1. WO2020116588 - METHOD FOR MANUFACTURING FERRITIC HEAT RESISTANT STEEL WELDED JOINT

Publication Number WO/2020/116588
Publication Date 11.06.2020
International Application No. PCT/JP2019/047717
International Filing Date 05.12.2019
IPC
B23K 9/23 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
23MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
KSOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
9Arc welding or cutting
23taking account of the properties of the materials to be welded
B23K 35/30 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
23MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
KSOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
35Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
22characterised by the composition or nature of the material
24Selection of soldering or welding materials proper
30with the principal constituent melting at less than 1550°C
C22C 19/05 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
19Alloys based on nickel or cobalt
03based on nickel
05with chromium
C22C 38/00 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/54 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
54with boron
Applicants
  • 日本製鉄株式会社 NIPPON STEEL CORPORATION [JP]/[JP]
Inventors
  • 平田 弘征 HIRATA, Hiroyuki
  • 浄▲徳▼ 佳奈 JOTOKU, Kana
  • 栗原 伸之佑 KURIHARA, Shinnosuke
  • 田中 克樹 TANAKA, Katsuki
Agents
  • 特許業務法人太陽国際特許事務所 TAIYO, NAKAJIMA & KATO
Priority Data
2018-22831405.12.2018JP
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) METHOD FOR MANUFACTURING FERRITIC HEAT RESISTANT STEEL WELDED JOINT
(FR) PROCÉDÉ DE FABRICATION D'UN JOINT SOUDÉ EN ACIER FERRITIQUE RÉSISTANT À LA CHALEUR
(JA) フェライト系耐熱鋼溶接継手の製造方法
Abstract
(EN)
This method for manufacturing a ferritic heat resistant steel welded joint includes a multilayer welding step of using a welding material for an Ni-based heat resistant alloy to perform multilayer welding of a ferritic heat resistant steel base material containing between 0.006 % by mass and 0.023 % by mass of B, wherein first layer welding is performed under welding conditions in which, in a cross section through a welded portion after welding of a first layer and before welding of a second layer in the multilayer welding step, a ratio between a surface area [SBM] of the melted ferritic heat resistant steel base material and a surface area [SWM] of the welded metal satisfy formula (1), with respect to the % by mass of B [%BBM] contained in the ferritic heat resistant steel base material. (1) 0.1 ≤ [SBM]/[SWM]≤-50×[%BBM]+1.3
(FR)
L'invention concerne un procédé de fabrication d'un joint soudé en acier ferritique résistant à la chaleur, comprenant une étape de soudage multicouche qui consiste à utiliser un matériau de soudage pour un alliage résistant à la chaleur à base de Ni pour réaliser un soudage multicouche d'un matériau de base en acier ferritique résistant à la chaleur contenant entre 0,006 % massique et 0,023 % massique de B. Le soudage de la première couche est effectué dans des conditions de soudage dans lesquelles, dans une section transversale à travers une portion soudée après le soudage d'une première couche et avant le soudage d'une deuxième couche dans l'étape de soudage multicouche, un rapport entre une aire [SBM] du matériau de base en acier ferritique résistant à la chaleur fondu et une aire [SWM] du métal soudé satisfait à la formule (1), en ce qui concerne le % massique de B [%BBM] contenu dans le matériau de base en acier ferritique résistant à la chaleur. (1) 0,1 ≤ [SBM]/[SWM]≤-50×[%BBM]+1,3
(JA)
Bを0.006質量%~0.023質量%含むフェライト系耐熱鋼母材をNi基耐熱合金用溶接材料で多層溶接する多層溶接工程を有し、前記多層溶接工程での初層溶接後かつ第二層溶接前の溶接部の横断面における、溶融した前記フェライト系耐熱鋼母材の面積[SBM]と溶接金属の面積[SWM]との比が、前記フェライト系耐熱鋼母材に含有されるBの質量%[%BBM]に対して下記(1)式を満たす溶接条件で初層溶接を行うフェライト系耐熱鋼溶接継手の製造方法。 0.1≦[SBM]/[SWM]≦-50×[%BBM]+1.3・・・(1)
Latest bibliographic data on file with the International Bureau