1. WO2020220499 - METHOD FOR PREPARING MAGNESIUM OXIDE LIGHT AND CALCIUM OXIDE LIGHT AND APPLICATION THEREOF IN PREPARATION OF CALCIUM-MAGNESIUM COMPOSITE EXPANDING AGENT

Publication Number WO/2020/220499
Publication Date 05.11.2020
International Application No. PCT/CN2019/099571
International Filing Date 07.08.2019
IPC
C04B 2/10 2006.01
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
2Lime, magnesia or dolomite
10Preheating, burning, calcining or cooling
CPC
C04B 2/10
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2Lime, magnesia or dolomite
10Preheating, burning calcining or cooling
C04B 2/102
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
2Lime, magnesia or dolomite
10Preheating, burning calcining or cooling
102of magnesia, e.g. dead burning
C04B 40/0046
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE
40Processes, in general, for influencing or modifying the properties of mortars, concrete or artificial stone compositions, e.g. their setting or hardening ability
0028Aspects relating to the mixing step of the mortar preparation
0039Premixtures of ingredients
0046characterised by their processing, e.g. sequence of mixing the ingredients when preparing the premixtures
Applicants
  • 镇江苏博特新材料有限公司 ZHENJIANG SOBUTE NEW MATERIAL CO., LTD. [CN]/[CN]
  • 江苏苏博特新材料股份有限公司 SOBUTE NEW MATERIALS CO.,LTD. [CN]/[CN]
Inventors
  • 刘加平 LIU, Jiaping
  • 张守治 ZHANG, Shouzhi
  • 张勇 ZHANG, Yong
  • 王育江 WANG, Yujiang
  • 王瑞 WANG, Rui
Agents
  • 南京天翼专利代理有限责任公司 NANJING TIANYI PATENT AGENT CO., LTD.
Priority Data
201910362948.430.04.2019CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) METHOD FOR PREPARING MAGNESIUM OXIDE LIGHT AND CALCIUM OXIDE LIGHT AND APPLICATION THEREOF IN PREPARATION OF CALCIUM-MAGNESIUM COMPOSITE EXPANDING AGENT
(FR) PROCÉDÉ DE PRÉPARATION DE FORME LÉGÈRE D'OXYDE DE MAGNÉSIUM ET DE FORME LÉGÈRE D'OXYDE DE CALCIUM ET APPLICATION ASSOCIÉE DANS LA PRÉPARATION D'UN AGENT EXPANSIF COMPOSITE DE CALCIUM-MAGNÉSIUM
(ZH) 一种制备轻质氧化镁和氧化钙的方法及其用于制备钙镁复合膨胀剂的应用
Abstract
(EN)
Method for preparing magnesium oxide light and calcium oxide light using dolomite and application thereof in the preparation of a calcium-magnesium composite expanding agent. Magnesium oxide and calcium oxide are effectively separated by a one-step method using a decomposition temperature difference bewteen magnesium oxide and calcium oxide during a dolomite calcination decomposition process and a difference in the weight of the decomposed material. The preparation of a calcium-magnesium composite expanding agent using magnesium oxide light and calcium oxide light resolves the problem of limitations in the origin of a magnesium expanding ingredient in the calcium-magnesium composite expanding agent, i.e., the magnesium oxide light, and the problem of quick hydration reaction rate and low effective expanding efficiency of a calcium expanding ingredient in the calcium-magnesium composite expanding agent, i.e., free calcium oxide, thereby optimizing an expanding process of directly calcinating dolomite to produce a calcium-magnesium composite expanding agent.
(FR)
L'invention concerne un procédé de préparation de la forme légère d'oxyde de magnésium et de la forme légère d'oxyde de calcium à l'aide de dolomite et une application associée dans la préparation d'un agent expansif composite de calcium-magnésium. L'oxyde de magnésium et l'oxyde de calcium sont efficacement séparés par un procédé constitué d'une seule étape au moyen d’une différence de température de décomposition entre l'oxyde de magnésium et l'oxyde de calcium pendant un processus de décomposition par calcination de dolomite et d’une différence du poids du matériau décomposé. La préparation d'un agent expansif composite de calcium-magnésium au moyen de la forme légère d'oxyde de magnésium et de la forme légère d'oxyde de calcium résout le problème de limitations dans l'apparition d'un ingrédient d'expansion au magnésium dans l'agent expansif composite de calcium-magnésium, c'est-à-dire la forme légère d'oxyde de magnésium, et le problème que constituent la rapidité de réaction d'hydratation et la faible efficacité d'expansion effective d'un ingrédient d'expansion au calcium dans l'agent expansif composite de calcium-magnésium, c'est-à-dire l’oxyde de calcium libre, ce qui permet d'optimiser un processus d'expansion consistant à calciner directement la dolomite afin de produire un agent expansif composite de calcium-magnésium.
(ZH)
一种利用白云石制备轻质氧化镁和氧化钙的方法及其用于制备钙镁复合膨胀剂的应用。利用白云石煅烧分解过程中碳酸镁和碳酸钙分解温度差异性以及分解后物料重量的差异性,一步法实现氧化镁和氧化钙有效分离。使用轻质氧化镁和氧化钙制备获得钙镁复合膨胀剂,解决了钙镁复合膨胀剂中镁质膨胀组分轻质氧化镁原料产地限制问题,及钙镁复合膨胀剂中钙质膨胀组分游离氧化钙水化反应速率太快、有效膨胀效能偏小的问题,优化了白云石直接煅烧生产钙镁复合膨胀剂的膨胀历程。