1. WO2020155243 - PROCÉDÉ DE PRÉPARATION DE MAGNÉSIE HAUTE DENSITÉ À PARTIR DE MAGNÉSITE AU MOYEN D'UN FRITTAGE PAR PLASMA À ÉTINCELLES

Numéro de publication WO/2020/155243
Date de publication 06.08.2020
N° de la demande internationale PCT/CN2019/076094
Date du dépôt international 26.02.2019
CIB
C04B 2/10 2006.01
CCHIMIE; MÉTALLURGIE
04CIMENTS; BÉTON; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES
BCHAUX; MAGNÉSIE; SCORIES; CIMENTS; LEURS COMPOSITIONS, p.ex. MORTIERS, BÉTON OU MATÉRIAUX DE CONSTRUCTION SIMILAIRES; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES; TRAITEMENT DE LA PIERRE NATURELLE
2Chaux, magnésie ou dolomite
10Préchauffage, cuisson, calcination ou refroidissement
C04B 2/12 2006.01
CCHIMIE; MÉTALLURGIE
04CIMENTS; BÉTON; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES
BCHAUX; MAGNÉSIE; SCORIES; CIMENTS; LEURS COMPOSITIONS, p.ex. MORTIERS, BÉTON OU MATÉRIAUX DE CONSTRUCTION SIMILAIRES; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES; TRAITEMENT DE LA PIERRE NATURELLE
2Chaux, magnésie ou dolomite
10Préchauffage, cuisson, calcination ou refroidissement
12dans des fours à cuve ou dans des fours verticaux
CPC
C04B 2/102
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2Lime, magnesia or dolomite
10Preheating, burning calcining or cooling
102of magnesia, e.g. dead burning
C04B 2/12
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2Lime, magnesia or dolomite
10Preheating, burning calcining or cooling
12in shaft or vertical furnaces
Déposants
  • 东北大学 NORTHEASTERN UNIVERSITY [CN]/[CN]
Inventeurs
  • 马北越 MA, Beiyue
  • 任鑫明 REN, Xinming
  • 靳恩东 JIN, Endong
  • 刘朝阳 LIU, Zhaoyang
  • 付高峰 FU, Gaofeng
  • 于景坤 YU, Jingkun
Mandataires
  • 沈阳东大知识产权代理有限公司 SHENYANG DONGDA INTELLECTUAL PROPERTY AGENCY CO., LTD
Données relatives à la priorité
201910109465.301.02.2019CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) METHOD FOR PREPARING HIGH-DENSITY MAGNESIA FROM MAGNESITE BY MEANS OF SPARK PLASMA SINTERING
(FR) PROCÉDÉ DE PRÉPARATION DE MAGNÉSIE HAUTE DENSITÉ À PARTIR DE MAGNÉSITE AU MOYEN D'UN FRITTAGE PAR PLASMA À ÉTINCELLES
(ZH) 一种利用菱镁矿放电等离子烧结制备高密度镁砂的方法
Abrégé
(EN)
Disclosed is a method for preparing high-density magnesia from magnesite by means of spark plasma sintering, which belongs to the technical field of efficient utilization of metallurgical resources. The specific preparation method involves: placing magnesite into a high-temperature furnace for calcination to obtain a light-burned magnesium oxide powder; placing the light-burned magnesium oxide powder into a ball milling tank, carrying out hydration and ball milling treatments on the light-burned magnesium oxide at the same time by using deionized water as a ball milling medium, and subjecting same to a drying treatment to obtain a magnesium hydroxide powder; placing the magnesium hydroxide powder into the high-temperature furnace for secondary calcination to obtain a secondary light-burned magnesium oxide powder; and finally, placing the secondary light-burned magnesium oxide fine powder into a graphite mold of a spark plasma sintering furnace, and subjecting same to spark plasma sintering at a certain temperature, time, and pressure to obtain the high-density magnesia.
(FR)
L'invention concerne un procédé de préparation de magnésie haute densité à partir de magnésite au moyen d'un frittage par plasma à étincelles, qui appartient au domaine technique de l'utilisation efficace de ressources métallurgiques. Le procédé de préparation spécifique comprend les étapes suivantes consistant à : mettre en place de la magnésite dans un four à haute température pour une calcination afin d'obtenir une poudre d'oxyde de magnésium légèrement calciné ; mettre en place la poudre d'oxyde de magnésium légèrement calciné dans un réservoir de broyage à billes, mettre en œuvre simultanément des traitements d'hydratation et de broyage à billes sur l'oxyde de magnésium légèrement calciné en utilisant de l'eau déionisée comme milieu de broyage à billes, et soumettre celui-ci à un traitement de séchage pour obtenir une poudre d'hydroxyde de magnésium ; mettre en place la poudre d'hydroxyde de magnésium dans le four à haute température pour une calcination secondaire afin d'obtenir une poudre d'oxyde de magnésium légèrement calciné secondaire ; et enfin, mettre en place la poudre fine d'oxyde de magnésium légèrement calciné secondaire dans un moule en graphite d'un four de frittage par plasma à étincelles, et soumettre celle-ci à un frittage par plasma à étincelles à une certaine température, pendant un certaine temps et à une certaine pression pour obtenir de la magnésie à haute densité.
(ZH)
一种利用菱镁矿放电等离子烧结制备高密度镁砂的方法,属于冶金资源高效利用技术领域。具体制备方法为:将菱镁矿置于高温炉内煅烧,获得轻烧氧化镁粉;将轻烧氧化镁粉置于球磨罐中,以去离子水为球磨介质,同时对轻烧氧化镁完成水化和球磨处理,经过干燥处理,获得氢氧化镁粉;将氢氧化镁粉置于高温炉内二次煅烧,获得二次轻烧氧化镁粉;最后,将二次轻烧氧化镁细粉置于放电等离子烧结炉的石墨模具内,在一定温度、时间和压力下进行放电等离子烧结,制得高密度镁砂。