1. WO2019124271 - PROCÉDÉ DE PRODUCTION D'UNE PLAQUE DE VERRE

Numéro de publication WO/2019/124271
Date de publication 27.06.2019
N° de la demande internationale PCT/JP2018/046174
Date du dépôt international 14.12.2018
CIB
C03B 25/12 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
BFABRICATION OU FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES;  TRAITEMENTS ADDITIONNELS DANS LA FABRICATION OU LE FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES
25Recuisson des articles de verre
04en continu
10avec déplacement vertical des produits en verre
12des feuilles de verre
C03B 17/06 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
BFABRICATION OU FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES;  TRAITEMENTS ADDITIONNELS DANS LA FABRICATION OU LE FAÇONNAGE DU VERRE, DE LA LAINE MINÉRALE OU DE SCORIES
17Façonnage du verre par coulée, poussée ou étirage vers le bas ou latéral au travers de fentes ou par écoulement au-dessus de lèvres
06Façonnage de feuilles de verre
CPC
C03B 17/064
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
17Forming ; molten; glass by flowing-out, pushing-out, ; extruding; or drawing downwardly or laterally from forming slits or by overflowing over lips
06Forming glass sheets
064by the overflow downdraw fusion process; Isopipes therefor
C03B 17/067
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
17Forming ; molten; glass by flowing-out, pushing-out, ; extruding; or drawing downwardly or laterally from forming slits or by overflowing over lips
06Forming glass sheets
067combined with thermal conditioning of the sheets
C03B 18/02
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
18Shaping glass in contact with the surface of a liquid
02Forming sheets
C03B 2201/07
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
2201Type of glass produced
06Doped silica-based glasses
07Impurity concentration specified
C03B 25/08
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
25Annealing glass products
04in a continuous way
06with horizontal displacement of the glass products
08of glass sheets
C03B 25/12
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
BMANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
25Annealing glass products
04in a continuous way
10with vertical displacement of the glass products
12of glass sheets
Déposants
  • 日本電気硝子株式会社 NIPPON ELECTRIC GLASS CO., LTD. [JP]/[JP]
Inventeurs
  • 櫻林 達 SAKURABAYASHI Toru
  • 梅村 博通 UMEMURA Hiromichi
Données relatives à la priorité
2017-24400820.12.2017JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) METHOD FOR PRODUCING GLASS PLATE
(FR) PROCÉDÉ DE PRODUCTION D'UNE PLAQUE DE VERRE
(JA) ガラス板の製造方法
Abrégé
(EN)
The present invention addresses the technical problem of providing a method for producing a glass plate, whereby it becomes possible to reduce the variations in a thermal shrinkage coefficient stably while keeping the thermal shrinkage coefficient at 15 ppm or less. The method for producing a glass plate according to the present invention includes: a melting step of melting a glass batch prepared so as to be formed into a glass having a B2O3 content of 3% by mass or less in an electric melting furnace 1; a molding step of molding the molten glass Gm into a plate-like glass; a slow cooling step of slowly cooling the plate-like glass in an annealing furnace 12; and a cutting step of cutting the slowly cooled plate-like glass Gr into a predetermined size to produce a glass plate Gs having a β-OH value of less than 0.2 /mm and a thermal shrinkage coefficient of 15 ppm or less. The method is characterized in that the thermal shrinkage coefficient of the glass plate Gs is measured and the rate of the cooling of the plate-like glass in the slow cooling step is adjusted in accordance with the difference from a desired thermal shrinkage coefficient value.
(FR)
La présente invention aborde le problème technique consistant à proposer un procédé de production d'une plaque de verre, moyennant quoi il devient possible de réduire, de manière stable, les variations du coefficient de retrait thermique tout en maintenant le coefficient de retrait thermique égal ou inférieur à 15 ppm. Le procédé de production d'une plaque de verre selon la présente invention comprend : une étape de fusion consistant à faire fondre un mélange vitrifiable préparé pour donner un verre présentant une teneur en B2O3 égale ou inférieure à 3 % en masse dans un four de fusion électrique (1) ; une étape de moulage consistant à mouler le verre fondu (Gm) pour obtenir un verre en forme de plaque ; une étape de refroidissement lent consistant à refroidir lentement le verre en forme de plaque dans un four à recuire (12) ; et une étape de découpe consistant à découper le verre en forme de plaque lentement refroidi (Gr) à une taille prédéterminée pour obtenir une plaque de verre (Gs) présentant une valeur β-OH inférieure à 0,2/mm et un coefficient de retrait thermique égal ou inférieur à 15 ppm. Le procédé est caractérisé en ce que le coefficient de retrait thermique de la plaque de verre (Gs) est mesuré et en ce que la vitesse de refroidissement du verre en forme de plaque lors de l'étape de refroidissement lent est ajustée en fonction de la différence par rapport à une valeur de coefficient de retrait thermique recherchée.
(JA)
本発明は、熱収縮率を15ppm以下にしながら、熱収縮率のばらつきを安定して抑えることが可能なガラス板の製造方法を提供することを技術的課題とする。本発明のガラス板の製造方法は、Bが3質量%以下のガラスとなるように調製されたガラスバッチを電気溶融炉1で溶融する溶融工程、溶融ガラスGmを板状ガラスに成形する成形工程、板状ガラスを徐冷炉12で徐冷する徐冷工程、徐冷した板状ガラスGrを所定寸法に切断することによって、β-OH値が0.2/mm未満で、熱収縮率が15ppm以下のガラス板Gsを得る切断工程、を含み、前記ガラス板Gsの熱収縮率を測定し、熱収縮率の目標値に対するばらつきに応じて徐冷工程における前記板状ガラスの冷却速度を調整することを特徴とする。