1. WO2020203470 - STEEL PLATE FOR CAN AND METHOD FOR MANUFACTURING SAME

Publication Number WO/2020/203470
Publication Date 08.10.2020
International Application No. PCT/JP2020/013035
International Filing Date 24.03.2020
IPC
C21D 9/46 2006.01
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
9Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
46for sheet metals
C22C 38/00 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/12 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
12containing tungsten, tantalum, molybdenum, vanadium or niobium
C22C 38/32 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
32with boron
Applicants
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP]/[JP]
Inventors
  • 齋藤 勇人 SAITO Hayato
  • 假屋 房亮 KARIYA Nobusuke
  • 小島 克己 KOJIMA Katsumi
Agents
  • 熊坂 晃 KUMASAKA Akira
  • 森 和弘 MORI Kazuhiro
  • 磯村 哲朗 ISOMURA Tetsuo
  • 坂井 哲也 SAKAI Tetsuya
Priority Data
2019-06516929.03.2019JP
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) STEEL PLATE FOR CAN AND METHOD FOR MANUFACTURING SAME
(FR) TÔLE D'ACIER POUR CANETTE ET SON PROCÉDÉ DE FABRICATION
(JA) 缶用鋼板およびその製造方法
Abstract
(EN)
A steel plate for a can according to the present invention which includes, in wt. %, as a component composition, 0.100% or more and less than 0.130% of C, 0.04% or less of Si, 0.10% or more and 0.60% or less of Mn, 0.020% or less of P, 0.020% or less of S, 0.01% or more and 0.10% or less of Al, 0.0005% or more and 0.0040% or less of N, 0.005% or more and 0.030% or less of Nb, and more than 0.0005% and 0.0050% or less of B, the remainder thereof being Fe and unavoidable impurities. The steel plate has a ferrite structure including 1.0% or more of pearlite as a surface fraction, has a tensile strength of 630 MPa or more and 750 MPa or less after heat treatment for 20 min at 210°C, has a yield elongation of 3.0% or less, and has an elongation of 3.0% or more and less than 10.0%.
(FR)
La présente invention concerne une tôle d'acier pour une canette comprenant, en % en poids, en tant que composition de composant, 0,100 % ou plus et moins de 0,130 % de C, 0,04 % ou moins de Si, 0,10 % ou plus et 0,60 % ou moins de Mn, 0,020 % ou moins de P, 0,020 % ou moins de S, 0,01 % ou plus et 0,10 % ou moins d'Al, 0,0005 % ou plus et 0,0040 % ou moins de N, 0,005 % ou plus et 0,030 % ou moins de Nb et plus de 0,0005 % et 0,0050 % ou moins de B, le reste étant du Fe et des impuretés inévitables. La tôle d'acier a une structure de ferrite comprenant 1,0 % ou plus de perlite comme fraction de surface, a une résistance à la traction de 630 MPa ou plus et de 750 MPa ou moins après un traitement thermique pendant 20 minutes à 210 °C, a un allongement à la limite d'élasticité de 3,0 % ou moins et a un allongement de 3,0 % ou plus et de moins de 10,0 %.
(JA)
成分組成として、質量%で、C:0.100%以上0.130%未満、Si:0.04%以下、Mn:0.10%以上0.60%以下、P:0.020%以下、S:0.020%以下、Al:0.01%以上0.10%以下、N:0.0005%以上0.0040%以下、Nb:0.005%以上0.030%以下、B:0.0005%超え0.0050%以下を含有し、残部はFe及び不可避的不純物からなり、パーライトを面積分率で1.0%以上含むフェライト組織を有し、210℃で20分の熱処理を施した後の引張強さが630MPa以上、750MPa以下、降伏伸びが3.0%以下であり、伸びが3.0%以上、10.0%未満である缶用鋼板。