1. WO2020001540 - MODIFIED Y TYPE MOLECULAR SIEVE, CATALYTIC CRACKING CATALYST HAVING SAME, AND PREPARATION METHOD THEREFOR AND APPLICATION THEREOF

Publication Number WO/2020/001540
Publication Date 02.01.2020
International Application No. PCT/CN2019/093279
International Filing Date 27.06.2019
IPC
B PERFORMING OPERATIONS; TRANSPORTING
01
PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
J
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS, COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
29
Catalysts comprising molecular sieves
04
having base-exchange properties, e.g. crystalline zeolites, pillared clays
06
Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
08
of the faujasite type, e.g. type X or Y
B PERFORMING OPERATIONS; TRANSPORTING
01
PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
J
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS, COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
35
Catalysts, in general, characterised by their form or physical properties
02
Solids
10
characterised by their surface properties or porosity
C CHEMISTRY; METALLURGY
10
PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
G
CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
11
Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
02
characterised by the catalyst used
04
Oxides
05
Crystalline alumino-silicates, e.g. molecular sieves
B01J 29/08 (2006.01)
B01J 35/10 (2006.01)
C10G 11/05 (2006.01)
CPC
B01J 29/08
B01J 35/10
C10G 11/05
Applicants
  • 中国石油化工股份有限公司 CHINA PETROLEUM & CHEMICAL CORPORATION [CN/CN]; 中国北京市 朝阳区朝阳门北大街22号 22 Chaoyangmen North Street, Chaoyang District Beijing 100728, CN
  • 中国石油化工股份有限公司石油化工科学研究院 RESEARCH INSTITUTE OF PETROLEUM PROCESSING, SINOPEC [CN/CN]; 中国北京市 海淀区学院路18号 18 Xueyuan Road, Haidian District Beijing 100083, CN
Inventors
  • 袁帅 YUAN, Shuai; CN
  • 周灵萍 ZHOU, Lingping; CN
  • 田辉平 TIAN, Huiping; CN
  • 沙浩 SHA, Hao; CN
  • 陈振宇 CHEN, Zhenyu; CN
  • 张蔚琳 ZHANG, Weilin; CN
Agents
  • 中国专利代理(香港)有限公司 CHINA PATENT AGENT (H.K.) LTD.; 中国香港特别行政区 湾仔港湾道23号鹰君中心22号楼 22/F, Great Eagle Centre, 23 Harbour Road, Wanchai Hong Kong, CN
Priority Data
201810714296.129.06.2018CN
201810715238.029.06.2018CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) MODIFIED Y TYPE MOLECULAR SIEVE, CATALYTIC CRACKING CATALYST HAVING SAME, AND PREPARATION METHOD THEREFOR AND APPLICATION THEREOF
(FR) TAMIS MOLÉCULAIRE DE TYPE Y MODIFIÉ, CATALYSEUR DE CRAQUAGE CATALYTIQUE LE COMPRENANT, SON PROCÉDÉ DE PRÉPARATION ET SON APPLICATION
(ZH) 改性Y型分子筛、包含它的催化裂化催化剂、及其制备和应用
Abstract
(EN)
A modified Y type molecular sieve, and a preparation method therefor and an application thereof. The calcium content of the modified Y type molecular sieve is about 0.3-4 wt% in terms of calcium oxide; the rare earth content is about 2.7 wt% in terms of rare earth oxide; the sodium content is not more than about 0.5 wt% in terms of sodium oxide; the total pore volume is about 0.33-0.39 mL/g, wherein the pore volume of secondary pores having a pore diameter of 2-100 nm occupies about 10-25% of the total pore volume; the lattice constant is about 2.440-2.455 nm; the content of non-framework aluminum occupies no higher than about 20% of the total aluminum content; the lattice collapse temperature is not less than about 1050°C; moreover, the ratio of B acid content to L acid content is no less than about 2.30 in the total acid content measured using a pyridine adsorption infrared method at the temperature of 200°C. The modified Y type molecular sieve and a catalytic cracking catalyst having same have higher heavy oil conversion activity and lower coke selectivity during heavy oil fluid catalytic cracking and can obtain a higher gasoline yield and an isomeric C4 yield, and the obtained gasoline has a higher isohydrocarbon content.
(FR)
L'invention concerne également un tamis moléculaire de type Y modifié, son procédé de préparation et son application. La teneur en calcium du tamis moléculaire de type Y modifié est d'environ 0,3 à 4% en poids en termes d'oxyde de calcium; la teneur en terres rares est d'environ 2,7% en poids en termes d'oxyde de terre rare; la teneur en sodium n'est pas supérieure à environ 0,5% en poids en termes d'oxyde de sodium; le volume poreux total est d'environ 0,33 à 0,39 mL/g, le volume poreux de pores secondaires ayant un diamètre de pore de 2 à 100 nm occupant environ 10 à 25% du volume poreux total; la constante de réseau est d'environ 2,440 à 2,455 nm; la teneur en aluminium non charpente n'occupe pas plus d'environ 20% du contenu total en aluminium; la température d'effondrement du réseau n'est pas Inférieure à environ 1050 °C; en outre, le rapport de la teneur en acide B à la teneur en acide L n'est pas inférieur à environ 2,30 dans la teneur totale en acide mesurée à l'aide d'un procédé infrarouge d'adsorption de pyridine à la température de 200 °C. Le tamis moléculaire de type Y modifié et un catalyseur de craquage catalytique les comprenant ont une activité de conversion d'huile lourde supérieure et une sélectivité de coke inférieure pendant de craquage catalytique de fluide d'huile lourde et peut obtenir un rendement d'essence supérieur et un rendement en C4 isomérique, et l'essence obtenue présente un taux d'isohydrocarbure supérieur.
(ZH)
一种改性Y型分子筛及其制备和应用,该改性Y型分子筛的钙含量以氧化钙计为约0.3-4重量%,稀土含量以氧化稀土计为约2-7重量%,钠含量以氧化钠计不超过约0.5重量%,总孔体积为约0.33-0.39mL/g,其中孔径为2-100nm的二级孔的孔体积占总孔体积的百分比为约10-25%,晶胞常数为约2.440-2.455nm,非骨架铝含量占总铝含量的百分比不高于约20%,晶格崩塌温度不低于约1050℃,并且,用吡啶吸附红外法在200℃时测定的总酸量中B酸量与L酸量的比值不低于约2.30。该改性Y型分子筛及包含它的催化裂化催化剂用于重油催化裂化时具有更高的重油转化活性和较低的焦炭选择性,能得到更高的汽油收率和异构C4收率,且所得汽油中具有更高的异构烃含量。