1. JPWO2020022481 - 高強度鋼板

Office Japon
Numéro de la demande 2019565584
Date de la demande 26.07.2019
Numéro de publication WO2020022481
Date de publication 17.03.2020
Numéro de délivrance 6677364
Date de délivrance 17.03.2020
Type de publication B1
CIB
C22C 38/00
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
C22C 38/06
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
06contenant de l'aluminium
C22C 38/58
CCHIMIE; MÉTALLURGIE
22MÉTALLURGIE; ALLIAGES FERREUX OU NON FERREUX; TRAITEMENT DES ALLIAGES OU DES MÉTAUX NON FERREUX
CALLIAGES
38Alliages ferreux, p.ex. aciers alliés
18contenant du chrome
40et du nickel
58et plus de 1,5% en poids de manganèse
C21D 9/46
CCHIMIE; MÉTALLURGIE
21MÉTALLURGIE DU FER
DMODIFICATION DE LA STRUCTURE PHYSIQUE DES MÉTAUX FERREUX; DISPOSITIFS GÉNÉRAUX POUR LE TRAITEMENT THERMIQUE DES MÉTAUX FERREUX OU NON FERREUX, OU DES ALLIAGES; PROCÉDÉS POUR RENDRE LE MÉTAL MALLÉABLE PAR DÉCARBURATION, REVENU OU AUTRES TRAITEMENTS
9Traitement thermique, p.ex. recuit, durcissement, trempe ou revenu, adapté à des objets particuliers; Fours à cet effet
46pour tôles
CPC
C21D 8/02
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
C21D 9/46
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
9Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
46for sheet metals
C22C 38/06
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
06containing aluminium
C22C 38/58
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
58with more than 1.5% by weight of manganese
Déposants 日本製鉄株式会社
Inventeurs 永野 真衣
林 宏太郎
上西 朗弘
Mandataires 棚井 澄雄
寺本 光生
勝俣 智夫
山口 洋
Données relatives à la priorité 2018141244 27.07.2018 JP
Titre
(JA) 高強度鋼板
Abrégé
(JA)

本願発明に係る焼付硬化量が大きく、均一焼付硬化性の高い高強度鋼板は、質量%で、C:0.13〜0.40%、Si:0.500〜3.000%、Mn:2.50〜5.00%、P:0.100%以下、S:0.010%以下、Al:0.001〜2.000%、N:0.010%以下を含有し、残部がFe及び不純物からなり、面積率で95%以上のマルテンサイトを含有し、残部組織が面積率で5%以下であり、厚さ方向断面におけるSi濃度の上限値C1(質量%)と下限値C2(質量%)の比C1/C2が1.25以下であり、長径が0.05μm以上1.00μm以下でアスペクト比1:3以上の析出物を30個/μm以上の個数密度で有し、引張強度が1300MPa以上の高強度鋼板である高強度鋼板が提供される。