1. WO2011108159 - COMPOSÉ FERRO-ALUMINATE DE CALCIUM, ADJUVANT DE CIMENT ET SON PROCÉDÉ DE FABRICATION, ET COMPOSITION DE CIMENT

Numéro de publication WO/2011/108159
Date de publication 09.09.2011
N° de la demande internationale PCT/JP2010/070972
Date du dépôt international 25.11.2010
CIB
C04B 22/08 2006.1
CCHIMIE; MÉTALLURGIE
04CIMENTS; BÉTON; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES
BCHAUX; MAGNÉSIE; SCORIES; CIMENTS; LEURS COMPOSITIONS, p.ex. MORTIERS, BÉTON OU MATÉRIAUX DE CONSTRUCTION SIMILAIRES; PIERRE ARTIFICIELLE; CÉRAMIQUES; RÉFRACTAIRES; TRAITEMENT DE LA PIERRE NATURELLE
22Emploi de matières inorganiques comme ingrédients actifs pour mortiers, béton ou pierre artificielle, p.ex. emploi d'accélérateurs 
08Acides ou leurs sels
C01G 49/00 2006.1
CCHIMIE; MÉTALLURGIE
01CHIMIE INORGANIQUE
GCOMPOSÉS CONTENANT DES MÉTAUX NON COUVERTS PAR LES SOUS-CLASSES C01D OU C01F104
49Composés du fer
CPC
C01G 49/0036
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
49Compounds of iron
0018Mixed oxides or hydroxides,
0036containing one alkaline earth metal, magnesium or lead
C01G 49/0045
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
49Compounds of iron
0018Mixed oxides or hydroxides,
0045containing aluminium
C01P 2002/72
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
2002Crystal-structural characteristics
70defined by measured X-ray, neutron or electron diffraction data
72by d-values or two theta-values, e.g. as X-ray diagram
C04B 2111/26
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2111Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
20Resistance against chemical, physical or biological attack
26Corrosion of reinforcement resistance
C04B 22/0093
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
22Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators ; , shrinkage compensating agents
0093Aluminates
C04B 28/02
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
28Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
02containing hydraulic cements other than calcium sulfates
Déposants
  • 電気化学工業株式会社 DENKI KAGAKU KOGYO KABUSHIKI KAISHA [JP]/[JP] (AllExceptUS)
  • 森泰一郎 MORI Taiichiro [JP]/[JP] (UsOnly)
  • 田原和人 TABARA Kazuto [JP]/[JP] (UsOnly)
  • 山本賢司 YAMAMOTO Kenji [JP]/[JP] (UsOnly)
  • 盛岡実 MORIOKA Minoru [JP]/[JP] (UsOnly)
  • 樋口隆行 HIGUCHI Takayuki [JP]/[JP] (UsOnly)
Inventeurs
  • 森泰一郎 MORI Taiichiro
  • 田原和人 TABARA Kazuto
  • 山本賢司 YAMAMOTO Kenji
  • 盛岡実 MORIOKA Minoru
  • 樋口隆行 HIGUCHI Takayuki
Mandataires
  • 松本 悟 MATSUMOTO Satoru
Données relatives à la priorité
PCT/JP2010/05327001.03.2010JP
Langue de publication Japonais (ja)
Langue de dépôt japonais (JA)
États désignés
Titre
(EN) CALCIUM FERROALUMINATE COMPOUND, CEMENT ADMIXTURE AND PROCESS FOR PRODUCING SAME, AND CEMENT COMPOSITION
(FR) COMPOSÉ FERRO-ALUMINATE DE CALCIUM, ADJUVANT DE CIMENT ET SON PROCÉDÉ DE FABRICATION, ET COMPOSITION DE CIMENT
(JA) カルシウムフェロアルミネート化合物、セメント混和材及びその製造方法、セメント組成物
Abrégé
(EN) Provided is a cement admixture which gives cured cement concrete that imparts excellent non-corrodible properties to the reinforcing bars present therein, has resistance to external infiltration of chloride ions, and can be inhibited from becoming porous because Ca-ion eluviation occurs little and that has self-healing ability. Also provided is a cement composition. The cement admixture is characterized by comprising a calcium ferroaluminate compound which is based on CaO, Al2O3, and Fe2O3, has an Fe2O3 content of 0.5-15 mass%, and has a CaO·2Al2O3 structure, the CaO/Al2O3 ratio being in the range of 0.15-0.7 by mole. It is preferred that the admixture have a degree of fineness of 2,000-7,000 cm2/g in terms of Blaine specific surface area and that a latent hydraulic substance and/or a pozzolanic substance (pozzolanic substance and the like) be used in combination with the calcium ferroaluminate compound. The pozzolanic substance and the like preferably comprise one or more substances selected from a group consisting of ground granulated blast furnace slag, fly ash, silica fume, metakaolin, incineration ash of pulp sludge, incineration ash of sewage sludge, and waste glass powder. It is preferred that the ratio of the calcium ferroaluminate compound to the pozzolanic substance and the like be from 10/1 to 1/10 by mass. The cement composition comprises a cement and the cement admixture.
(FR) L'invention porte sur un adjuvant de ciment qui donne un béton de ciment durci qui confère d'excellentes propriétés anti-corrosion à des barres d'armature qui y sont présentes, qui possède une résistance aux infiltrations externes d'ions chlorure, et dont il est possible d'empêcher la porosité, du fait qu'il y a peu d'éluviation des ions Ca et qui présente une capacité d'autoréparation. L'invention porte également sur une composition de ciment. L'adjuvant de ciment est caractérisé en ce qu'il comprend un composé ferro-aluminate de calcium qui est à base de CaO, d'Al2O3 et de Fe2O3, qui a une teneur en Fe2O3 de 0,5 à 15 % en masse et qui a une structure CaO·2Al2O3, le rapport CaO/Al2O3 étant compris dans la plage de 0,15 à 0,7 en moles. De préférence, l'adjuvant possède un degré de finesse de 2 000 à 7 000 cm2/g en termes de l'aire spécifique de Blaine, et une substance hydraulique latente et/ou une substance pouzzolanique (substance pouzzolanique et autres) est utilisée en combinaison avec le composé ferro-aluminate de calcium. La substance pouzzolanique et autres comportent, de préférence, une ou plusieurs substances choisies dans un groupe constitué par un laitier de haut fourneau granulé et broyé, des cendres volantes, des fumées de silice, du métakaolin, des cendres d'incinération des boues de pulpe, des cendres d'incinération des boues d'épuration et de la poudre de verre de déchets. De préférence, le rapport du composé ferro-aluminate de calcium à la substance pouzzolanique et autres est de 10/1 à 1/10 en masse. La composition de ciment comporte un ciment et l'adjuvant de ciment.
(JA)  セメントコンクリート硬化体において、内部の鉄筋に優れた防錆効果を付与し、外部から侵入する塩化物イオンの浸透抵抗性を有し、さらに、Caイオンの溶脱も少ないため多孔化も抑制でき、さらに自己治癒能力を有するセメント混和材及びセメント組成物を提供することを課題とする CaO-Al-Fe系からなり、Feの含有量が0.5~15質量%であり、CaO・2Al構造を持つカルシウムフェロアルミネート化合物を含有し、CaO/Alモル比が、0.15~0.7の範囲にあることを特徴とするセメント混和材である。粉末度が、ブレーン比表面積値で2,000~7,000cm/gであること、さらに潜在水硬性物質および/またはポゾラン物質(ポゾラン物質等)を併用すること、前記ポゾラン物質等が、高炉水砕スラグ微粉末、フライアッシュ、シリカフューム、メタカオリン、パルプスラッジ焼却灰、下水汚泥焼却灰、及び廃ガラス粉末からなる群から選ばれた一種または二種以上を含有してなること、前記カルシウムフェロアルミネート化合物とポゾラン物質等との配合割合が、質量比で10/1~1/10であることが好ましい。また、セメントと、前記セメント混和材を含有するセメント組成物である。