1. (WO2019066328) FIL MACHINE ET FIL D'ACIER POUR RESSORTS AYANT D'EXCELLENTES PROPRIÉTÉS DE RÉSISTANCE À LA FATIGUE À LA CORROSION, ET LEUR PROCÉDÉ DE PRODUCTION
Dernières données bibliographiques dont dispose le Bureau international    Formuler une observation

N° de publication : WO/2019/066328 N° de la demande internationale : PCT/KR2018/010764
Date de publication : 04.04.2019 Date de dépôt international : 13.09.2018
CIB :
C22C 38/24 (2006.01) ,C22C 38/02 (2006.01) ,C22C 38/04 (2006.01) ,C22C 38/34 (2006.01) ,C22C 38/26 (2006.01) ,C21D 3/04 (2006.01) ,C21D 8/06 (2006.01) ,C21D 9/52 (2006.01)
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
C
ALLIAGES
38
Alliages ferreux, p.ex. aciers alliés
18
contenant du chrome
24
et du vanadium
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
C
ALLIAGES
38
Alliages ferreux, p.ex. aciers alliés
02
contenant du silicium
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
C
ALLIAGES
38
Alliages ferreux, p.ex. aciers alliés
04
contenant du manganèse
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
C
ALLIAGES
38
Alliages ferreux, p.ex. aciers alliés
18
contenant du chrome
34
et plus de 1,5% en poids de silicium
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
C
ALLIAGES
38
Alliages ferreux, p.ex. aciers alliés
18
contenant du chrome
26
et du niobium ou du tantale
C CHIMIE; MÉTALLURGIE
21
MÉTALLURGIE DU FER
D
MODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
3
Procédés de diffusion pour l'extraction de non-métaux; Fours à cet effet
02
Extraction de non-métaux
04
Décarburation
C CHIMIE; MÉTALLURGIE
21
MÉTALLURGIE DU FER
D
MODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
8
Modification des propriétés physiques par déformation en combinaison avec, ou suivie par, un traitement thermique
06
pendant la fabrication de barres ou de fils
C CHIMIE; MÉTALLURGIE
21
MÉTALLURGIE DU FER
D
MODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9
Traitement thermique, p.ex. recuit, durcissement, trempe, revenu, adapté à des objets particuliers; Fours à cet effet
52
pour fils métalliques; pour bandes métalliques
Déposants :
주식회사 포스코 POSCO [KR/KR]; 경상북도 포항시 남구 동해안로 6261 (괴동동) (Goedong-dong) 6261, Donghaean-ro, Nam-gu Pohang-si, Gyeongsangbuk-do 37859, KR
Inventeurs :
김관호 KIM, Kwan-Ho; KR
Mandataire :
특허법인 씨엔에스 C&S PATENT AND LAW OFFICE; 서울시 강남구 언주로30길 13, 대림아크로텔 7층 7th Floor, Daelim Acrotel 13, Eonju-ro 30-gil Gangnam-gu, Seoul 06292, KR
Données relatives à la priorité :
10-2017-012726329.09.2017KR
Titre (EN) WIRE ROD AND STEEL WIRE FOR SPRINGS HAVING EXCELLENT CORROSION FATIGUE RESISTANCE PROPERTIES, AND METHOD FOR PRODUCING SAME
(FR) FIL MACHINE ET FIL D'ACIER POUR RESSORTS AYANT D'EXCELLENTES PROPRIÉTÉS DE RÉSISTANCE À LA FATIGUE À LA CORROSION, ET LEUR PROCÉDÉ DE PRODUCTION
(KO) 내부식 피로특성이 우수한 스프링용 선재, 강선 및 이들의 제조방법
Abrégé :
(EN) The present invention relates to a wire rod and a steel wire which are for springs and have excellent corrosion fatigue resistance properties, and a method for producing same, and more particularly, to a wire rod and a steel wire which are for springs and have excellent corrosion fatigue resistance properties, and a method for producing same, wherein the wire rod and steel wire can be applied to vehicle suspensions springs, torsion bars, and stabilizers. An embodiment of the present invention provides a wire rod and a steel wire which are for springs and have excellent corrosion fatigue resistance properties, and a method for producing same, the wire rod and steel wire containing, in wt%, 0.40-0.70% of C, 1.20-2.30% of Si, 0.20-0.80% of Mn, 0.20-0.80% of Cr, 0.015% or less of P, 0.015% or less of S, and 0.010% or less of N, with the remainder comprising Fe and other unavoidable impurities, along with at least one among 0.01-0.20% of V and 0.01-0.10% of Nb, wherein the V and Nb satisfy relational expression 1 below, the average grain size of spherical austenite is no greater than 20 µm, and the surface decarburization depth is no greater than 0.1 mm. [Relational expression 1] [V]+[Nb] ≥ 0.08 (where the V and Nb contents are in wt%)
(FR) La présente invention concerne un fil machine et un fil d'acier qui sont destinés à des ressorts et ont d'excellentes propriétés de résistance à la fatigue à la corrosion, et leur procédé de production, et plus particulièrement, un fil machine et un fil d'acier qui sont destinés à des ressorts et ont d'excellentes propriétés de résistance à la fatigue à la corrosion, et un procédé de production de ceux-ci, le fil machine et le fil d'acier pouvant être appliqués à des ressorts de suspension de véhicule, des barres de torsion et des stabilisateurs. Un mode de réalisation de la présente invention concerne un fil machine et un fil d'acier qui sont destinés pour des ressorts et ont d'excellentes propriétés de résistance à la fatigue à la corrosion, et un procédé de production de ceux-ci, le fil machine et le fil d'acier contenant, en % en poids, 0,40 à 0,70 % de C, 1,20 à 2,30 % de Si, 0,20 à 0,80 % de Mn, 0,20 à 0,80 % de Cr, 0 015 % ou moins de P, 0 015 % ou moins de S, et 0 010 % ou moins de N, le reste comprenant du Fe et d'autres impuretés inévitables, ainsi qu'au moins l'un parmi 0,01 à 0,20 % de V et 0,01 à 0,10 % de Nb, le V et le Nb satisfaisant l'expression relationnelle 1 ci-dessous, la taille moyenne des grains d'austénite sphérique n'étant pas supérieure à 20 µm, et la profondeur de décarburation superficielle n'étant pas supérieure à 0,1 mm. [Expression relationnelle 1] [V] + [Nb] ≥ 0,08 (où les teneurs en V et Nb sont en % en poids)
(KO) 본 발명은 내부식 피로특성이 우수한 스프링용 선재, 강선 및 이들의 제조방법에 관한 것으로서, 보다 상세하게는 자동차용 현가 스프링, 토션 바, 스태빌라이저 등에 적용 가능한 내부식 피로특성이 우수한 스프링용 선재, 강선 및 이들의 제조방법에 관한 것이다. 본 발명의 일 실시형태는 중량%로, C: 0.40~0.70%, Si: 1.20~2.30%, Mn: 0.20~0.80%, Cr: 0.20~0.80%, P: 0.015% 이하, S: 0.015% 이하, N: 0.010% 이하, 잔부 Fe 및 기타 불가피한 불순물을 포함하고, 추가로, V: 0.01~0.20% 및 Nb: 0.01~0.10% 중 1종 또는 2종을 포함하며, 상기 V 및 Nb는 하기 관계식 1을 만족하고, 구오스테나이트의 평균 결정립 크기는 20㎛ 이하이며, 표면 탈탄 깊이는 0.1mm 이하인 내부식 피로특성이 우수한 스프링용 선재, 강선 및 이들의 제조방법을 제공한다. [관계식 1] [V]+[Nb] ≥ 0.08 (단, 상기 V 및 Nb의 함량은 중량%를 의미함.)
front page image
États désignés : AE, AG, AL, AM, AO, AT, AU, AZ, BA, BB, BG, BH, BN, BR, BW, BY, BZ, CA, CH, CL, CN, CO, CR, CU, CZ, DE, DJ, DK, DM, DO, DZ, EC, EE, EG, ES, FI, GB, GD, GE, GH, GM, GT, HN, HR, HU, ID, IL, IN, IR, IS, JO, JP, KE, KG, KH, KN, KP, KW, KZ, LA, LC, LK, LR, LS, LU, LY, MA, MD, ME, MG, MK, MN, MW, MX, MY, MZ, NA, NG, NI, NO, NZ, OM, PA, PE, PG, PH, PL, PT, QA, RO, RS, RU, RW, SA, SC, SD, SE, SG, SK, SL, SM, ST, SV, SY, TH, TJ, TM, TN, TR, TT, TZ, UA, UG, US, UZ, VC, VN, ZA, ZM, ZW
Organisation régionale africaine de la propriété intellectuelle (ARIPO) (BW, GH, GM, KE, LR, LS, MW, MZ, NA, RW, SD, SL, ST, SZ, TZ, UG, ZM, ZW)
Office eurasien des brevets (OEAB) (AM, AZ, BY, KG, KZ, RU, TJ, TM)
Office européen des brevets (OEB) (AL, AT, BE, BG, CH, CY, CZ, DE, DK, EE, ES, FI, FR, GB, GR, HR, HU, IE, IS, IT, LT, LU, LV, MC, MK, MT, NL, NO, PL, PT, RO, RS, SE, SI, SK, SM, TR)
Organisation africaine de la propriété intellectuelle (OAPI) (BF, BJ, CF, CG, CI, CM, GA, GN, GQ, GW, KM, ML, MR, NE, SN, TD, TG)
Langue de publication : coréen (KO)
Langue de dépôt : coréen (KO)