Traitement en cours

Veuillez attendre...

Paramétrages

Paramétrages

Aller à Demande

1. WO2012133668 - FILM DE RÉSINE DE POLY(VINYLACÉTAL) ET STRUCTURE MULTICOUCHE L'UTILISANT

Numéro de publication WO/2012/133668
Date de publication 04.10.2012
N° de la demande internationale PCT/JP2012/058406
Date du dépôt international 29.03.2012
CIB
C08J 5/18 2006.01
CCHIMIE; MÉTALLURGIE
08COMPOSÉS MACROMOLÉCULAIRES ORGANIQUES; LEUR PRÉPARATION OU LEUR MISE EN UVRE CHIMIQUE; COMPOSITIONS À BASE DE COMPOSÉS MACROMOLÉCULAIRES
JMISE EN ŒUVRE; PROCÉDÉS GÉNÉRAUX POUR FORMER DES MÉLANGES; POST-TRAITEMENT NON COUVERT PAR LES SOUS-CLASSES C08B, C08C, C08F, C08G ou C08H149
5Fabrication d'objets ou de matériaux façonnés contenant des substances macromoléculaires
18Fabrication de bandes ou de feuilles
B29C 47/88 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
29TRAVAIL DES MATIÈRES PLASTIQUES; TRAVAIL DES SUBSTANCES À L'ÉTAT PLASTIQUE EN GÉNÉRAL
CFAÇONNAGE OU ASSEMBLAGE DES MATIÈRES PLASTIQUES; FAÇONNAGE DES MATIÈRES À L'ÉTAT PLASTIQUE NON PRÉVU AILLEURS; POST-TRAITEMENT DES PRODUITS FAÇONNÉS, p.ex. RÉPARATION
47Moulage par extrusion, c. à d. en exprimant la matière à mouler dans une matrice ou une filière qui lui donne la forme désirée; Appareils à cet effet
08Eléments constitutifs, détails ou accessoires; Opérations auxiliaires
78Chauffage ou refroidissement de la matière à extruder ou de la matière extrudée
88Chauffage ou refroidissement de la matière extrudée
B29C 47/92 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
29TRAVAIL DES MATIÈRES PLASTIQUES; TRAVAIL DES SUBSTANCES À L'ÉTAT PLASTIQUE EN GÉNÉRAL
CFAÇONNAGE OU ASSEMBLAGE DES MATIÈRES PLASTIQUES; FAÇONNAGE DES MATIÈRES À L'ÉTAT PLASTIQUE NON PRÉVU AILLEURS; POST-TRAITEMENT DES PRODUITS FAÇONNÉS, p.ex. RÉPARATION
47Moulage par extrusion, c. à d. en exprimant la matière à mouler dans une matrice ou une filière qui lui donne la forme désirée; Appareils à cet effet
08Eléments constitutifs, détails ou accessoires; Opérations auxiliaires
92Mesure, commande ou régulation
C03C 27/12 2006.01
CCHIMIE; MÉTALLURGIE
03VERRE; LAINE MINÉRALE OU DE SCORIES
CCOMPOSITION CHIMIQUE DES VERRES, GLAÇURES OU ÉMAUX VITREUX; TRAITEMENT DE LA SURFACE DU VERRE; TRAITEMENT DE SURFACE DES FIBRES OU FILAMENTS DE VERRE, DE SUBSTANCES MINÉRALES OU DE SCORIES; LIAISON DU VERRE AU VERRE OU À D'AUTRES MATÉRIAUX
27Liaison de pièces de verre à des pièces en d'autres matériaux inorganiques; Liaison verre-verre par des procédés autres que la fusion
06Liaison verre-verre par des procédés autres que la fusion
10au moyen d'un adhésif spécialement adapté à ce but
12Verre stratifié
B29K 29/00 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
29TRAVAIL DES MATIÈRES PLASTIQUES; TRAVAIL DES SUBSTANCES À L'ÉTAT PLASTIQUE EN GÉNÉRAL
KSCHÉMA D'INDEXATION ASSOCIÉ AUX SOUS-CLASSES B29B, B29C OU B29D105
29Utilisation de poly(alcool de vinyle), poly(éthers de vinyle), poly(aldéhydes de vinyle), poly(cétones de vinyle) ou poly(cétals de vinyle) comme matière de moulage
B29L 7/00 2006.01
BTECHNIQUES INDUSTRIELLES; TRANSPORTS
29TRAVAIL DES MATIÈRES PLASTIQUES; TRAVAIL DES SUBSTANCES À L'ÉTAT PLASTIQUE EN GÉNÉRAL
LSCHÉMA D'INDEXATION ASSOCIÉ À LA SOUS-CLASSE B29C63
7Objets plats, p.ex. pellicules ou feuilles
CPC
B29C 2948/92171
BPERFORMING OPERATIONS; TRANSPORTING
29WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
CSHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
2948Indexing scheme relating to extrusion moulding
92Measuring, controlling or regulating
92009Measured parameter
92114Dimensions
92171Distortion, shrinkage, dilatation, swell or warpage
B29C 2948/922
BPERFORMING OPERATIONS; TRANSPORTING
29WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
CSHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
2948Indexing scheme relating to extrusion moulding
92Measuring, controlling or regulating
92009Measured parameter
922Viscosity; Melt flow index [MFI]; Molecular weight
B29C 2948/92209
BPERFORMING OPERATIONS; TRANSPORTING
29WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
CSHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
2948Indexing scheme relating to extrusion moulding
92Measuring, controlling or regulating
92009Measured parameter
92209Temperature
B29C 2948/92428
BPERFORMING OPERATIONS; TRANSPORTING
29WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
CSHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
2948Indexing scheme relating to extrusion moulding
92Measuring, controlling or regulating
92323Location or phase of measurement
92428Calibration, after-treatment, or cooling zone
B29C 2948/92485
BPERFORMING OPERATIONS; TRANSPORTING
29WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
CSHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
2948Indexing scheme relating to extrusion moulding
92Measuring, controlling or regulating
92323Location or phase of measurement
92485Start-up, shut-down or parameter setting phase; Emergency shut-down; Material change; Test or laboratory equipment or studies
B29C 2948/92647
BPERFORMING OPERATIONS; TRANSPORTING
29WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
CSHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
2948Indexing scheme relating to extrusion moulding
92Measuring, controlling or regulating
92504Controlled parameter
92609Dimensions
92647Thickness
Déposants
  • 株式会社クラレ KURARAY CO., LTD. [JP]/[JP] (AllExceptUS)
  • 小田英晶 ODA Hidemasa [JP]/[JP] (UsOnly)
  • 向瀬峰 MUKOSE Takashi [JP]/[JP] (UsOnly)
  • 床尾万喜雄 TOKOH Makio [JP]/[JP] (UsOnly)
Inventeurs
  • 小田英晶 ODA Hidemasa
  • 向瀬峰 MUKOSE Takashi
  • 床尾万喜雄 TOKOH Makio
Mandataires
  • 田村良介 TAMURA Ryosuke
Données relatives à la priorité
2011-07209029.03.2011JP
Langue de publication japonais (JA)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) POLY(VINYL ACETAL) RESIN FILM AND MULTILAYER STRUCTURE USING SAME
(FR) FILM DE RÉSINE DE POLY(VINYLACÉTAL) ET STRUCTURE MULTICOUCHE L'UTILISANT
(JA) ポリビニルアセタール系樹脂フィルムおよびそれを用いた多層構造体
Abrégé
(EN)
The invention prevents the intrusion of bubbles and the occurrence of unfilled areas at the edges of poly(vinyl acetal) resin films that are used as one layer of multilayer structures such as laminated glass or solar cell modules by: the range of thickness thereof in the width direction being 10% or less; the volatile matter content being 1.0 mass% or less; and making MD1, MD2 and MD3 all to be 3 - 20% when the portions that are 5% of the total width from either edge in the width direction are each heated for 30 minutes at 150°C and the larger value of the thermal shrinkages in the direction of flow, which is parallel thereto and perpendicular to the width direction, is called thermal shrinkage MD1 and the other value is called MD2 and, when the central portion in the width direction is heated for 30 minutes at 150°C and the thermal shrinkage in the direction of flow, which is parallel thereto and perpendicular to the width direction, is called thermal shrinkage MD3.
(FR)
L'invention concerne la prévention de l'intrusion de bulles et de l'occurrence de zones non remplies au niveau des bords de films de résine de poly(vinylacétal) qui sont utilisés comme une couche de structures multicouches telles que le verre stratifié ou des modules de cellules solaires : grâce à la plage d'épaisseur dans le sens de la largeur de 10% ou moins ; grâce à la teneur en matière volatile de 1,0% en masse ou moins ; et en rendant toutes les valeurs de retraits thermiques MD1, MD2 et MD3 entre 3-20%, quand les parties qui représentent 5% de la largeur totale à partir de l'un ou l'autre bord dans le sens de la largeur sont chacune chauffées pendant 30 minutes à 150°C, la plus grande valeur des retraits thermiques dans le sens de l'écoulement, qui est parallèle à celui-ci et perpendiculaire au sens de la largeur, est appelée retrait thermique MD1 et l'autre valeur est appelée MD2 et, quand la partie centrale dans le sens de la largeur est chauffée pendant 30 minutes à 150°C, le retrait thermique dans le sens de l'écoulement, qui est parallèle à celui-ci et perpendiculaire au sens de la largeur, est appelé retrait thermique MD3.
(JA)
本発明は、合わせガラスや太陽電池モジュール等の多層構造体の一層に使用されるポリビニルアセタール系樹脂フィルムにおいて、その幅方向の厚さ分布が10%以下、揮発分が1.0質量%以下であり、幅方向の両端からその全幅の5%内側部分についてそれぞれ150℃で30分加熱した際に、それに平行かつ幅方向に垂直である流れ方向の熱収縮率が大きい方の値を熱収縮率MD1、もう一方の値をMD2とし、その幅方向の中央部分を150℃で30分加熱した際のそれに平行かつ幅方向に垂直である流れ方向の熱収縮率を熱収縮率MD3とした場合に、上記MD1、MD2及びMD3のいずれもが3~20%とすることにより、その端部での泡の噛み込みや未充填部分の発生を防止する。