1. WO2020109850 - TÔLE D'ACIER RECUIT LAMINÉE À CHAUD PRÉSENTANT UN RAPPORT D'EXPANSION DE TROU ÉLEVÉ ET SON PROCÉDÉ DE FABRICATION

Numéro de publication WO/2020/109850
Date de publication 04.06.2020
N° de la demande internationale PCT/IB2018/059510
Date du dépôt international 30.11.2018
CIB
C21D 9/50 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9Traitement thermique, p.ex. recuit, durcissement, trempe ou revenu, adapté à des objets particuliers; Fours à cet effet
50pour joints de soudure
B23K 11/06 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
23MACHINES-OUTILS; TRAVAIL DES MÉTAUX NON PRÉVU AILLEURS
KBRASAGE OU DÉBRASAGE; SOUDAGE; REVÊTEMENT OU PLACAGE PAR BRASAGE OU SOUDAGE; DÉCOUPAGE PAR CHAUFFAGE LOCALISÉ, p.ex. DÉCOUPAGE AU CHALUMEAU; TRAVAIL PAR RAYON LASER
11Soudage par résistance; Sectionnement par chauffage par résistance
06en utilisant des électrodes à molette
B23K 11/30 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
23MACHINES-OUTILS; TRAVAIL DES MÉTAUX NON PRÉVU AILLEURS
KBRASAGE OU DÉBRASAGE; SOUDAGE; REVÊTEMENT OU PLACAGE PAR BRASAGE OU SOUDAGE; DÉCOUPAGE PAR CHAUFFAGE LOCALISÉ, p.ex. DÉCOUPAGE AU CHALUMEAU; TRAVAIL PAR RAYON LASER
11Soudage par résistance; Sectionnement par chauffage par résistance
30Caractéristiques relatives aux électrodes
C21D 8/02 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
02pendant la fabrication de produits plats ou de bandes
C21D 8/04 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
02pendant la fabrication de produits plats ou de bandes
04pour produire des produits plats ou des bandes pour l'emboutissage profond
C21D 9/46 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9Traitement thermique, p.ex. recuit, durcissement, trempe ou revenu, adapté à des objets particuliers; Fours à cet effet
46pour tôles
CPC
C21D 1/19
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
1General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
18Hardening
19by interrupted quenching
C21D 1/20
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
1General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
18Hardening
19by interrupted quenching
20Isothermal quenching, e.g. bainitic hardening
C21D 2211/001
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
001Austenite
C21D 2211/002
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
002Bainite
C21D 2211/008
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
2211Microstructure comprising significant phases
008Martensite
C21D 6/008
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
6Heat treatment of ferrous alloys
008containing Si
Déposants
  • ARCELORMITTAL [LU]/[LU]
Inventeurs
  • HELL, Jean-Christophe
Mandataires
  • PLAISANT, Sophie
Données relatives à la priorité
Langue de publication anglais (EN)
Langue de dépôt anglais (EN)
États désignés
Titre
(EN) COLD ROLLED ANNEALED STEEL SHEET WITH HIGH HOLE EXPANSION RATIO AND MANUFACTURING PROCESS THEREOF
(FR) TÔLE D'ACIER RECUIT LAMINÉE À CHAUD PRÉSENTANT UN RAPPORT D'EXPANSION DE TROU ÉLEVÉ ET SON PROCÉDÉ DE FABRICATION
Abrégé
(EN)
A cold rolled annealed steel sheet having a chemical composition comprising, in weight %: 0.30% ≤ C ≤ 0.50%, 1.00% ≤ Mn ≤ 2.50%, 1.00% ≤ Si ≤ 2.00%, Al ≤ 2.00%, Cr ≤ 0.100%, 0.100% ≤ Mo ≤ 0. 500%, 0.020% ≤ Nb ≤ 0.200%, B ≤ 0.0005%, P ≤0.02%, S ≤ 0.005%, N≤0.01%, the remainder being Fe and unavoidable impurities, with the percentages in carbon, manganese, chromium, molybdenum and boron are such that the alloy satisfies the following condition: 250%C + 120%Mn - 200%Cr + 200%Mo-10000%B ≥ 320, and wherein the microstructure comprises in surface fraction, 35% to 45 % of islands of martensite and retained austenite (M-A), the total retained austenite is higher than or equal to 24%, the remainder consisting of bainitic ferrite.
(FR)
L'invention concerne une tôle d'acier recuit laminée à froid présentant une composition chimique comprenant, en % en poids : 0,30 % ≤ C ≤ 0,50 %, 1,00 % ≤ Mn ≤ 2,50 %, 1,00 % ≤ Si ≤ 2,00 %, Al ≤ 2,00 %, Cr ≤ 0,100 %, 0,100 % ≤ Mo ≤ 0,500 %, 0,020 % ≤ Nb ≤ 0,200 %, B ≤ 0,0005 %, P ≤ 0,02 %, S ≤ 0,005 %, N ≤ 0,01 %, le reste étant du Fe et des impuretés inévitables, les pourcentages en carbone, manganèse, chrome, molybdène et bore étant tels que l'alliage satisfait la condition suivante : 250 % C + 120 % Mn - 200 % Cr + 200 % Mo - 10 000 % B ≥ 320, et la microstructure comprenant en fraction de surface, 35 % à 45 % d'îlots de martensite et d'austénite résiduelle (M-A), l'austénite résiduelle totale étant supérieure ou égale à 24 %, le reste étant constitué de ferrite bainitique.