1. WO2020071219 - SEAMLESS STEEL PIPE SUITABLE FOR USE IN SOUR ENVIRONMENT

Publication Number WO/2020/071219
Publication Date 09.04.2020
International Application No. PCT/JP2019/037758
International Filing Date 26.09.2019
IPC
C22C 38/00 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/54 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
54with boron
C21D 8/10 2006.01
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
10during manufacturing of tubular bodies
CPC
C21D 8/10
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
10during manufacturing of tubular bodies
C22C 38/00
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C22C 38/54
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
18containing chromium
40with nickel
54with boron
Applicants
  • 日本製鉄株式会社 NIPPON STEEL CORPORATION [JP]/[JP]
Inventors
  • 神谷 裕紀 KAMITANI, Hiroki
  • 小松原 伸明 KOMATSUBARA, Nobuaki
  • 岡田 誠也 OKADA, Seiya
  • 相馬 貴志 SOMA, Atsushi
  • 荒井 勇次 ARAI, Yuji
  • 吉田 晋士 YOSHIDA, Shinji
Agents
  • アセンド特許業務法人 ASCEND IP LAW FIRM
Priority Data
2018-18700601.10.2018JP
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) SEAMLESS STEEL PIPE SUITABLE FOR USE IN SOUR ENVIRONMENT
(FR) TUYAU D'ACIER SANS SOUDURE APPROPRIÉ POUR UNE UTILISATION DANS UN ENVIRONNEMENT ACIDE
(JA) サワー環境での使用に適した継目無鋼管
Abstract
(EN)
Provided is a seamless steel pipe that has a yield strength of 758 to 862 MPa (110 ksi grade) and has excellent HIC resistance. This seamless steel pipe consists of, in mass%, 0.15 to 0.45% of C, 0.05 to 1.00% of Si, 0.01 to 1.00 of Mn, 0.030% or less of P, 0.0050% or less of S, 0.005 to 0.070% of Al, 0.30 to 1.50% of Cr, 0.25 to 2.00% of Mo, 0.002 to 0.020% of Ti, 0.002 to 0.100% of Nb, 0.0005 to 0.0040% of B, 0.0001 to 0.0015% of a rare earth element, 0.0001 to 0.0100% of Ca, 0.0100% or less of N, and 0.0020% or less of O, the balance being Fe and impurities, and has a chemical composition that satisfies formula (1) indicated in the specification. The maximum major axis length of an inclusion estimated by extreme value statistical processing is 150 μm or less. The yield strength is 758 to 862 MPa.
(FR)
L'invention concerne un tuyau d'acier sans soudure qui présente une limite d'élasticité de 758 à 862 MPa (grade 110 ksi) et qui possède une excellente résistance HIC. Ce tuyau d'acier sans soudure est constitué, en % en masse, de 0,15 à 0,45 % de C, de 0,05 à 1,00 % de Si, de 0,01 à 1,00 % de Mn, d'une quantité inférieure ou égale à 0,030 % de P, d'une quantité inférieure ou égale à 0,0050 % de S, de 0,005 à 0,070 % d'Al, de 0,30 à 1,50 % de Cr, de 0,25 à 2,00 % de Mo, de 0,002 à 0,020 % de Ti, de 0,002 à 0,100 % de Nb, de 0,0005 à 0,0040 % de B, de 0,0001 à 0,0015 % d'un élément de terre rare, de 0,0001 à 0,0100 % de Ca, d'une quantité inférieure ou égale à 0,0100 % de N, et d'une quantité inférieure ou égale à 0,0020 % de O, le complément étant constitué de Fe et d'impuretés, et a une composition chimique qui satisfait à la formule (1) indiquée dans la description. La longueur maximale de l'axe principal d'une inclusion estimée à l'aide d'un traitement statistique de valeurs extrêmes est inférieure ou égale à 150 µm. La limite d'élasticité est de 758 à 862 MPa.
(JA)
758~862MPa(110ksi級)の降伏強度と、優れた耐HIC性とを有する継目無鋼管を提供する。本開示による継目無鋼管は、質量%で、C:0.15~0.45%、Si:0.05~1.00%、Mn:0.01~1.00%、P:0.030%以下、S:0.0050%以下、Al:0.005~0.070%、Cr:0.30~1.50%、Mo:0.25~2.00%、Ti:0.002~0.020%、Nb:0.002~0.100%、B:0.0005~0.0040%、希土類元素:0.0001~0.0015%、Ca:0.0001~0.0100%、N:0.0100%以下、及び、O:0.0020%以下を含有し、残部がFe及び不純物からなり、明細書に記載の式(1)を満たす化学組成を有する。極値統計処理による介在物の予測最大長径が150μm以下である。降伏強度が758~862MPaである。