1. (WO2008060330) COMPOSITION DE REVÊTEMENT ULTRA EFFICACE UTILISANT UN SYSTÈME D'ISOCYANATE MÉLANGÉ CHIMIQUEMENT
Note: Texte fondé sur des processus automatiques de reconnaissance optique de caractères. Seule la version PDF a une valeur juridique
CLAIMS

1. An ultraproductive coating composition comprising a film forming crosslinkable component and a crosslinking component wherein said crosslinking component comprises
(a) 5-95% by weight based upon the total weight of the
crosslinking component of a polyisocyanate adduct mixture
and
(b) 95-5% by weight based upon the total weight of the
crosslinking component of at least one other crosslinking
component selected from the group diisocyanates and/or
polyisocyanates,
wherein said film forming crosslinkable component comprises a polymer, oligomer, or a dispersed gelled polymeric material that has functional groups that are crosslinkable with isocyanate groups of said crosslinking component and the gloss retention after tape of said coating is at least 80%.

2. The composition according to claim I wherein said polyisocyanate adduct mixture comprises at least one aliphatic polyisocyanate trimer and at least one cycloaliphatic polyisocyanate trimer.

3. The composition of claim 2, wherein said non-cycloaliphatic polyisocyanate trimer is derived from hexamethylene diisocyanate and said cycloaliphatic polyisocyanate trimer is derived from isophorone diisocyanate.

4. The composition of claim 2, wherein said non-cycloaliphatic polyisocyanate trimer is derived from hexamethylene diisocyanate.

5. The composition of claim 2, wherein said cycloaliphatic
polyisocyanate trimer is derived from isophorone diisocyanate.

6. The coating composition of claim 1 wherein said other crosslinking component (b) is a polyisocyanate derived from 1 ,6-hexamethyIene diisocyanate.

7. The coating composition of claim 1 , wherein the dry to tape time at ambient temperature after the composition is applied to a suitable substrate is less than or equal to 1 hour (minutes?).

8. The coating composition of claim 1 used as a primer.

9. The coating composition of claim 1 used as a basecoat in a basecoat/clearcoat paint system.

10. The coating composition of claim 1 used as a clearcoat in a basecoat/clearcoat paint system.

1 1. The coating composition of claim 1 used as a single-stage basecoat finish.

12. The coating composition of claim 2 wherein the weight ratio of non- cycloaliphatic polyisocyanate trimer to cycloaliphatic polyisocyanate trimer is 1 :4.

13. The coating composition of claim 1 wherein said composition contains 10-20% of component (a) and 80-90% of component (b).

14. A substrate coated with a dried, cured layer of the coating
composition of claim 1.

15. A substrate coated with at least one dried, cured layer of the coating composition of claim 1.

16. An aviation substrate coated with at least one layer of a dried cured layer of the coating composition of claim 1 .

17. A process for producing a coating on the surface of a substrate wherein the process comprises the steps of
a) applying a layer of pigmented basecoat on the surface of
said substrate,
b) applying a layer of a clearcoat on said pigmented basecoat; and
c) drying and curing the basecoat and clearcoat layers wherein, the pigmented basecoat comprises a film-forming crosslinkable component, a crosslinking component, and at least one pigment, wherein said crosslinking component comprises (i) 5% to 95% by weight based upon the total weight of the crosslinking component of a polyisocyanate adduct mixture and (ii) 95% to 5% by weight based upon the total weight of the crosslinking component of at least one other crosslinking component selected from the group diisocyanates or polyisocyanates, wherein said dried and cured layer has a gloss retention after tape of at least 80%.