1. WO2020196400 - ZIRCONIA MICROPARTICULATE MATERIAL, CATALYST FOR GAS TREATMENT USE, AND METHOD FOR PRODUCING SAME

Publication Number WO/2020/196400
Publication Date 01.10.2020
International Application No. PCT/JP2020/012706
International Filing Date 23.03.2020
IPC
C01G 25/02 2006.01
CCHEMISTRY; METALLURGY
01INORGANIC CHEMISTRY
GCOMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F94
25Compounds of zirconium
02Oxides
B01D 53/94 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
53Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases or aerosols
34Chemical or biological purification of waste gases
92of engine exhaust gases
94by catalytic processes
B01J 23/46 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
JCHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
23Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/113
38of noble metals
40of the platinum group metals
46Ruthenium, rhodium, osmium or iridium
Applicants
  • 国立大学法人東海国立大学機構 NATIONAL UNIVERSITY CORPORATION TOKAI NATIONAL HIGHER EDUCATION AND RESEARCH SYSTEM [JP]/[JP]
Inventors
  • 小澤 正邦 OZAWA, Masakuni
Agents
  • 特許業務法人三枝国際特許事務所 SAEGUSA & PARTNERS
Priority Data
2019-06175227.03.2019JP
2019-06175427.03.2019JP
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) ZIRCONIA MICROPARTICULATE MATERIAL, CATALYST FOR GAS TREATMENT USE, AND METHOD FOR PRODUCING SAME
(FR) MATÉRIAU MICROPARTICULAIRE DE ZIRCONE, CATALYSEUR POUR UTILISATION DE TRAITEMENT DE GAZ ET SON PROCÉDÉ DE PRODUCTION
(JA) ジルコニア微粒子材料、ガス処理用触媒及びその製造方法
Abstract
(EN)
(1) A tetragonal zirconia microparticulate material in which the ratio of the content of monoclinic crystals is 10% or less wherein the total amount of all of crystal phases is defined as 100%, the average grain diameter is 20 nm or less, and the ratio of the content of single crystals is 90% or more wherein the total amount of all of crystals is defined as 100%. By using the tetragonal zirconia microparticulate material, it is possible to provide: tetragonal unstabilized zirconia nanoparticles each having the form of a single crystal; a simple method for producing the tetragonal unstabilized zirconia nanoparticles; and a use of the tetragonal unstabilized zirconia nanoparticles as a catalyst material. (2) A monoclinic zirconia microparticulate material in which the ratio of the content of tetragonal crystals is 20% or less and the ratio of the content of grains each having a grain diameter of 5 to 30 nm is 60% or more wherein the total amount of all of crystal phases is defined as 100%. By using the monoclinic zirconia microparticulate material, it is possible to provide: zirconia microparticles each of which can be used as a single nanoparticulate crystal and has a complicated form or a nanosheet-like form; a simple method for producing the zirconia microparticles; and a use of the zirconia microparticles as a catalyst material.
(FR)
(1) Un matériau microparticulaire de zircone tétragonal dans lequel le rapport de la teneur en cristaux monocliniques est de 10 % ou moins, la quantité totale de toutes les phases cristallines étant définie comme étant de 100 %, le diamètre moyen des grains est inférieur ou égal à 20 nm, et le rapport de la teneur en monocristaux est de 90 % ou plus, la quantité totale de tous les cristaux étant définie comme étant de 100 %. En utilisant le matériau microparticulaire de zircone tétragonal, il est possible de fournir : des nanoparticules de zircone non stabilisées tétragonales ayant chacune la forme d'un monocristal ; un procédé simple de production des nanoparticules de zircone non stabilisées tétragonales ; et une utilisation des nanoparticules de zircone non stabilisées tétragonales en tant que matériau catalyseur. (2) Un matériau microparticulaire de zircone monoclinique dans lequel le rapport de la teneur en cristaux tétragonaux est de 20 % ou moins et le rapport de la teneur en grains ayant chacun un diamètre de grain de 5 à 30 nm est de 60 % ou plus, la quantité totale de toutes les phases cristallines étant définie comme étant de 100 %. En utilisant le matériau microparticulaire de zircone monoclinique, il est possible de fournir : des microparticules de zircone dont chacune peut être utilisée en tant que cristal nanoparticulaire unique et présente une forme compliquée ou une forme de type nanofeuille ; un procédé simple de production des microparticules de zircone ; et une utilisation des microparticules de zircone en tant que matériau catalyseur.
(JA)
(1)正方晶ジルコニア微粒子材料であって、全結晶相を100%として含有する単斜晶の割合が10%以下であり、平均粒子径が20nm以下であり、且つ、全結晶を100%として含有する単結晶の割合が90%以上である、正方晶ジルコニア微粒子材料。当該正方晶ジルコニア微粒子材料により、単結晶状の正方晶の無添加ジルコニアナノ粒子、簡便な製造方法及びその触媒材としての利用法を提供できる。(2)単斜晶ジルコニア微粒子材料であって、全結晶相を100%として含有する正方晶の割合が20%以下であり、粒径が5~30nmの粒子の割合が60%以上である、単斜晶ジルコニア微粒子材料。当該単斜晶ジルコニア微粒子材料により、単独のナノ粒子の結晶として複雑形状あるいはナノシート状のジルコニア微粒子、及びその簡便な製造方法、その触媒材としての利用法を提供できる。