1. (WO2002012580) FEUILLES D'ACIER LAMINEES A FROID ET A CHAUD PRESENTANT UNE EXCELLENTE TREMPABILITE ET UNE EXCELLENTE RESISTANCE AU VIEILLISSEMENT A LA TEMPERATURE ORDINAIRE ET PROCEDE DE FABRICATION ASSOCIE
Dernières données bibliographiques dont dispose le Bureau international   

N° de publication :    WO/2002/012580    N° de la demande internationale :    PCT/JP2001/006635
Date de publication : 14.02.2002 Date de dépôt international : 01.08.2001
CIB :
C21D 8/02 (2006.01), C21D 9/46 (2006.01), C22C 38/00 (2006.01), C22C 38/02 (2006.01), C22C 38/04 (2006.01), C22C 38/12 (2006.01), C22C 38/18 (2006.01), C22C 38/22 (2006.01), C22C 38/24 (2006.01), C22C 38/38 (2006.01), C23C 2/02 (2006.01), C23C 2/40 (2006.01)
Déposants : NIPPON STEEL CORPORATION [JP/JP]; 6-3, Otemachi 2-chome Chiyoda-ku, Tokyo 100-8071 (JP) (Tous Sauf US).
YOSHINAGA, Naoki [JP/JP]; (JP) (US Seulement).
TAKAHASHI, Manabu [JP/JP]; (JP) (US Seulement).
SUGIURA, Natsuko [JP/JP]; (JP) (US Seulement).
MIYASAKA, Akihiro [JP/JP]; (JP) (US Seulement).
SUGIYAMA, Masaaki [JP/JP]; (JP) (US Seulement)
Inventeurs : YOSHINAGA, Naoki; (JP).
TAKAHASHI, Manabu; (JP).
SUGIURA, Natsuko; (JP).
MIYASAKA, Akihiro; (JP).
SUGIYAMA, Masaaki; (JP)
Mandataire : ISHIDA, Takashi; A. AOKI, ISHIDA & ASSOCIATES Toranomon 37 Mori Bldg., 5-1, Toranomon 3-chome Minato-ku, Tokyo 105-8423 (JP)
Données relatives à la priorité :
2000-237510 04.08.2000 JP
Titre (EN) COLD ROLLED STEEL SHEET AND HOT ROLLED STEEL SHEET EXCELLENT IN BAKE HARDENABILITY AND RESISTANCE TO ORDINARY TEMPERATURE AGING AND METHOD FOR THEIR PRODUCTION
(FR) FEUILLES D'ACIER LAMINEES A FROID ET A CHAUD PRESENTANT UNE EXCELLENTE TREMPABILITE ET UNE EXCELLENTE RESISTANCE AU VIEILLISSEMENT A LA TEMPERATURE ORDINAIRE ET PROCEDE DE FABRICATION ASSOCIE
Abrégé : front page image
(EN)A steel sheet which has a chemical composition, in mass %: C: 0.0001 to 20 %, Si: 2.0 % or less, Mn: 3.0 % or less, P: 0.15 % or less, S: 0.015 % or less, Al: 0.10 % or less, N: 0.001 to 0.10 %, Cr: 2.5 % or less, Mo: 1.0 % or less, V: 0.1 % or less and balance: Fe and inevitable impurities, provided that it contains Al and N so as to satisfy the formula 0.52Al/N < 5 and that it contains one or more of Cr, Mo and V so as to satisfy the above contents and also satisfy the formula (Cr + 3.5Mo + 39 V) $m(G) 0.1, and which exhibits BH170 of 45 Mpa or more wherein a steel sheet having been heat-treated at 170 ° for 20 minutes after tensile deformation of 2 % is evaluated, and both of BH160 and BH150 of 35 Mpa or more wherein evaluation is carried out for steel sheets having been heat-treated at 160 ° and 150 °, respectively, for 10 minutes after tensile deformation of 2 %, and exhibits a yield point elongation of 0.6 % or less in a tensile test after it is heat-treated at 100 ° for 1 hour. The steel sheet has good bake hardenability and also good resistance to aging at an ordinary temperature.
(FR)L'invention concerne une feuille d'acier dont la composition chimique, en pourcentage en masse, comprend: C: entre 0,0001 et 20 %, Si: $m(F) 2.0 %, Mn: $m(F) 3,0 %, P: $m(F) 0,15 %, S: $m(F) 0,015 %, Al: $m(F) 0, 10 %, N: entre 0, 001 et 0, 10 %, Cr: $m(F) 2,5 %, Mo: $m(F) 1,0 %, V: $m(F) 0,1 % et les restes: Fe et d'inévitables impuretés, pour autant que cette composition renferme Al et N, de manière à répondre à la formule 0,52Al/N < 5, et au moins un parmi Cr, Mo et V, de manière à satisfaire aux teneurs susmentionnées, ainsi qu'à la formule (Cr + 3, 5 Mo + 39 V) $m(G) 0,1, et présente également un BH170 d'au moins 45 Mpa, une feuille d'acide ayant été traitée thermiquement à 170° pendant 20 minutes, après une évaluation de la déformation à la traction de 2 %, et aussi bien un BH160 qu'un BH150 de 35 Mpa, une évaluation étant effectuée pour des feuilles d'acier ayant été pré-traitées thermiquement, respectivement, à 160° et 150° pendant 10 minutes, après une déformation à la traction de 2 %. Cette feuille d'acier présente un allongement à la limite apparente d'élasticité d'au moins de 0,6 % dans un test à la traction, après que cette dernière à été traitée thermiquement à 100° pendant 1 heure. La feuille d'acier présente une excellente trempabilité et également une bonne résistance au vieillissement à une température ordinaire.