1. WO2020194484 - FERRITIC STAINLESS STEEL SHEET AND METHOD FOR PRODUCING SAME

Publication Number WO/2020/194484
Publication Date 01.10.2020
International Application No. PCT/JP2019/012676
International Filing Date 26.03.2019
IPC
C22C 38/00 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C21D 9/46 2006.01
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
9Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
46for sheet metals
C22C 38/50 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
50with titanium or zirconium
C22C 38/52 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
52with cobalt
C22C 38/60 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
60containing lead, selenium, tellurium or antimony, or more than 0.04% by weight of sulfur
Applicants
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP]/[JP]
Inventors
  • 西田 修司 NISHIDA Shuji
  • 吉野 正崇 YOSHINO Masataka
  • 高 法剛 GAO FAGANG
  • 山口 広史 YAMAGUCHI Hiroshi
Agents
  • 熊坂 晃 KUMASAKA Akira
  • 森 和弘 MORI Kazuhiro
  • 磯村 哲朗 ISOMURA Tetsuo
  • 坂井 哲也 SAKAI Tetsuya
Priority Data
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) FERRITIC STAINLESS STEEL SHEET AND METHOD FOR PRODUCING SAME
(FR) TÔLE D'ACIER INOXYDABLE FERRITIQUE ET PROCÉDÉ DE PRODUCTION D’UNE TELLE TÔLE
(JA) フェライト系ステンレス鋼板およびその製造方法
Abstract
(EN)
Provided is a ferritic stainless steel sheet which does not require a dehydrogenation treatment for the production thereof and has excellent corrosion resistance and hydrogen embrittlement resistance properties in spite of the fact that Ni, Cu and Mn are not contained in larger amounts. The ferritic stainless steel sheet has a component composition comprising, in % by mass, 0.001 to 0.020% of C, 0.10 to 0.60% of Si, 0.10 to 0.60% of Mn, 0.040% or less of P, 0.030% or less of S, 0.030 to 0.060% of Al, 16.5 to 19.0% of Cr, 0.15 to 0.35% of Ti, 0.30 to 0.60% of Nb, 0.01 to 0.60% of Ni, 0.0025 to 0.0050% of O (oxygen), 0.001 to 0.020% of N and a remainder made up by Fe and unavoidable impurities, and is so configured that the number of precipitates each having a cross-sectional area of 5.0 μm2 or more in a 1-mm2 zone is 300 or less and the average cross-sectional area of precipitates each having a cross-sectional area of 5.0 μm2 or more is 20.0 μm2 or less.
(FR)
L'invention concerne une tôle d'acier inoxydable ferritique qui ne nécessite pas de traitement de déshydrogénation lors de sa production et qui présente d'excellentes propriétés de résistance à la corrosion et de résistance à la fragilisation par l'hydrogène malgré le fait que Ni, Cu et Mn ne sont pas présents en de plus grandes quantités. La tôle d'acier inoxydable ferritique a une composition de constituants comprenant, en % en masse, de 0,001 à 0,020 % de C, de 0,10 à 0,60 % de Si, de 0,10 à 0,60 % de Mn, 0,040 % ou moins de P, 0,030 % ou moins de S, de 0,030 à 0,060 % d'Al, de 16,5 à 19,0 % de Cr, de 0,15 à 0,35 % de Ti, de 0,30 à 0,60 % de Nb, de 0,01 à 0,60 % de Ni, de 0,0025 à 0,0050 % d'O (oxygène), de 0,001 à 0,020 % de N et le reste étant constitué de Fe et d'impuretés inévitables, et est conçue de sorte que le nombre de précipités ayant chacun une section transversale supérieure ou égale à 5,0 μm μm2 dans une zone de 1-mm2 est inférieur ou égal à 300 et que la section transversale moyenne des précipités ayant chacun une section transversale supérieure ou égale à 5,0 μm2 est inférieure ou égale à 20,0 μm2.
(JA)
製造時に脱水素処理を必要とせずに、更にはNi、Cu、Mnを多量に含有させずに、耐食性および耐水素脆化特性に優れるフェライト系ステンレス鋼板を提供すること。 質量%で、C:0.001~0.020%、Si:0.10~0.60%、Mn:0.10~0.60%、P:0.040%以下、S:0.030%以下、Al:0.030~0.060%、Cr:16.5~19.0%、Ti:0.15~0.35%、Nb:0.30~0.60%、Ni:0.01~0.60%、O(酸素):0.0025~0.0050%、およびN:0.001~0.020%を含有し、残部がFeおよび不可避的不純物からなる成分組成を有し、5.0μm以上の断面積を有する析出物が1mm区画内において300個以下であり、かつ、5.0μm以上の断面積を有する析出物の平均断面積が20.0μm以下であるようにする。