1. WO2020066815 - COPOLYMERIZED POLYPHENYLENE SULFIDE FIBERS

Publication Number WO/2020/066815
Publication Date 02.04.2020
International Application No. PCT/JP2019/036674
International Filing Date 19.09.2019
IPC
D01F 6/76 2006.01
DTEXTILES; PAPER
01NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
FCHEMICAL FEATURES IN THE MANUFACTURE OF MAN-MADE FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
6Monocomponent man-made filaments or the like of synthetic polymers; Manufacture thereof
58from homopolycondensation products
76from other polycondensation products
CPC
D01F 6/76
DTEXTILES; PAPER
01NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
FCHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
6Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
58from homopolycondensation products
76from other polycondensation products
Applicants
  • 東レ株式会社 TORAY INDUSTRIES, INC. [JP]/[JP]
Inventors
  • 土屋匠平 TSUCHIYA, Shohei
  • 勝田大士 KATSUTA, Hiroo
  • 船津義嗣 FUNATSU, Yoshitsugu
Priority Data
2018-18252727.09.2018JP
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) COPOLYMERIZED POLYPHENYLENE SULFIDE FIBERS
(FR) FIBRE DE SULFURE DE POLYPHÉNYLÈNE COPOLYMÉRISÉ
(JA) 共重合ポリフェニレンスルフィド繊維
Abstract
(EN)
In order to provide copolymerized polyphenylene sulfide fibers that have a low thermal shrinkage and fine size, exhibits excellent fusibility, and is suitable for use as a paper making binder, the copolymerized polyphenylene sulfide fibers are formed so as to be characterized by: comprising a copolymerized polyphenylene sulfide which includes a p-phenylene sulfide unit as the main component, and includes, in repeating units, 3-40 mol% of a m-phenylene sulfide unit; and having a crystallinity degree of 10.0-30.0%, an average fiber diameter of 5-25 μm, and a hot water shrinkage factor of at most 25.0% at 98°C.
(FR)
Dans le cadre de la présente invention, afin de fournir des fibres de sulfure de polyphénylène copolymérisé qui aient un faible retrait thermique et une petite taille, présentent une excellente fusibilité, et soient appropriées pour une utilisation en tant que liant de fabrication de papier, les fibres de sulfure de polyphénylène copolymérisé sont formées de manière à être caractérisées en ce qu'elles : comprennent un sulfure de polyphénylène copolymérisé qui comprend une unité de sulfure de p-phénylène en tant que composant principal, et comprend, en unités de répétition, de 3 à 40 % en moles d'une unité de sulfure de m-phénylène ; et ont un degré de cristallinité de 10,0 à 30,0 %, un diamètre moyen de fibre de 5 à 25 µm, et un facteur de retrait en eau chaude maximum de 25,0 % à 98 °C.
(JA)
細繊度かつ熱収縮率が小さく、融着性に優れた抄紙バインダー用途に適した共重合ポリフェニレンスルフィド繊維を提供するために、p-フェニレンスルフィド単位を主成分とし、繰り返し単位に3モル%以上40モル%以下のm-フェニレンスルフィド単位を含む共重合ポリフェニレンスルフィドからなり、結晶化度が10.0%以上30.0%以下、平均繊維径が5μm以上25μm以下、さらに98℃における熱水収縮率が25.0%以下であることを特徴とする共重合ポリフェニレンスルフィド繊維とする。