1. WO2020107135 - VACUUM ZINC INFILTRATION METHOD FOR METAL SURFACE TREATMENT AND PREPARATION METHOD

Publication Number WO/2020/107135
Publication Date 04.06.2020
International Application No. PCT/CN2018/112994
International Filing Date 27.11.2018
IPC
C23C 10/36 2006.01
CCHEMISTRY; METALLURGY
23COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
CCOATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
10Solid state diffusion of only metal elements or silicon into metallic material surfaces
28using solids, e.g. powders, pastes
34Embedding in a powder mixture, i.e. pack cementation
36only one element being diffused
CPC
C23C 10/36
CCHEMISTRY; METALLURGY
23COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
CCOATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
10Solid state diffusion of only metal elements or silicon into metallic material surfaces
28using solids, e.g. powders, pastes
34Embedding in a powder mixture, i.e. pack cementation
36only one element being diffused
Applicants
  • 李屹晨 LI, Yichen [CN]/[CN]
Inventors
  • 李屹晨 LI, Yichen
Agents
  • 石家庄领皓专利代理有限公司 SHIJIAZHUANG LINGHAO PATENT COMMISSIONING CO., LTD
Priority Data
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) VACUUM ZINC INFILTRATION METHOD FOR METAL SURFACE TREATMENT AND PREPARATION METHOD
(FR) PROCÉDÉ D'INFILTRATION DE ZINC SOUS VIDE POUR TRAITEMENT DE SURFACE MÉTALLIQUE ET PROCÉDÉ DE PRÉPARATION
(ZH) 一种金属表面处理的真空渗锌方法及其制备方法
Abstract
(EN)
A vacuum zinc infiltration method for metal surface treatment, comprising the following steps: performing oil removal, rust removal, water washing, and drying treatment on the surface of a steel product to be treated, placing the steel product together with an infiltration agent, a filler, and an adjuvant into a vacuum zinc infiltration furnace, performing sealing and vacuumizing to 10-9.65 kPa, then heating to 70-85°Ϲ, and maintaining a constant temperature for 10-15 min; and then vacuumizing to 1.05-0.56 Pa and heating to 400-450°Ϲ, maintaining a constant temperature for 150-170 min, cooling to below 100°Ϲ, discharging the steel product from the furnace, placing the discharged steel product into a water washing pool for washing, and drying the washed steel product. The zinc infiltration agent consists of the following components in proportion by mass: 80-95 of zinc powder, 2-6 of aluminum powder, 0.8-1.7 of gold powder, and 0.4-0.8 of nickel powder; the filler consists of the following component in proportion by mass: 50-60 of quartz sand, having a particle size of 40-80 meshes. By means of the technical solution above, the problem that a metal component treated with a metal surface treatment method in the prior art cannot satisfy the requirement of a user for the degree of corrosion resistance is solved.
(FR)
L'invention concerne un procédé d'infiltration de zinc sous vide pour un traitement de surface métallique, comprenant les étapes suivantes consistant à : réaliser une élimination d'huile, une élimination de rouille, un lavage à l'eau et un traitement de séchage sur la surface d'un produit en acier à traiter, placer le produit en acier conjointement avec un agent d'infiltration, une charge et un adjuvant dans un four d'infiltration de zinc sous vide, réaliser une mise en étanchéité et une mise sous vide de 10 à 9,65 kPa, puis chauffer à 70-85°C, et maintenir une température constante pendant 10 à 15 min ; puis mettre sous vide jusqu'à 1,05-0,56 Pa et chauffer à 400-450 °C, maintenir une température constante pendant 150-170 min, refroidir jusqu'à une température inférieure à 100 °C, évacuer le produit en acier du four, placer le produit en acier évacué dans un bain de lavage à l'eau pour laver, et sécher le produit en acier lavé. L'agent d'infiltration de zinc comprend les composants suivants en parties en masse : 80-95 de poudre de zinc, 2-6 de poudre d'aluminium, 0,8-1,7 de poudre d'or et 0,4-0,8 de poudre de nickel ; la charge est constituée du composant suivant en proportion en masse : 50-60 de sable de quartz, ayant une taille de particule de 40-80 mesh. La solution technique ci-dessus permet de résoudre le problème selon lequel un composant métallique traité avec un procédé de traitement de surface métallique dans l'état de la technique ne peut pas répondre à l'exigence d'un utilisateur en matière de degré de résistance à la corrosion.
(ZH)
一种金属表面处理的真空渗锌方法,包括以下步骤:对待处理的钢铁制件表面进行除油、除锈、水洗和干燥处理,将所述钢铁制件与渗剂、填充剂、助剂放入真空渗锌炉内,密封抽真空至10-9.65 kPa,然后加热至70-85℃,恒温10-15 min;接着抽真空至1.05-0.56 Pa并加热至400-450℃,恒温150-170 min,冷却至100℃以下出炉,将出炉后的钢铁制件放入水洗池内进行冲洗,将冲洗后的钢铁制件进行烘干。所述渗锌剂由以下质量配比的组分组成:锌粉80-95,铝粉2-6,金粉0.8-1.7,镍粉0.4-0.8,所述填充剂由以下质量配比的组分组成:石英砂50-60,粒度40-80目。通过上述技术方案,解决了现有技术中金属表面处理方法处理的金属构件不能满足用户耐腐蚀程度的要求。