1. WO2020108594 - PLAQUE OU BANDE EN ACIER FORMÉE À CHAUD AVEC PLACAGE À BASE DE ZINC AYANT D'EXCELLENTES PERFORMANCES DE PLIAGE À FROID, ET SON PROCÉDÉ DE FABRICATION

Numéro de publication WO/2020/108594
Date de publication 04.06.2020
N° de la demande internationale PCT/CN2019/121860
Date du dépôt international 29.11.2019
CIB
C22C 38/02 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
02contenant du silicium 
C22C 38/04 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
04contenant du manganèse
C22C 38/60 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
60contenant du plomb, du sélénium, du tellure, de l'antimoine, ou plus de 0,04% en poids de soufre
C22C 38/06 2006.01
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
06contenant de l'aluminium
C23C 2/40 2006.01
CCHIMIE; MÉTALLURGIE
23REVÊTEMENT DE MATÉRIAUX MÉTALLIQUES; REVÊTEMENT DE MATÉRIAUX AVEC DES MATÉRIAUX MÉTALLIQUES; TRAITEMENT CHIMIQUE DE SURFACE; TRAITEMENT DE DIFFUSION DE MATÉRIAUX MÉTALLIQUES; REVÊTEMENT PAR ÉVAPORATION SOUS VIDE, PAR PULVÉRISATION CATHODIQUE, PAR IMPLANTATION D'IONS OU PAR DÉPÔT CHIMIQUE EN PHASE VAPEUR, EN GÉNÉRAL; MOYENS POUR EMPÊCHER LA CORROSION DES MATÉRIAUX MÉTALLIQUES, L'ENTARTRAGE OU LES INCRUSTATIONS, EN GÉNÉRAL
CREVÊTEMENT DE MATÉRIAUX MÉTALLIQUES; REVÊTEMENT DE MATÉRIAUX AVEC DES MATÉRIAUX MÉTALLIQUES; TRAITEMENT DE SURFACE DE MATÉRIAUX MÉTALLIQUES PAR DIFFUSION DANS LA SURFACE, PAR CONVERSION CHIMIQUE OU SUBSTITUTION; REVÊTEMENT PAR ÉVAPORATION SOUS VIDE, PAR PULVÉRISATION CATHODIQUE, PAR IMPLANTATION D'IONS OU PAR DÉPÔT CHIMIQUE EN PHASE VAPEUR, EN GÉNÉRAL
2Procédés de trempage à chaud ou d'immersion pour appliquer le matériau de revêtement à l'état fondu sans modifier la forme de l'objet immergé; Appareils à cet effet
34caractérisés par la forme du matériau à traiter
36Objets allongés
40Plaques; Bandes
C21D 8/02 2006.01
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
02pendant la fabrication de produits plats ou de bandes
CPC
C21D 8/0205
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0205of ferrous alloys
C21D 8/0226
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0221characterised by the working steps
0226Hot rolling
C21D 8/0236
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0221characterised by the working steps
0236Cold rolling
C21D 8/0273
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
0247characterised by the heat treatment
0273Final recrystallisation annealing
C22C 38/001
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
001containing N
C22C 38/002
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
002containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
Déposants
  • 宝山钢铁股份有限公司 BAOSHAN IRON & STEEL CO., LTD. [CN]/[CN]
Inventeurs
  • 毕文珍 BI, Wenzhen
  • 洪继要 HONG, Jiyao
  • 王利 WANG, Li
Mandataires
  • 上海专利商标事务所有限公司 SHANGHAI PATENT & TRADEMARK LAW OFFICE, LLC
Données relatives à la priorité
201811454798.130.11.2018CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) ZINC-BASED PLATED HOT-FORMED STEEL PLATE OR STEEL STRIP HAVING EXCELLENT COLD BENDING PERFORMANCE, AND MANUFACTURING METHOD THEREOF
(FR) PLAQUE OU BANDE EN ACIER FORMÉE À CHAUD AVEC PLACAGE À BASE DE ZINC AYANT D'EXCELLENTES PERFORMANCES DE PLIAGE À FROID, ET SON PROCÉDÉ DE FABRICATION
(ZH) 一种冷弯性能优良的锌系镀覆热成型钢板或钢带及其制造方法
Abrégé
(EN)
Provided are a zinc-based plated hot-formed steel plate or steel strip having excellent cold bending performance, and a manufacturing method thereof; said zinc-based plated hot-formed steel plate or steel strip comprises a substrate having a surface decarburized layer thickness of less than 20 um and a zinc-based plated layer having an adhesion amount of 10 to 100 g/m^2; the component weight percentages of the substrate are: C: 0.1–0.8%, Si: 0.05–2.0%, Mn: 0.5–3.0%, P≤0.1%, S≤0.05%, Al≤0.1%, N≤0.01%; the remainder is Fe and unavoidable impurities; the average size of original austenite grains of the substrate is less than 15 um. After hot forming of the substrate, the hot-formed steel plate or steel strip has a tensile strength of 1500 MPa and elongation after fracture of 5%, and the coating is continuous and complete, there are no cracks extending to the substrate, and the steel plate has excellent cold bending performance.
(FR)
L'invention concerne une plaque ou une bande en acier formée à chaud avec placage à base de zinc ayant d'excellentes performances de pliage à froid, et son procédé de fabrication. Ladite plaque ou bande en acier formée à chaud avec placage à base de zinc comprend un substrat ayant une épaisseur de couche décarburée de surface inférieure à 20 µm et une couche de placage à base de zinc ayant une quantité d'adhérence allant de 10 à 100 g/m^2. Les pourcentages massiques des composants du substrat sont : C : 0,1–0,8 %, Si : 0,05–2,0 %, Mn : 0,5–3,0 %, P≤0,1 %, S≤0,05 %, Al≤0,1 %, N≤0,01 %; le reste étant du Fe et les inévitables impuretés. La taille moyenne des grains d'austénite d'origine du substrat est inférieure à 15 µm. Après la formation à chaud du substrat, la plaque en acier ou la bande en acier formée à chaud présente une résistance à la traction de 1 500 MPa et un allongement après fracture de 5 %, et le revêtement est continu et complet, il n'y a pas de fissures qui s'étendent jusqu'au substrat, et la plaque en acier présente d'excellentes performances de pliage à froid.
(ZH)
一种冷弯性能优良的锌系镀覆热成型钢板或钢带及其制造方法,该锌系镀覆热成型钢板或钢带包括表面脱碳层厚度在20um以下的基板及其上附着量为10~100g/m2的锌系镀层;基板的成分重量百分比为:C:0.1~0.8%、Si:0.05~2.0%、Mn:0.5~3.0%、P≤0.1%、S≤0.05%、Al≤0.1%、N≤0.01%,余Fe和不可避免的杂质;基板的原始奥氏体晶粒平均尺寸在15um以下。该热成型钢板或钢带在满足基板热成型后抗拉强度1500MPa,断后延伸率5%的基础上,镀层连续完整,无扩展至基板的裂纹,且钢板冷弯性能优良。