1. WO2020116588 - PROCÉDÉ DE FABRICATION D'UN JOINT SOUDÉ EN ACIER FERRITIQUE RÉSISTANT À LA CHALEUR

Numéro de publication WO/2020/116588
Date de publication 11.06.2020
N° de la demande internationale PCT/JP2019/047717
Date du dépôt international 05.12.2019
CIB
B23K 9/23 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
23MACHINES-OUTILS; TRAVAIL DES MÉTAUX NON PRÉVU AILLEURS
KBRASAGE OU DÉBRASAGE; SOUDAGE; REVÊTEMENT OU PLACAGE PAR BRASAGE OU SOUDAGE; DÉCOUPAGE PAR CHAUFFAGE LOCALISÉ, p.ex. DÉCOUPAGE AU CHALUMEAU; TRAVAIL PAR RAYON LASER
9Soudage ou découpage à l'arc
23tenant compte des propriétés des matériaux à souder
B23K 35/30 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
23MACHINES-OUTILS; TRAVAIL DES MÉTAUX NON PRÉVU AILLEURS
KBRASAGE OU DÉBRASAGE; SOUDAGE; REVÊTEMENT OU PLACAGE PAR BRASAGE OU SOUDAGE; DÉCOUPAGE PAR CHAUFFAGE LOCALISÉ, p.ex. DÉCOUPAGE AU CHALUMEAU; TRAVAIL PAR RAYON LASER
35Baguettes, électrodes, matériaux ou environnements utilisés pour le brasage, le soudage ou le découpage
22caractérisés par la composition ou la nature du matériau
24Emploi de matériaux spécifiés pour le soudage ou le brasage
30dont le principal constituant fond à moins de 1550 C
C22C 19/05 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
19Alliages à base de nickel ou de cobalt, seuls ou ensemble
03à base de nickel
05avec du chrome
C22C 38/00 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
C22C 38/54 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
54et du bore
Déposants
  • 日本製鉄株式会社 NIPPON STEEL CORPORATION [JP]/[JP]
Inventeurs
  • 平田 弘征 HIRATA, Hiroyuki
  • 浄▲徳▼ 佳奈 JOTOKU, Kana
  • 栗原 伸之佑 KURIHARA, Shinnosuke
  • 田中 克樹 TANAKA, Katsuki
Mandataires
  • 特許業務法人太陽国際特許事務所 TAIYO, NAKAJIMA & KATO
Données relatives à la priorité
2018-22831405.12.2018JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) METHOD FOR MANUFACTURING FERRITIC HEAT RESISTANT STEEL WELDED JOINT
(FR) PROCÉDÉ DE FABRICATION D'UN JOINT SOUDÉ EN ACIER FERRITIQUE RÉSISTANT À LA CHALEUR
(JA) フェライト系耐熱鋼溶接継手の製造方法
Abrégé
(EN)
This method for manufacturing a ferritic heat resistant steel welded joint includes a multilayer welding step of using a welding material for an Ni-based heat resistant alloy to perform multilayer welding of a ferritic heat resistant steel base material containing between 0.006 % by mass and 0.023 % by mass of B, wherein first layer welding is performed under welding conditions in which, in a cross section through a welded portion after welding of a first layer and before welding of a second layer in the multilayer welding step, a ratio between a surface area [SBM] of the melted ferritic heat resistant steel base material and a surface area [SWM] of the welded metal satisfy formula (1), with respect to the % by mass of B [%BBM] contained in the ferritic heat resistant steel base material. (1) 0.1 ≤ [SBM]/[SWM]≤-50×[%BBM]+1.3
(FR)
L'invention concerne un procédé de fabrication d'un joint soudé en acier ferritique résistant à la chaleur, comprenant une étape de soudage multicouche qui consiste à utiliser un matériau de soudage pour un alliage résistant à la chaleur à base de Ni pour réaliser un soudage multicouche d'un matériau de base en acier ferritique résistant à la chaleur contenant entre 0,006 % massique et 0,023 % massique de B. Le soudage de la première couche est effectué dans des conditions de soudage dans lesquelles, dans une section transversale à travers une portion soudée après le soudage d'une première couche et avant le soudage d'une deuxième couche dans l'étape de soudage multicouche, un rapport entre une aire [SBM] du matériau de base en acier ferritique résistant à la chaleur fondu et une aire [SWM] du métal soudé satisfait à la formule (1), en ce qui concerne le % massique de B [%BBM] contenu dans le matériau de base en acier ferritique résistant à la chaleur. (1) 0,1 ≤ [SBM]/[SWM]≤-50×[%BBM]+1,3
(JA)
Bを0.006質量%~0.023質量%含むフェライト系耐熱鋼母材をNi基耐熱合金用溶接材料で多層溶接する多層溶接工程を有し、前記多層溶接工程での初層溶接後かつ第二層溶接前の溶接部の横断面における、溶融した前記フェライト系耐熱鋼母材の面積[SBM]と溶接金属の面積[SWM]との比が、前記フェライト系耐熱鋼母材に含有されるBの質量%[%BBM]に対して下記(1)式を満たす溶接条件で初層溶接を行うフェライト系耐熱鋼溶接継手の製造方法。 0.1≦[SBM]/[SWM]≦-50×[%BBM]+1.3・・・(1)