(EN) Disclosed is a bivalent manganese-doped full inorganic perovskite quantum dot glass, the composition thereof being: B2O3: 25%-45%, SiO2: 25%-45%, MCO3: 1%-10%, Al2O3: 1%-10%, ZnO: 1%-5%, Cs2CO3: 1%-10%, PbCl2: 1%-10%, NaCl: 1%-10%, and MnCl2: 1%-10%, wherein M is Ca, Sr or Ba. The preparation of the quantum dot glass comprises: grinding all raw material components of the glass, melting same after uniformly mixing, then compression moulding the melt and then annealing and heat treating same, and obtaining the bivalent manganese-doped quantum dot glass through the heat treatments at different temperatures. The doped quantum dot glass prepared has good chemical stability and a higher fluorescence quantum efficiency, and is a light-emitting material with a great application prospect.
(FR) L'invention concerne un verre à boîtes quantiques de pérovskite entièrement inorganique dopé au manganèse bivalent, dont la composition est : B2O3 : 25-45 %, SiO2 : 25-45 %, MCO3 : 1-10 %, Al2O3 : 1-10 %, ZnO : 1-5 %, Cs2CO3 : 1-10 %, PbCl2 : 1-10 %, NaCl : 1-10 %, et MnCl2 : 1-10 %, où M est Ca, Sr ou Ba. La préparation du verre à boîtes quantiques comprend : le broyage de toutes les composants de départ du verre, leur fusion après mélange uniforme, puis le moulage par compression de la masse fondue et son recuit et traitement thermique, et l'obtention du verre à boîtes quantiques dopé au manganèse bivalent par des traitements thermiques à différentes températures. Le verre à boîtes quantiques dopé préparé a une bonne stabilité chimique et un rendement quantique de fluorescence supérieur, et constitue un matériau électroluminescent ayant une large perspective d'applications.
(ZH) 一种二价锰掺杂的全无机钙钛矿量子点玻璃,其组成为B2O3:25~45%, SiO2:25~45%, MCO3:1~10%, Al2O3:1~10%, ZnO:1~5%, Cs2CO3:1~10%, PbCl2:1~10%, NaCl:1~10%, MnCl2:1~10%,其中M为Ca、Sr或Ba。该量子点玻璃的制备为将各玻璃原料组分研磨,混匀后进行熔融,然后将熔体压制成型后进行退火和热处理,通过不同温度的热处理,即可得到二价锰掺杂的量子点玻璃。所制备的量子点掺杂玻璃具有良好的化学稳定性,较高的荧光量子效率,是一种极具应用前景的发光材料。