(EN) PURPOSE: To obtain a polyethylene terephthalate scarcely containing oligomers such as cyclic trimer, hardly causing stain of molds, excellent in moldability and heat resistance and useful for bottles, etc., by esterifying terephthalic acid, etc., with ethylene glycol, etc., and polymerizing the resultant ester under specific conditions.
CONSTITUTION: Terephthalic acid (ester forming derivative) is esterified with ethylene glycol and the this resultant esterified product is heat-melted in the presence of a polycondensation catalyst to carry out liquid phase polycondensation. The resultant polycondensate is heated at a temperature not higher than a melting point under inert atmosphere to carry out solid phase polycondensation and the resultant solid phase polycondensate is brought into contact for 5min to 10hr with steam or steam-containing gas having a temperature kept to 70-150C and the polycondensation catalyst contained in the polymer is deactivated to provide the objective polymer.
COPYRIGHT: (C)1994,JPO&Japio
【構成】 テレフタル酸またはそのエステル形成性誘導
体と、エチレングリコールまたはそのエステル形成性誘
導体とをエステル化するエステル化工程と、上記エステ
ル化工程で得られたエステル化物を重縮合触媒の存在下
で加熱溶融する液相重縮合工程と、上記液相重縮合工程
で得られた重縮合反応物を不活性雰囲気下で溶融点以下
の温度に加熱する固相重縮合工程と、上記固相重縮合工
程で得られた重縮合反応物を７０℃～１５０℃の温度の
水蒸気または水蒸気含有ガスに５分間～１０時間接触さ
せる水蒸気処理工程とを含むことを特徴とするポリエチ
レンテレフタレートの製造方法。
【効果】 成形時に生成する環状三量体などのオリゴマ
ー類の量が少なく、しかも成形時にポリエチレンテレフ
タレート中に含まれる環状三量体などのオリゴマー類の
総量が少ないため、成形時に金型汚れが発生しにくい。