABRICATION DE FER OU D'ACIER PUDDLÉS; TRAITEMENT DES ALLIAGES FERREUX À L'ÉTAT LIQUIDE
7Traitement à l'état liquide des alliages ferreux, p.ex. des aciers, non couverts par les groupes C21C1/-C21C5/149
04Elimination des impuretés par addition d'agent traitant
076Emploi de scories ou de flux comme agents traitants
Déposants
  • 常熟市龙腾特种钢有限公司 CHANGSHU LONGTENG SPECIAL STEEL CO., LTD [CN]/[CN]
  • 常熟市龙腾滚动体制造有限公司 CHANGSHU LONGTENG ROLLING ELEMENT CO., LTD [CN]/[CN]
Inventeurs
  • 刘荣泉 LIU, Rongquan
  • 丁振涛 DING, Zhentao
  • 李鹏 LI, Peng
  • 耿振杰 GENG, Zhenjie
  • 朱春乐 ZHU, Chunle
  • 诸葛宇明 ZHUGE, Yuming
Mandataires
  • 南京经纬专利商标代理有限公司 NANJING JINGWEI PATENT & TRADEMARK AGENCY CO., LTD
Données relatives à la priorité
201910590476.802.07.2019CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) NON-BRITTLE STEEL FOR PRESTRESSED CONCRETE STEEL BAR, AND PRODUCTION METHOD THEREFOR
(FR) ACIER NON CASSANT POUR BARRE D'ACIER POUR BÉTON PRÉCONTRAINT, ET SON PROCÉDÉ DE PRODUCTION
(ZH) 一种不易脆断的预应力混凝土钢棒用钢及其生产方法
Abrégé
(EN)
Disclosed are a non-brittle steel for a prestressed concrete steel bar, and a production method therefor. The steel comprises the following chemical components in percentages by mass: 0.25% - 0.35% of C, 1.10% - 1.40% of Si, 0.55% - 0.75% of Mn, P ≤ 0.025%, S ≤ 0.010%, with the balance being Fe and inevitable impurities. By means of the method, it can be ensured that material gases, inclusions, mechanical properties, etc. meet material requirements, the requirements for machining a steel bar by means of wires are met, a heat treatment tempering temperature is increased without reducing the strength of the steel bar, the fracture ratio of a prestressed concrete steel bar is greatly reduced, the yield and the production efficiency are improved, energy is saved, and production costs are saved for a user.
(FR)
Cette invention concerne un acier non cassant pour une barre d'acier pour béton précontraint, et son procédé de production. L'acier comprend les constituants chimiques suivants en pourcentage en poids : 0,25 % à 0,35 % de C, 1,10 % à 1,40 % de Si, 0,55 % à 0,75 % de Mn, P ≤ 0,025 %, S ≤ 0,010 %, le reste étant du Fe et les inévitables impuretés. Le procédé selon l'invention permet de garantir que les gaz de matériau, inclusions, propriétés mécaniques, etc. satisfont les exigences de matériau, que les exigences d'usinage d'une barre d'acier au moyen de fils sont satisfaites, qu'une température de traitement thermique de revenu est augmentée sans réduire la résistance de la barre d'acier, que le rapport de rupture d'une barre d'acier pour béton précontraint est considérablement réduit, que le rendement et l'efficacité de production sont améliorés, que l'énergie est économisée, et que les coûts de production sont économisés pour un utilisateur.
(ZH)
本发明公开一种不易脆断的预应力混凝土钢棒用钢及其生产方法,它包括以下质量百分比的化学成分:C:0.25~0.35%、Si:1.10~1.40%、Mn:0.55~0.75%、P:≤0.025%和S:≤0.010%,余量为Fe和不可避免的杂质。该方法能够保证材料气体、夹杂物、力学性能等满足材料要求,满足线材加工钢棒的要求,在钢棒强度不降低的情况下提高热处理回火温度,大幅降低预应力混凝土钢棒的断裂比例,提高成材率和生产效率,而且节约了能源及用户生产成本。