1. WO2020197886 - POLYMER / ADHESIVE COMPOSITE FIBERS FOR INTER-FIBER ADHESION

Publication Number WO/2020/197886
Publication Date 01.10.2020
International Application No. PCT/US2020/023371
International Filing Date 18.03.2020
IPC
B01D 69/12 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
69Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
12Composite membranes; Ultra-thin membranes
B01D 71/06 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
71Semi-permeable membranes for separation processes or apparatus characterised by the material; Manufacturing processes specially adapted therefor
06Organic material
B01D 67/00 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
67Processes specially adapted for manufacturing semi-permeable membranes for separation processes or apparatus
Applicants
  • PARKER-HANNIFIN CORPORATION [US]/[US]
Inventors
  • LI, Lei
  • RANE, Yatinkumar N.
  • LIU, Kaiyi
  • CARR, Thomas D.
  • PASTRANA, Ryan
Agents
  • BRIDGE, Jeremy R.
Priority Data
62/823,13025.03.2019US
62/863,16718.06.2019US
Publication Language English (EN)
Filing Language English (EN)
Designated States
Title
(EN) POLYMER / ADHESIVE COMPOSITE FIBERS FOR INTER-FIBER ADHESION
(FR) FIBRES COMPOSITES POLYMÈRES/ADHÉSIVES POUR ADHÉRENCE ENTRE FIBRES
Abstract
(EN)
A method of preparing a composite nanofiber layer, which exhibits high internal bond strength by spinning a polymer (from solution) with a melting point of at least 25 deg C higher than that of the other polymer solution with low melting point polymer. The two polymer solutions can be miscible or immiscible. The unique blending of such two polymer solutions are performed just above the spinning head to obtain such composite nanofiber layer with desired final product performance. The nanofiber layer is post-treated with heat of about 100 - 180 deg C along with or without pressure of 40 - 60 psi. After such post-treatment, the low melting temperature polymer partially melts and attaches with adjacent fibers and at intersections just enough to improve the internal bond strength up to 120 psi without affecting the permeability of the porous structure yielding air permeability of at least 1.25 CFM.
(FR)
L'invention concerne un procédé de préparation d'une couche de nanofibres composites, qui présente une résistance de liaison interne élevée par filage d'un polymère (à partir d'une solution) avec un point de fusion d'au moins 25 °C supérieur à celui de l'autre solution de polymère avec un polymère à bas point de fusion. Les deux solutions de polymère peuvent être miscibles ou non miscibles. Le mélange unique de ces deux solutions de polymère est effectué juste au-dessus de la tête de filage afin d'obtenir une telle couche de nanofibres composites avec les performances finales souhaitées du produit. La couche de nanofibres est post-traitée par la chaleur d'environ 100 à 180 °C avec ou sans pression de 40 à 60 psi. Après un tel post-traitement, le polymère à basse température de fusion fond partiellement et se fixe à des fibres adjacentes et à des intersections juste assez afin d'améliorer la résistance de liaison interne jusqu'à 120 psi sans affecter la perméabilité de la structure poreuse donnant une perméabilité à l'air d'au moins 1,25 CFM.