(EN) Disclosed is a method for obtaining magnesium oxide powder which has excellent dispersion properties, a small average particle diameter, a uniform particle diameter and which does not include micro-size particles. The particles of the magnesium oxide powder have: a BET specific surface area of 5m2/g or higher; a 50% cumulative particle diameter (D50) of 0.3-1.5μm, as determined by laser diffraction scattering particle size distribution measurement; a D90/D10 ratio of 5 or less, where D10 is the 10% cumulative particle diameter and D90 is the 90% cumulative particle diameter as determined by laser diffraction scattering particle size distribution measurement; and D10 is 0.1μm or higher.
(FR) La présente invention a pour objet un procédé d'obtention d'une poudre d'oxyde de magnésium qui possède d'excellentes propriétés de dispersion, un petit diamètre moyen des particules, un diamètre des particules uniforme, et qui ne comprend pas de particules microscopiques. Les particules de la poudre d'oxyde de magnésium ont : une surface spécifique BET de 5 m2/g ou plus; un diamètre particulaire cumulé à 50 % (D50) de 0,3 à 1,5 μm, tel que déterminé par la mesure de la distribution de la taille des particules par diffraction et diffusion laser; un rapport D90/D10 de 5 ou moins, D10 étant le diamètre particulaire cumulé à 10 % et D90 étant le diamètre particulaire cumulé à 90 % tels que déterminés par la mesure de la distribution de la taille des particules par diffraction et diffusion laser; et D10 est égal à 0,1 μm ou plus.
(JA) 分散性に優れ、平均粒子径が小さく、粒子径が均一で、微小サイズの粒子を含まない酸化マグネシウム粉末を得る。 ＢＥＴ比表面積が５ｍ２／ｇ以上、レーザ回折散乱式粒度分布測定による累積５０％粒子径（Ｄ５０）が０．３～１．５μｍ、レーザ回折散乱式粒度分布測定による累積１０％粒子径（Ｄ１０）と累積９０％粒子径（Ｄ９０）との比Ｄ９０／Ｄ１０が５以下、及びＤ１０が０．１μｍ以上の粒子である、酸化マグネシウム粉末である。