1. WO2020199117 - FERRITIC STAINLESS STEEL PLATE WITH GOOD HIGH-TEMPERATURE STRENGTH AND FORMABILITY AND PREPARATION METHOD THEREFOR

Publication Number WO/2020/199117
Publication Date 08.10.2020
International Application No. PCT/CN2019/080970
International Filing Date 02.04.2019
IPC
C22C 38/00 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/02 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
02containing silicon
C22C 38/22 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
22with molybdenum or tungsten
CPC
C21D 8/02
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
C22C 38/00
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/02
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
02containing silicon
C22C 38/04
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
04containing manganese
C22C 38/22
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
22with molybdenum or tungsten
C22C 38/26
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
26with niobium or tantalum
Applicants
  • 东北大学 NORTHEASTERN UNIVERSITY [CN]/[CN]
Inventors
  • 陈礼清 CHEN, Liqing
  • 刘后龙 LIU, Houlong
  • 魏亮亮 WEI, Liangliang
  • 郑家昊 ZHENG, Jiahao
  • 马明玉 MA, Mingyu
Agents
  • 沈阳东大知识产权代理有限公司 SHENYANG DONGDA INTELLECTUAL PROPERTY AGENCY CO., LTD
Priority Data
201910247207.129.03.2019CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) FERRITIC STAINLESS STEEL PLATE WITH GOOD HIGH-TEMPERATURE STRENGTH AND FORMABILITY AND PREPARATION METHOD THEREFOR
(FR) TÔLE EN ACIER INOXYDABLE FERRITIQUE PRÉSENTANT UNE BONNE RÉSISTANCE ET UNE BONNE APTITUDE AU FORMAGE À HAUTE TEMPÉRATURE ET PROCÉDÉ DE PRÉPARATION ASSOCIÉ
(ZH) 高温强度和成形性能良好的铁素体不锈钢板及其制备方法
Abstract
(EN)
Disclosed are a ferritic stainless steel plate with a good high-temperature strength and formability, comprising the following components in percentages by mass: C≤0.01%, 0.006-0.01% of N, 0.4-0.6% of Si, 18-20% of Cr, 1.8-2.1% of Mo, 0.2-0.5% of Nb, 0.1-0.2% of Ti, 0.4-1.5% of W, 0.04-0.1% of Ce, 0.25-0.35% of Mn, S≤0.005%, P≤0.01%, and the balance being Fe. The preparation method for the ferritic stainless steel plate comprises the following steps: successively carrying out smelting, casting and forging, then successively hot rolling and cold rolling at corresponding temperatures, controlling the reduction rate and the annealing temperatures after rolling twice, and cooling to prepare the ferritic stainless steel plate with a good high-temperature strength and formability. According to the above-mentioned preparation method, the high-temperature strength of the ferritic stainless steel is improved by adding a suitable amount of W, and an optimized rolling process is provided, so that the ferritic stainless steel plate with a good high-temperature strength and formability can be produced, wherein same can be used in high-temperature working environments of parts such as hot ends of automobile exhaust manifolds.
(FR)
L'invention concerne une tôle en acier inoxydable ferritique présentant une bonne résistance et une bonne aptitude au formage à haute température, comprenant les constituants suivants, en pourcentages en masse : C ≤ 0,01%, 0,006-0,01% de N, 0,4-0,6% de Si, 18-20% de Cr, 1,8-2,1% de Mo, 0,2-0,5% de Nb, 0,1-0,2% de Ti, 0,4-1,5% de W, 0,04-0,1% de Ce, 0,25-0,35% de Mn, S ≤ 0,005%, P ≤ 0,01% et le reste étant du Fe. Le procédé de préparation de la tôle en acier inoxydable ferritique comprend les étapes suivantes, consistant à : réaliser successivement une fusion, un coulage et un forgeage, puis successivement un laminage à chaud et un laminage à froid à des températures correspondantes, réguler le taux de réduction et les températures de recuit après le double laminage et refroidir pour préparer la tôle en acier inoxydable ferritique présentant une bonne résistance et une bonne aptitude au formage à haute température. Selon le procédé de préparation mentionné ci-dessus, la résistance à haute température de l'acier inoxydable ferritique est améliorée par l'ajout d'une quantité appropriée de W et un procédé de laminage optimisé est proposé, de telle sorte que la tôle en acier inoxydable ferritique présentant une bonne résistance et une bonne aptitude au formage à haute température peut être produite, celle-ci pouvant être utilisée dans des environnements de travail à haute température de pièces telles que des extrémités chaudes de collecteurs d'échappement d'automobile.
(ZH)
一种高温强度和成形性能良好的铁素体不锈钢板,其成分按质量百分比计,包括C≤0.01%,N 0.006~0.01%,Si 0.4~0.6%,Cr 18~20%,Mo 1.8~2.1%,Nb 0.2~0.5%,Ti 0.1~0.2%,W 0.4~1.5%,Ce 0.04~0.1%,Mn 0.25~0.35%,S≤0.005%,P≤0.01%,余量为Fe。以及上述铁素体不锈钢板的制备方法,依次经过冶炼浇铸与锻造后,在相应温度下依次进行热轧和冷轧,并控制压下率及两次轧制后的退火温度,冷却制得高温强度和成形性能良好的铁素体不锈钢板。上述制备方法通过加入适量W提高铁素体不锈钢的高温强度,并提供最优化的轧制工艺,能够生产出具有良好高温强度和成形性能的铁素体不锈钢板,可用于汽车排气歧管热端等部件的高温工作环境。