1. WO2020111732 - PLAQUE D'ACIER ÉPAISSE À HAUTE RÉSISTANCE POUR CANALISATION, POSSÉDANT UNE EXCELLENTE DUCTILITÉ ET TÉNACITÉ À BASSE TEMPÉRATURE AINSI QU'UN FAIBLE COEFFICIENT D'ÉLASTICITÉ, ET SON PROCÉDÉ

Numéro de publication WO/2020/111732
Date de publication 04.06.2020
N° de la demande internationale PCT/KR2019/016374
Date du dépôt international 26.11.2019
CIB
C22C 38/58 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
58et plus de 1,5% en poids de manganèse
CPC
C21D 8/02
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
C22C 38/00
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/02
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
02containing silicon
C22C 38/06
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
06containing aluminium
C22C 38/42
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
42with copper
C22C 38/44
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
44with molybdenum or tungsten
Déposants
  • 주식회사 포스코 POSCO [KR]/[KR]
Inventeurs
  • 배진호 BAE, Jin-Ho
Mandataires
  • 특허법인 씨엔에스 C&S PATENT AND LAW OFFICE
Données relatives à la priorité
10-2018-015070629.11.2018KR
Langue de publication coréen (KO)
Langue de dépôt coréen (KO)
États désignés
Titre
(EN) HIGH STRENGTH THICK STEEL PLATE FOR LINEPIPE HAVING EXCELLENT LOW TEMPERATURE TOUGHNESS AND DUCTILITY AS WELL AS LOW YIELD RATIO, AND METHOD THEREOF
(FR) PLAQUE D'ACIER ÉPAISSE À HAUTE RÉSISTANCE POUR CANALISATION, POSSÉDANT UNE EXCELLENTE DUCTILITÉ ET TÉNACITÉ À BASSE TEMPÉRATURE AINSI QU'UN FAIBLE COEFFICIENT D'ÉLASTICITÉ, ET SON PROCÉDÉ
(KO) 저온인성과 연신율이 우수하며, 항복비가 작은 후물 고강도 라인파이프용 강재 및 그 제조방법
Abrégé
(EN)
One embodiment of the present invention provides a high strength thick steel plate for a line pipe having excellent low temperature toughness and ductility as well as a low yield ratio, and a method thereof, the steel plate comprising by weight%: 0.03 to 0.055% of C; 0.1 to 0.35% of Si; 1.7 to 2.2% of Mn; 0.01 to 0.04% of Al; 0.005 to 0.025% of Ti; 0.008% or less of N; 0.08 to 0.12% of Nb; 0.2 to 0.45% of Cr; 0.2 to 0.35% of Ni; 0.05 to 0.3% of Cu; 0.2 to 0.4% of Mo; 0.02% or less of P; 0.002% or less of S; 0.0005 to 0.004% of Ca; 0.01 to 0.04% of V; 0.0005% or less of B; and residual Fe and other unavoidable impurities, and satisfying relational expressions 1 to 4, wherein the microstructure thereof comprises by area%: 1 to 5% of polygonal ferrite; 60 to 75% of acicular ferrite; 20 to 30% of bainitic ferrite; and 5% or less of island martensite. [Relational expression 1] 19 ≤ (Mo/96)/(P/31) ≤ 30 [Relational expression 2] 1.42 ≤ Cr+2Mo+Cu+Ni+1000B ≤ 1.75 [Relational expression 3] 4 < {3C/12 + Mn/55}×100 ≤ 4.9 [Relational expression 4] 600 ≤ 400C+6800Nb+600V+800Ti+300Al ≤ 820 (wherein the content of the alloying elements described in the relational expressions 1 to 4 is by % by weight.)
(FR)
Un mode de réalisation de la présente invention concerne une plaque d'acier épaisse à haute résistance pour une canalisation, possédant une excellente ductilité et ténacité à basse température, ainsi qu'un faible coefficient d'élasticité, et un procédé associé, la plaque d'acier comprenant en % en poids : 0,03 à 0 055% de C ; 0,1 à 0,35% de Si ; 1,7 à 2,2% de Mn ; 0,01 à 0,04% d'Al ; 0,005 à 0,025% de Ti ; 0,008% ou moins de N ; 0,08 à 0,12% de Nb ; 0,2 à 0,45% de Cr ; 0,2 à 0,35% de Ni ; 0,05 à 0,3% de Cu ; 0,2 à 0,4% de Mo ; 0,02% ou moins de P ; 0,002% ou moins de S ; 0,0005 à 0,004% de Ca ; 0,01 à 0,04% de V ; 0,0005% ou moins de B ; et du Fe résiduel et d'autres impuretés inévitables, et satisfaisant les expressions relationnelles 1 à 4, la microstructure de celle-ci comprenant par % en surface : 1 À 5% de ferrite polygonale ; 60 à 75% de ferrite aciculaire ; 20 à 30% de ferrite bainitique ; et 5% ou moins d'îlots de martensite. [Expression relationnelle 1] 19 ≤ (Mo/96)/(P/31) ≤ 30 [expression relationnelle 2] 1,42 ≤ Cr+2Mo+Cu+Ni+1000B ≤ 1,75 [expression relationnelle 3] 4 < {3C/12 + Mn/55}×100 ≤ 4.9 [expression relationnelle 4] 600 ≤ 400C+6800Nb+600V+800Ti+300Al ≤ 820 (la teneur des éléments d'alliage décrits dans les expressions relationnelles 1 à 4 étant exprimée en % en poids.)
(KO)
본 발명의 일 실시형태는 중량%로, C: 0.03~0.055%, Si: 0.1~0.35%, Mn: 1.7~2.2%, Al: 0.01~0.04%, Ti: 0.005~0.025%, N: 0.008% 이하, Nb: 0.08~0.12%, Cr: 0.2~0.45%, Ni: 0.2~0.35%, Cu: 0.05~0.3%, Mo: 0.2~0.4%, P: 0.02%이하, S: 0.002%이하, Ca: 0.0005~0.004%, V: 0.01~0.04%, B: 0.0005%이하, 잔부 Fe 및 기타 불가피한 불순물을 포함하고, 하기 관계식 1 내지 4의 조건을 만족하며, 미세조직은 면적%로, 폴리고날 페라이트: 1~5%, 애시큘러 페라이트: 60~75%, 베이니틱 페라이트: 20~30% 및 도상 마르텐사이트: 5% 이하를 포함하는 저온인성과 연신율이 우수하며, 항복비가 작은 후물 고강도 라인파이프용 강재 및 그 제조방법을 제공한다. [관계식 1] 19 ≤ (Mo/96)/(P/31) ≤ 30 [관계식 2] 1.42 ≤ Cr+2Mo+Cu+Ni+1000B ≤ 1.75 [관계식 3] 4 < {3C/12+Mn/55}×100 ≤ 4.9 [관계식 4] 600 ≤ 400C+6800Nb+600V+800Ti+300Al ≤ 820 (단, 상기 관계식 1 내지 4에 기재된 합금원소의 함량은 중량%임.)