1. WO2022001886 - TEMPERING-FREE WEAR-RESISTANT HOT-ROLLED STRIP STEEL AND PRODUCTION METHOD THEREOF

Publication Number WO/2022/001886
Publication Date 06.01.2022
International Application No. PCT/CN2021/102485
International Filing Date 25.06.2021
IPC
C22C 38/14 2006.1
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
14containing titanium or zirconium
C22C 38/06 2006.1
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
06containing aluminium
C22C 38/04 2006.1
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
04containing manganese
C21D 8/02 2006.1
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
C21D 11/00 2006.1
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
11Process control or regulation for heat treatments
Applicants
  • 武汉钢铁有限公司 WUHAN IRON AND STEEL COMPANY LIMITED [CN]/[CN]
Inventors
  • 何亚元 HE, Yayuan
  • 徐进桥 XU, Jinqiao
  • 张扬 ZHANG, Yang
  • 张鹏武 ZHANG, Pengwu
  • 王跃 WANG, Yue
  • 尹云洋 YIN, Yunyang
  • 胡唐国 HU, Tangguo
  • 李利巍 LI, Liwei
  • 骆海贺 LUO, Haihe
  • 刘斌 LIU, Bin
Agents
  • 湖北武汉永嘉专利代理有限公司 HUBEI WUHAN YONGJIA PATENT AGENCY CO., LTD.
Priority Data
202010595525.X28.06.2020CN
Publication Language Chinese (zh)
Filing Language Chinese (ZH)
Designated States
Title
(EN) TEMPERING-FREE WEAR-RESISTANT HOT-ROLLED STRIP STEEL AND PRODUCTION METHOD THEREOF
(FR) FEUILLARD D'ACIER LAMINÉ À CHAUD RÉSISTANT À L'USURE SANS REVENU ET SON PROCÉDÉ DE PRODUCTION
(ZH) 一种免回火型耐磨热轧带钢及生产方法
Abstract
(EN) A tempering-free wear-resistant hot-rolled strip steel, comprising the following ingredients in weight percentage: C: 0.08-0.22%, Si: 0.1-0.55%, Mn: 0.8-1.5%, P≤0.012%, S≤0.005%, Als: 0.01-0.055%, Ti: 0.005-0.019%, and N≤0.007%; the production method comprises: smelting desulphurised molten iron and casting into blanks; heating the cast blanks; rough rolling; finishing rolling; fast cooling; coiling; and conventional levelling. The present invention, whilst ensuring that the tensile strength of the steel plate is ≥1100 MPa and the elongation is ≥12%, enables the Brinell hardness of the surface of the steel plate to be 330-390, and the hardness of the core to reach more than 95% of the hardness of the surface, improving the hardness uniformity of the steel plate in the direction of thickness, and increasing the service life by more than 20% compared with wear-resistant steel of the same level; the alloying elements are simple and no expensive element is added, no tempering is required, and quenching is performed only online, so that the production process is short, energy consumption can be reduced by at least 15%, and the unevenness reaches no more than 4.5 mm/m.
(FR) L'invention concerne un feuillard d'acier laminé à chaud résistant à l'usure sans revenu, comprenant les ingrédients suivants en pourcentage en poids : du C : entre 0,08 et 0,22 %, du Si : entre 0,1 et 0,55 %, du Mn : entre 0,8 et 1,5 %, du P ≤ 0,012 %, du S ≤ 0,005 %, du Als : entre 0,01 et 0,055 %, du Ti : entre 0,005 et 0,019 %, et du N ≤ 0,007 % ; le procédé de production consistant : à faire fondre du fer fondu désulfuré et à couler en ébauches ; à chauffer les ébauches coulées ; à effectuer un laminage grossier ; à finir le laminage ; à effectuer un refroidissement rapide ; à bobiner ; et à effectuer une mise à niveau classique. La présente invention, tout en garantissant que la résistance à la traction de la plaque d'acier est ≥ 1 100 MPa et que l'allongement est ≥ 12 %, permet à la dureté Brinell de la surface de la plaque d'acier d'être comprise entre 330 et 390, et à la dureté du noyau d'atteindre plus de 95 % de la dureté de la surface, améliorant l'uniformité de dureté de la plaque d'acier dans le sens de l'épaisseur et augmentant la durée de vie de plus de 20 % par rapport à l'acier résistant à l'usure du même niveau ; les éléments d'alliage sont simples et aucun élément onéreux n'est ajouté, aucune trempe n'est nécessaire et la trempe n'est effectuée qu'en ligne de telle sorte que le processus de production soit court, que la consommation d'énergie puisse être réduite d'au moins 15 % et que l'inégalité n'atteigne pas plus de 4,5 mm/m.
(ZH) 一种免回火型耐磨热轧带钢,其组分及重量百分比含量为:C:0.08~0.22%,Si:0.1~0.55%,Mn:0.8~1.5%,P≤0.012%,S≤0.005%,Als:0.01~0.055%,Ti:0.005~0.019%,N≤0.007%;生产方法:经脱硫铁水,冶炼并浇铸成坯;对铸坯加热;粗轧;精轧;快冷;卷取;常规平整。本发明在保证钢板抗拉强度≥1100MPa,延伸率≥12%的前提下,钢板表面布氏硬度在330~390,心部硬度达到表面硬度的95%以上,使钢板厚度方向硬度均匀性更好且使使用寿命较同级别耐磨钢提高20%以上;合金元素简单,无昂贵元素添加,且不需回火,仅在线进行淬火,使生产流程短,能耗可降低至少15%,不平度达到不超过4.5mm/m。