1. WO2020001430 - ULTRAHIGH-STRENGTH HOT-ROLLED STEEL SHEET AND STEEL STRIP HAVING GOOD FATIGUE AND REAMING PROPERTIES AND MANUFACTURING METHOD THEREFOR

Publication Number WO/2020/001430
Publication Date 02.01.2020
International Application No. PCT/CN2019/092766
International Filing Date 25.06.2019
IPC
C CHEMISTRY; METALLURGY
22
METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
C
ALLOYS
38
Ferrous alloys, e.g. steel alloys
18
containing chromium
26
with niobium or tantalum
C CHEMISTRY; METALLURGY
21
METALLURGY OF IRON
D
MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
9
Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
46
for sheet metals
C22C 38/26 (2006.01)
C21D 9/46 (2006.01)
CPC
C21D 8/02
C21D 9/46
C22C 38/02
C22C 38/06
C22C 38/22
C22C 38/24
Applicants
  • 宝山钢铁股份有限公司 BAOSHAN IRON & STEEL CO., LTD. [CN/CN]; 中国上海市 宝山区富锦路885号 No.885, Fujin Road, Baoshan District Shanghai 201900, CN
Inventors
  • 张瀚龙 ZHANG, Hanlong; CN
  • 张玉龙 ZHANG, Yulong; CN
  • 王利 WANG, Li; CN
Agents
  • 上海专利商标事务所有限公司 SHANGHAI PATENT & TRADEMARK LAW OFFICE, LLC; 中国上海市 桂平路435号 435 Guiping Road Shanghai 200233, CN
Priority Data
201810681968.327.06.2018CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) ULTRAHIGH-STRENGTH HOT-ROLLED STEEL SHEET AND STEEL STRIP HAVING GOOD FATIGUE AND REAMING PROPERTIES AND MANUFACTURING METHOD THEREFOR
(FR) TÔLE D'ACIER LAMINÉE À CHAUD À ULTRA-HAUTE RÉSISTANCE ET BANDE D'ACIER AYANT DE BONNES PROPRIÉTÉS DE FATIGUE ET D'ALÉSAGE ET PROCÉDÉ DE FABRICATION ASSOCIÉ
(ZH) 具有良好的疲劳及扩孔性能的超高强热轧钢板和钢带及其制造方法
Abstract
(EN)
An ultrahigh-strength hot-rolled steel sheet and steel strip having good fatigue and reaming properties and a manufacturing method therefor. The weight percentages of the components of the steel sheet and the steel strip are: C: 0.07-0.14%, Si: 0.1-0.4%, Mn: 1.55-2.00%, P≤0.015%, S≤0.004%, Al: 0.01-0.05%, N≤0.005%, Cr: 0.15-0.50%, V: 0.1-0.35%, Nb: 0.01%-0.06%, Mo: 0.15-0.50%, Ti≤0.02%, and the balance of Fe and unavoidable impurities. Such components need to meet: 1.0≤[(Cr/52)/(C/4)+(Nb/93+Ti/48+V/51+Mo/96)/(C/12)]≤1.6. The tensile strength of the ultrahigh-strength hot-rolled steel sheet and steel strip is ≥780MPa, the yield strength thereof is ≥660MPa, the tensile fatigue limit (10 million cycles) FL thereof is ≥570MPa, or the fatigue limit to tensile strength FL/Rm thereof is ≥0.72. The reaming rate meets: if an original hole is a punched hole, the reaming rate thereof is >85%; and if the original hole is a reamed hole, the reaming rate thereof is >120%.
(FR)
L'invention concerne une tôle d'acier laminée à chaud à ultra-haute résistance et une bande d'acier ayant de bonnes propriétés de fatigue et d'alésage et un procédé de fabrication associé. Les pourcentages en poids des composants de la tôle d'acier et de la bande d'acier sont les suivants : C : 0,07 à 0,14 %, Si : 0,1 à 0,4 %, Mn : 1,55 à 2,00 %, P ≤ 0,015 %, S ≤ 0,004 %, Al : 0,01 à 0,05 %, N ≤ 0,005 %, Cr : 0,15 à 0,50 %, V : 0,1 à 0,35 %, Nb : 0,01 % à 0,06 %, Mo : 0,15 à 0,50 %, Ti ≤ 0,02 %, et le reste étant constitué de Fe et d'impuretés inévitables. De tels composants doivent satisfaire les conditions suivantes : 1,0 ≤ [ (Cr/52)/ (C/4) + (Nb/93 + Ti/48 + V/51 + Mo/96)/ (C/12)] ≤ 1,6. La résistance à la traction de la tôle d'acier laminée à chaud à ultra-haute résistance et de la bande d'acier est ≥ 780 MPa, leur limite d'élasticité est ≥ 660 MPa, leur limite de fatigue en traction (10 millions de cycles) FL est ≥ 570 MPa, ou leur limite de fatigue à la résistance à la traction FL/Rm est ≥ 0,72. Le taux d'alésage satisfait la condition suivante : si un trou d'origine est un trou poinçonné, son taux d'alésage est > 85 % ; et si le trou d'origine est un trou alésé, son taux d'alésage est > 120 %.
(ZH)
具有良好的疲劳及扩孔性能的超高强热轧钢板和钢带及其制造方法,该钢板和钢带成分重量百分比为:C:0.07~0.14%,Si:0.1~0.4%,Mn:1.55~2.00%,P≤0.015%,S≤0.004%,Al:0.01~0.05%,N≤0.005%,Cr:0.15~0.50%,V:0.1~0.35%,Nb:0.01%~0.06%,Mo:0.15~0.50%,且Ti≤0.02%,其余为Fe和不可避免的杂质;且同时需满足: 1.0≤[(Cr/52)/(C/4)+(Nb/93+Ti/48+V/51+Mo/96)/(C/12)]≤1.6。该超高强热轧钢板和钢带的抗拉强度≥780MPa、屈服强度≥660MPa,拉伸疲劳极限(循环1000万次)FL≥570MPa,或疲劳极限比抗拉强度FL/Rm≥0.72,扩孔率满足:若原始孔为冲压孔:扩孔率>85%;若原始孔为铰孔:扩孔率>120%。