1. WO2020062826 - PROCÉDÉ DE PRÉPARATION D'UNE MEMBRANE EN FIBRES COMPOSITES DE POLYIMIDE ET DE POLYCARBONATE À STRUCTURE COIFFÉE CONTENANT DU FLUOR

Numéro de publication WO/2020/062826
Date de publication 02.04.2020
N° de la demande internationale PCT/CN2019/081021
Date du dépôt international 02.04.2019
CIB
D01D 5/00 2006.01
DTEXTILES; PAPIER
01FIBRES OU FILS NATURELS OU FAITS PAR L'HOMME; FILATURE
DPROCÉDÉS OU APPAREILS MÉCANIQUES POUR LA FABRICATION DES FILAMENTS, FILS, FIBRES, SOIES OU RUBANS FAITS PAR L’HOMME
5Formation des filaments, fils ou similaires
CPC
D01D 5/0007
DTEXTILES; PAPER
01NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
DMECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
5Formation of filaments, threads, or the like
0007Electro-spinning
D01D 5/0038
DTEXTILES; PAPER
01NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
DMECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
5Formation of filaments, threads, or the like
0007Electro-spinning
0015characterised by the initial state of the material
003the material being a polymer solution or dispersion
0038the fibre formed by solvent evaporation, i.e. dry electro-spinning
D04H 1/728
DTEXTILES; PAPER
04BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
HMAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL
1Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
70characterised by the method of forming fleeces or layers, e.g. reorientation of fibres
72the fibres being randomly arranged
728by electro-spinning
D06M 15/513
DTEXTILES; PAPER
06TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
MTREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
15Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
19with synthetic macromolecular compounds
37Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
507Polyesters
513Polycarbonates
D06M 2101/30
DTEXTILES; PAPER
06TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
MTREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
2101Chemical constitution of the fibres, threads, yarns, fabrics or fibrous goods made from such materials, to be treated
16Synthetic fibres, other than mineral fibres
30Synthetic polymers consisting of macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
H01M 2/162
HELECTRICITY
01BASIC ELECTRIC ELEMENTS
MPROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
2Constructional details or processes of manufacture of the non-active parts
14Separators; Membranes; Diaphragms; Spacing elements
16characterised by the material
1606comprising fibrous material
162Organic fibrous material
Déposants
  • 青岛大学 QINGDAO UNIVERSITY [CN]/[CN]
Inventeurs
  • 杜辉 DU, Hui
  • 段雅静 DUAN, Yajing
  • 陈照军 CHEN, Zhaojun
Données relatives à la priorité
201811143576.828.09.2018CN
Langue de publication chinois (ZH)
Langue de dépôt chinois (ZH)
États désignés
Titre
(EN) PREPARATION METHOD FOR FLUORINE-CONTAINING CAPPED STRUCTURE POLYCARBONATE AND POLYIMIDE COMPOSITE FIBER MEMBRANE
(FR) PROCÉDÉ DE PRÉPARATION D'UNE MEMBRANE EN FIBRES COMPOSITES DE POLYIMIDE ET DE POLYCARBONATE À STRUCTURE COIFFÉE CONTENANT DU FLUOR
(ZH) 一种含氟封端结构的聚碳酸酯/聚酰亚胺复合纤维膜的制备方法
Abrégé
(EN)
A preparation method for a fluorine-containing capped structure polycarbonate and polyimide composite fiber membrane, comprising: first preparing a polyamic acid solution using 4,4'-diaminodiphenyl ether and pyromellitic dianhydride; performing electrospinning on the polyamic acid solution to obtain a polyamic acid fiber membrane; then performing imidization to obtain a polyimide fiber membrane, and finally dipping the polyimide fiber membrane in a polycarbonate DMF solution and vacuum-drying same, so as to obtain a fluorine-containing capped structure polycarbonate and polyimide composite fiber membrane. The polycarbonate has a fluorine-containing capped structure, effectively improving the thermal stability and affinity for electrolyte of the composite fiber membrane, improving the safety of a lithium ion battery. The preparation method is easy to operate and convenient for industrial production, achieving air permeability and affinity while improving the thermal stability performance of a separator, achieving excellent overall performance, and being applicable to the preparation for a lithium ion battery separator to satisfy high demand of use.
(FR)
La présente invention concerne un procédé de préparation de membrane en fibres composites de polyimide et de polycarbonate à structure coiffée contenant du fluor comprenant les étapes suivantes consistant : à préparer une solution d'acide polyamique en utilisant de l'éther de 4,4'-diaminodiphényle et du dianhydride pyromellitique ; à effectuer une électrofilature sur la solution d'acide polyamique afin d'obtenir une membrane en fibres d'acide polyamique ; puis à effectuer une imidisation afin d'obtenir une membrane en fibres de polyimide, et finalement, à immerger la membrane en fibres de polyimide dans une solution de DMF de polycarbonate et à sécher sous vide cette dernière, de manière à obtenir une membrane en fibres composites de polyimide et de polycarbonate à structure coiffée contenant du fluor. Le polycarbonate a une structure coiffée contenant du fluor qui améliore efficacement la stabilité thermique et l'affinité de l'électrolyte de la membrane en fibres composites et qui améliore en outre la sécurité d'une batterie aux ions de lithium. Le procédé de préparation est pratique et facile à mettre en œuvre pour la production industrielle et il favorise la perméabilité à l'air et l'affinité tout en améliorant les performances de stabilité thermique d'un séparateur, ce qui permet d'obtenir une excellente performance globale, et d'appliquer le procédé à la préparation d'un séparateur de batterie aux ions de lithium en vue de satisfaire une demande élevée d'utilisation.
(ZH)
一种含氟封端结构的聚碳酸酯/聚酰亚胺复合纤维膜的制备方法,首先采用4,4'-二氨基二苯醚和均苯四甲酸二酐制备得到聚酰胺酸溶液;将聚酰胺酸溶液静电纺丝制得聚酰胺酸纤维膜;然后进行亚胺化得到聚酰亚胺纤维膜,最后放入聚碳酸酯DMF溶液中浸泡,真空干燥后即得。该聚碳酸酯具有含氟封端结构,有效提高了复合纤维膜的热稳定性和对电解液的亲和性,提高了锂离子电池的安全性。该制备方法操作简单,便于工业化生产,实现了隔膜热稳定性能提高的同时具有较高的透气性和亲和性,综合性能优异,应用于锂离子电池隔膜的制备中以满足更高的使用要求。