1. (WO2019064679) SUBSTRAT EN ALLIAGE D’ALUMINIUM POUR DISQUES MAGNÉTIQUES, SON PROCÉDÉ DE PRODUCTION, ET DISQUE MAGNÉTIQUE UTILISANT LEDIT SUBSTRAT EN ALLIAGE D’ALUMINIUM POUR DISQUES MAGNÉTIQUES
Dernières données bibliographiques dont dispose le Bureau international    Formuler une observation

N° de publication : WO/2019/064679 N° de la demande internationale : PCT/JP2018/018817
Date de publication : 04.04.2019 Date de dépôt international : 15.05.2018
CIB :
C22C 21/00 (2006.01) ,C22F 1/04 (2006.01) ,G11B 5/73 (2006.01) ,G11B 5/82 (2006.01) ,G11B 5/84 (2006.01) ,G11B 25/04 (2006.01) ,C22F 1/00 (2006.01)
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
C
ALLIAGES
21
Alliages à base d'aluminium
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
F
MODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX OU ALLIAGES NON FERREUX
1
Modification de la structure physique des métaux ou alliages non ferreux par traitement thermique ou par travail à chaud ou à froid
04
de l'aluminium ou de ses alliages
G PHYSIQUE
11
ENREGISTREMENT DE L'INFORMATION
B
ENREGISTREMENT DE L'INFORMATION BASÉ SUR UN MOUVEMENT RELATIF ENTRE LE SUPPORT D'ENREGISTREMENT ET LE TRANSDUCTEUR
5
Enregistrement par magnétisation ou démagnétisation d'un support d'enregistrement; Reproduction par des moyens magnétiques; Supports d'enregistrement correspondants
62
Supports d'enregistrement caractérisés par l'emploi d'un matériau spécifié
73
Couches de base
G PHYSIQUE
11
ENREGISTREMENT DE L'INFORMATION
B
ENREGISTREMENT DE L'INFORMATION BASÉ SUR UN MOUVEMENT RELATIF ENTRE LE SUPPORT D'ENREGISTREMENT ET LE TRANSDUCTEUR
5
Enregistrement par magnétisation ou démagnétisation d'un support d'enregistrement; Reproduction par des moyens magnétiques; Supports d'enregistrement correspondants
74
Supports d'enregistrement caractérisés par leur forme, p.ex. feuille ayant une forme lui permettant de s'enrouler autour d'un tambour
82
Disques
G PHYSIQUE
11
ENREGISTREMENT DE L'INFORMATION
B
ENREGISTREMENT DE L'INFORMATION BASÉ SUR UN MOUVEMENT RELATIF ENTRE LE SUPPORT D'ENREGISTREMENT ET LE TRANSDUCTEUR
5
Enregistrement par magnétisation ou démagnétisation d'un support d'enregistrement; Reproduction par des moyens magnétiques; Supports d'enregistrement correspondants
84
Procédés ou appareils spécialement adaptés à la fabrication de supports d'enregistrement
G PHYSIQUE
11
ENREGISTREMENT DE L'INFORMATION
B
ENREGISTREMENT DE L'INFORMATION BASÉ SUR UN MOUVEMENT RELATIF ENTRE LE SUPPORT D'ENREGISTREMENT ET LE TRANSDUCTEUR
25
Appareils caractérisés par la forme du support d'enregistrement employé mais non spécifiques du procédé d'enregistrement ou de reproduction
04
utilisant des supports d'enregistrement plats, p.ex. disques, cartes
C CHIMIE; MÉTALLURGIE
22
MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
F
MODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX OU ALLIAGES NON FERREUX
1
Modification de la structure physique des métaux ou alliages non ferreux par traitement thermique ou par travail à chaud ou à froid
Déposants :
株式会社UACJ UACJ CORPORATION [JP/JP]; 東京都千代田区大手町一丁目7番2号 1-7-2, Otemachi, Chiyoda-ku, Tokyo 1000004, JP
古河電気工業株式会社 FURUKAWA ELECTRIC CO., LTD. [JP/JP]; 東京都千代田区丸の内二丁目2番3号 2-3, Marunouchi 2-chome, Chiyoda-ku, Tokyo 1008322, JP
Inventeurs :
北脇 高太郎 KITAWAKI Kotaro; JP
畠山 英之 HATAKEYAMA Hideyuki; JP
中山 賢 NAKAYAMA Takashi; JP
藤井 康生 FUJII Yasuo; JP
熊谷 航 KUMAGAI Wataru; JP
Mandataire :
木村 満 KIMURA MITSURU; 東京都千代田区神田錦町二丁目7番地 協販ビル2階 2nd Floor, Kyohan Building, 7, Kandanishiki-cho 2-chome, Chiyoda-ku, Tokyo 1010054, JP
Données relatives à la priorité :
2017-18916928.09.2017JP
Titre (EN) ALUMINUM ALLOY SUBSTRATE FOR MAGNETIC DISKS, METHOD FOR PRODUCING SAME, AND MAGNETIC DISK USING SAID ALUMINUM ALLOY SUBSTRATE FOR MAGNETIC DISKS
(FR) SUBSTRAT EN ALLIAGE D’ALUMINIUM POUR DISQUES MAGNÉTIQUES, SON PROCÉDÉ DE PRODUCTION, ET DISQUE MAGNÉTIQUE UTILISANT LEDIT SUBSTRAT EN ALLIAGE D’ALUMINIUM POUR DISQUES MAGNÉTIQUES
(JA) 磁気ディスク用アルミニウム合金基板及びその製造方法、ならびに、当該磁気ディスク用アルミニウム合金基板を用いた磁気ディスク
Abrégé :
(EN) An aluminum alloy substrate for magnetic disks, which is formed from an aluminum alloy that contains 0.4-3.0 mass% (hereinafter referred to as "%") of Fe, less than 0.10% of Si and less than 0.10% of Mg, with the balance being made up of Al and unavoidable impurities, and wherein Al-Fe intermetallic compounds having a maximum length of 2 μm or more but less than 3 μm are dispersed at a distribution density of 1,000 compounds/mm2 or more and Mg-Si intermetallic compounds having a maximum length of 1 μm or more are dispersed at a distribution density of 1 compound/mm2 or less; a method for producing this aluminum alloy substrate for magnetic disks; and a magnetic disk which is obtained by arranging an electroless Ni-P plating layer on the surface of this aluminum alloy substrate for magnetic disks, and subsequently arranging a magnetic layer on the electroless Ni-P plating layer.
(FR) La présente invention concerne un substrat en alliage d’aluminium pour disques magnétiques, qui est formé d’un alliage d’aluminium qui contient de 0,4 à 3,0 % en masse (appelé ci-après "%") de Fe, moins de 0,10 % de Si et moins de 0,10 % de Mg, le reste étant constitué de Al et d’impuretés inévitables, et des composés intermétalliques Al-Fe ayant une longueur maximale de 2 µm ou plus mais moins de 3 µm étant dispersés à une densité de distribution de 1 000 composés/mm2 ou plus et des composés intermétalliques Mg-Si ayant une longueur maximale de 1 µm ou plus étant dispersés à une densité de distribution de 1 composé/mm2 ou moins ; un procédé de production de ce substrat en alliage d’aluminium pour disques magnétiques ; et un disque magnétique qui est obtenu par agencement d’une couche de placage de Ni-P autocatalytique sur la surface de ce substrat en alliage d’aluminium pour disques magnétiques, et ensuite l’agencement d’une couche magnétique sur la couche de placage de Ni-P autocatalytique.
(JA) Fe:0.4~3.0mass%(以下、「%」)、Si:0.10%未満、Mg:0.10%未満を含有し、残部Al及び不可避不純物からなるアルミニウム合金からなり、2μm以上3μm未満の最長径を有するAl-Fe系金属間化合物が1000個/mm以上の分布密度で分散し、1μm以上の最長径を有するMg-Si系金属間化合物が1個/mm以下の分布密度で分散する磁気ディスク用アルミニウム合金基板及びその製造方法、ならびに、当該磁気ディスク用アルミニウム合金基板の表面に、無電解Ni-Pめっき処理層とその上の磁性体層が設けられている磁気ディスク。
front page image
États désignés : AE, AG, AL, AM, AO, AT, AU, AZ, BA, BB, BG, BH, BN, BR, BW, BY, BZ, CA, CH, CL, CN, CO, CR, CU, CZ, DE, DJ, DK, DM, DO, DZ, EC, EE, EG, ES, FI, GB, GD, GE, GH, GM, GT, HN, HR, HU, ID, IL, IN, IR, IS, JO, KE, KG, KH, KN, KP, KR, KW, KZ, LA, LC, LK, LR, LS, LU, LY, MA, MD, ME, MG, MK, MN, MW, MX, MY, MZ, NA, NG, NI, NO, NZ, OM, PA, PE, PG, PH, PL, PT, QA, RO, RS, RU, RW, SA, SC, SD, SE, SG, SK, SL, SM, ST, SV, SY, TH, TJ, TM, TN, TR, TT, TZ, UA, UG, US, UZ, VC, VN, ZA, ZM, ZW
Organisation régionale africaine de la propriété intellectuelle (ARIPO) (BW, GH, GM, KE, LR, LS, MW, MZ, NA, RW, SD, SL, ST, SZ, TZ, UG, ZM, ZW)
Office eurasien des brevets (OEAB) (AM, AZ, BY, KG, KZ, RU, TJ, TM)
Office européen des brevets (OEB) (AL, AT, BE, BG, CH, CY, CZ, DE, DK, EE, ES, FI, FR, GB, GR, HR, HU, IE, IS, IT, LT, LU, LV, MC, MK, MT, NL, NO, PL, PT, RO, RS, SE, SI, SK, SM, TR)
Organisation africaine de la propriété intellectuelle (OAPI) (BF, BJ, CF, CG, CI, CM, GA, GN, GQ, GW, KM, ML, MR, NE, SN, TD, TG)
Langue de publication : japonais (JA)
Langue de dépôt : japonais (JA)